Analysis of morphological characteristics of low vacuum laser welded joint of Ti6Al4V alloy

  • Harbin Welding Institute Limited Company, Harbin, 150028, China

More Information
  • Received Date: November 29, 2022
  • Available Online: July 20, 2023
    Graphical Abstract
    • Abstract
  • In order to explore the morphology characteristics of the laser welded joint of Ti6Al4V alloy under low vacuum environment, non-penetration welding was performed under 5 Pa ambient pressure. The influence law of laser power and defocus amount on the weld morphology was studied, and the stability and formation interval of the typical joint morphology were analyzed. The results show that the weld bead quality can be obtained by changing the process parameters in a wide range under low vacuum ambient pressure, and the weld penetration increases linearly with the increase of output power. The geometric features of welded joints can be divided into two types: the U shape formed when the line energy utilization factor is less than 0.13 or greater than 0.14, and the V shape formed when the line energy utilization factor is between 0.13 and 0.14. V shape keyhole stability is poor, it is difficult to maintain the quasi steady state, weld penetration depth fluctuation is large, easy to form defects at the bottom of the weld.
    • FullText(HTML)
    • References (22)
  • Gao F Y, Mu Z Z, Ma Z W, et al. Fine microstructure characterization of titanium alloy laser narrow gap welded joint[J]. China Welding, 2021, 30(3): 31 − 38.
    方乃文, 郭二军, 徐锴, 等. 钛合金激光填丝焊缝晶粒生长及相变原位观察[J]. 中国有色金属学报, 2022, 32(6): 1665 − 1672.

    Fang Naiwen, Guo Erjun, Xu Kai, et al. In-situ observation of grain growth and phase transformation in laser welding of titanium alloy with filler wire[J]. The Chinese Journal of Nonferrous Metals, 2022, 32(6): 1665 − 1672.
    Qin Y Q, Zhang D F, Jiang W X, et al. Microstructure and mechanical properties of welded joints of titanium alloy Ti60 after laser welding and subsequent heat treatment[J]. Metal Science and Heat Treatment, 2021, 62(11-12): 689 − 695. doi: 10.1007/s11041-021-00623-7
    Zhang L J, Pei J Y, Jian L, et al. Effects of laser welding and post-weld heat treatment on microstructure and mechanical properties of aged Ti55531 alloy[J]. Materials, 2018, 11(10): 1907. doi: 10.3390/ma11101907
    Zeng C Y, Zhang Y P, Hu J L, et al. The role of microstructure on corrosion fatigue behavior of thick-plate Ti6Al4V joint via vacuum electron beam welding[J]. Vacuum, 2020, 182: 109714. doi: 10.1016/j.vacuum.2020.109714
    Lu Y, Turner R, Brooks J, et al. A study of process-induced grain structures during steady state and non-steady state electron-beam welding of a titanium alloy[J]. Journal of Materials Science & Technology, 2022, 11(18): 117 − 127.
    Hu M J, Liu J H. Effects of zonal heat treatment on residual stresses and mechanical properties of electron beam welded TC4 alloy plates[J]. Transactions of Nonferrous Metals Society of China, 2009, 19(2): 324 − 329. doi: 10.1016/S1003-6326(08)60272-1
    Cheng M, Yu B, Guo R, et al. Electron beam welding of a novel near α high temperature titanium alloy powder compact: effect of post-welding heat treatment on tensile properties[J]. Journal of Materials Research and Technology, 2021, 10(5): 153 − 163.
    Yoshiaki A, Nobuyuki A, Tatsuharu O. Fundamental phenomena in high power CO2 laser (report II): vacuum laser welding (welding physics, process & instrument)[J]. Transactions of JWRI, 1985, 14(2): 217 − 222.
    Katayama S, Kobayashi Y, Mizutani M, et al. Effect of vacuum on penetration and defects in laser welding[J]. Journal of Laser Applications, 2001, 13(5): 187 − 192. doi: 10.2351/1.1404413
    孟圣昊, 司昌健, 任逸群, 等. 中厚板TC4钛合金真空环境激光焊接特性[J]. 焊接学报, 2021, 42(8): 40 − 47. doi: 10.12073/j.hjxb.20201124001

    Meng Shenghao, Si Changjian, Ren Yiqun, et al. Laser welding characteristics of TC4 titanium alloy in vacuum environment[J]. Transactions of the China Welding Institution, 2021, 42(8): 40 − 47. doi: 10.12073/j.hjxb.20201124001
    姜梦. 低真空激光焊接特性及热物理过程的试验研究与数值模拟[D]. 哈尔滨: 哈尔滨工业大学, 2020.

    Jiang Meng. Experimental study and numerical modeling of thermophysical process in laser welding under low vacuum and its welding characteristics[D]. Harbin: Harbin Institute of Technology, 2020.
    Reisgen U, Olschok S, Jakobs S, et al. Welding with the laser beam in vacuum[J]. Laser Technik Journal, 2015, 12(2): 42 − 46. doi: 10.1002/latj.201500014
    Francis J A, Holtum N, Olschok S, et al. Vacuum laser welding of SA508 steel[J]. Journal of Materials Processing Technology, 2019, 274: 116269. doi: 10.1016/j.jmatprotec.2019.116269
    Youhei A, Yousuke K, Hiroshi N, et al. Effect of reduced pressure atmosphere on weld geometry in partial penetration laser welding of stainless steel and aluminium alloy with high power and high brightness laser[J]. Science & Technology of Welding & Joining, 2014, 19(4): 324 − 332.
    Reisgen U, Olschok S, Turner C. Welding of thick plate copper with laser beam welding under vacuum[J]. Journal of Laser Applications, 2017, 29(2): 022402. doi: 10.2351/1.4983165
    Jiang M, Tao W, Chen Y B, et al. Comparison of processing window in full penetration laser welding of thick high-strength steel under atmosphere and sub-atmosphere[J]. Optics & Laser Technology, 2019, 109: 449 − 455.
    张明军. 万瓦级光纤激光深熔焊接厚板金属蒸汽行为与缺陷控制[D]. 湖南: 湖南大学, 2013.

    Zhang Mingjun. Study on the behavior of metallic vapor plume and defects control during deep penetration laser welding of thick plate using 10-kW level high power fiber laser[D]. Hunan: Hunan University, 2013.
    Luo Y. Bubble flow and the formation of cavity defect in weld pool of vacuum electron beam welding[J]. Vacuum, 2011, 86(1): 11 − 17. doi: 10.1016/j.vacuum.2011.03.024
    高福洋, 高奇, 蒋鹏, 等. 钛合金电子束深熔焊根部缺陷机理分析[J]. 焊接学报, 2018, 39(10): 30 − 34.

    Gao Fuyang, Gao Qi, Jiang Peng, et al. Analysis on mechanism of root defect in titanium alloy electron beam welding[J]. Transactions of the China Welding Institution, 2018, 39(10): 30 − 34.
    Zhao H, Niu W, Zhang B, et al. Modelling of keyhole dynamics and porosity formation considering the adaptive keyhole shape and three-phase coupling during deep-penetration laser welding[J]. Journal of Physics D:Applied Physics, 2011, 44(48): 485302. doi: 10.1088/0022-3727/44/48/485302
    Pang S Y, Chen X, Shao X Y, et al. Dynamics of vapor plume in transient keyhole during laser welding of stainless steel: local evaporation, plume swing and gas entrapment into porosity[J]. Optics and Lasers in Engineering, 2016, 82: 28 − 40. doi: 10.1016/j.optlaseng.2016.01.019
    • Related Articles

  • Related Articles

    [1]XUE Yongzhi, HU Lifang, WANG Hao, LI Rong, WANG Wenxian. Electric current characteristic and mechanical properties of Si-glass-Al anodic bonding process[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2019, 40(6): 71-76,86. DOI: 10.12073/j.hjxb.2019400157
    [2]CHEN Daming, HU Lifang, SHI Fangrong, MENG Qinsen. Mechanism and mechanical property of Si-glass-Si anodic bonding process[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2019, 40(2): 123-127. DOI: 10.12073/j.hjxb.2019400054
    [3]CHEN Daming, HU Lifang, XUE Yongzhi, CHEN Shaoping, WANG Wenxian. Interfacial investigation and mechanical properties of Al-glass-Al anodic bonding process[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2018, 39(9): 71-75. DOI: 10.12073/j.hjxb.2018390227
    [4]YIN Xu, LIU Cuirong, DU Chao, WU Changxiong. Effect of inorganic fillers on properties of polymer solid electrolyte and metal aluminum bonding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2015, 36(11): 37-40.
    [5]LIU Cuirong, MENG Qingsen, HU Lifang, HU Minying. Microstructure and bonding mechanism of anodic bonded interface between pyrex glass and kovar alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (2): 73-76.
    [6]WANG Fu-liang, LI Jun-hui, HAN Lei, ZHONG Jue. Effect of bonding time on thick aluminum wire wedge bonding strength[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (5): 47-51.
    [7]LONG Zhi-li, HAN lei, WU Yun-xin, ZHOU Hong-quan. Effect of different temperature on strength of thermosonic bonding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2005, (8): 23-26,38.
    [8]ZOU Jia-sheng, XU Zhi-rong, ZHAO Qi-zhang, CHEN Zheng. Bonding strength of double partial transient liquid phase bonding with Si3N4/Ti/Cu/Ni/Cu/Ti/Si3N4[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2005, (2): 41-44.
    [9]Liu Huijie, Feng Jicai, Qian Yiyu. Interface Structures and Bonding Strength of SiC/TiAl Joints in Diffusion Bonding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1999, (3): 170-174.
    [10]Feng Jicai, Liu Huijie, Han Shengyang, Li Zhuoran, Zhang Jiuhai. Interface Structures and Bonding Strength of SiC/Nb/SiC Diffusion Bonded Joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1997, (2): 20-23.

  • Cited by

    Periodical cited type(0)

    Other cited types(4)

Catalog

    Get Citation
    PDF
    XML
    Article views (260) PDF downloads (94) Cited by(4)
    Turn off MathJax
    Article Contents
    Abstract
    References
    Related Articles

    Website Copyright © Editorial Office of Transactions of the China Welding Institution, Welding Journals Publishing HouseTel：0451-86323218Address：No. 2077, Chuangxin Road, Songbei District, Harbin

    Supported by: Beijing Renhe Information Technology Co. Ltd    Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return