ZOU Jiasheng, ZENG Peng, XU Xiangping. Interfacial structure and strength of Si3N4 ceramics joint brazed with amorphous filler metal and Cu layer[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (11): 47-50.
Citation: ZOU Jiasheng, ZENG Peng, XU Xiangping. Interfacial structure and strength of Si3N4 ceramics joint brazed with amorphous filler metal and Cu layer[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (11): 47-50.

Interfacial structure and strength of Si3N4 ceramics joint brazed with amorphous filler metal and Cu layer

More Information
  • Received Date: August 25, 2011
  • Si3N4 ceramics was brazed with TiZrCuB amorphous filler metal and Cu interlayer, the effect of brazing metal composition and thickness of copper foil on interfacial structure and bonding strength were studied in this paper.The result shows that the joint strength is up to 241 MPa when the brazing temperature is 1 323 K, holding time is 30min, the thickness of Cu interlayer is 70 m and the exerted pressure is 0.027 MPa.the reaction layer is TiN, the interface microstructure is compounds of Si3N4/TiN/Ti-Si+Ti-Zr+Cu-Zr+α-Cu;changing the thickness of interlayer can adjust the thickness and composition of the reaction layer;As the thickness of Cu interlayer increases, Ti-Si compound layer has gradually separated from the TiN layer, and it is pushed to the weld center and refined to a granula shape.
  • Related Articles

    [1]XU Xiangping, WANG Hong, ZOU Jiasheng, XIA Chunzhi. Interfacial structure and properties of Si3N4 ceramic and TiAl alloys brazed with Ti/Ag-Cu/Cu interlayers[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2016, 37(12): 91-94.
    [2]ZHANG Deku, ZHANG Wenjun, JIANG Jiamin. High temperature brazing of Si3N4 ceramic using Cu-Ti active filler metal[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(5): 59-62.
    [3]ZOU Jiasheng, ZUO Huaiwen, XU Xiangping. Interfacial structure and strength of Si3N4 ceramics joint brazed with amorphous filler metal and Cu layer[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (12): 5-8.
    [4]ZOU Jiasheng, ZHAO Hongquan, JIANG Zhiguo. Microstructure and strength of Si3N4 joint brazed with Ti40Zr25Ni15Cu20 amorphous brazing alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2007, (3): 45-48.
    [5]YANG Jun, WU Ai-ping, ZOU Gui-sheng, ZHANG De-ku. Solid-liquid state bonding of Si3N4 ceramics and its joint high-temperature properties[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (7): 18-20.
    [6]ZOU Jia-sheng, XU Zhi-rong, ZHAO Qi-zhang, CHEN Zheng. Bonding strength of double partial transient liquid phase bonding with Si3N4/Ti/Cu/Ni/Cu/Ti/Si3N4[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2005, (2): 41-44.
    [7]ZOU Jia-sheng, ZHAI Jian-guang, CHU Ya-jie, CHEN Zheng. Effect of Ti foil thickness on interfacial structure and strength in PTLP bonding of Si3N4/Ti/Cu/Ti/Si3N4[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (6): 19-22.
    [8]YANG Min, ZOU Zeng-da, LIU Xiu-zhong, WANG Yu-fu, CUI Feng-you. Strength and fracture behavior of Si3N4 ceramic/Inconel 600 alloy liquid phase inductive diffusion bonding joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (4): 36-38,42.
    [9]CHEN Zheng, GU Xiao-bo, LI Guo-an, FANG Fang. Diffusion Bonding of Si3N4 Ceramic to Ni with Non-active Metal Interlayers of FeNi/Cu[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2001, (3): 25-28.
    [10]Wang Wenxian, Jia Shijun, Zhao Pengsheng, Zhang Yongqing. Influence of Interfacial Reaction on Joint Strength in Brazing Titanized Si3N4 to Q235 Steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1997, (4): 193-199.

Catalog

    Article views (208) PDF downloads (80) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return