Fretting wear behaviour of FeNiBSiCe alloy flame sprayed coatings

  • 1.

    Mechanical Engineering Department, Lanzhou Polytechnic College, Lanzhou, 730050, China

  • 2.

    State Key Laboratory of New Nonferrous Metal Materials, Lanzhou University of Science & Technology, Lanzhou 730050, China

  • 3.

    Mechanical Engineering Department, Lanzhou Polytechnic College, Lanzhou, 730050, China;State Key Laboratory of New Nonferrous Metal Materials, Lanzhou University of Science & Technology, Lanzhou 730050, China

More Information
  • Received Date: June 07, 2007
    Graphical Abstract
    • Abstract
  • The fretting wear properties of FeNiBSiCe alloy coatings coupling with SAE52100 steel under reciprocating sliding were examined by using a ball-on-disc reciprocating tribotester.Effects of load and sliding speed on fretting tribological properties of the coatings were studied.Worn surfaces of the coatings were analyzed by a scanning electron microscopy (SEM), a field emission scanning electron microscopy (FESEM) and energy dispersive spectroscopy (EDS), respectively.The friction coefficient of the coatings decreased slightly with the load, but increased with sliding speed at first, and then tended to be a constant value.The wear rate of the coatings increased with the load, but dramatically decreased at first and then slightly decreased with the sliding speed.An adhered oxide debris layerwas formed on the worn surface in friction.Fretting wear mechanism of the coatings was microplough at normal load, microfracture, oxidation wear and a large amount of counterpart material was transferred to the coatings at high load and high sliding speed.
    • FullText(HTML)
    • References (0)
    • Related Articles

  • Related Articles

    [1]LIU Kun, LI Jie, WANG Hao, JIAN Sijie. Evaluating solidification cracking susceptibility of Mg alloys and intergranular liquid backfilling during welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2023, 44(9): 9-15. DOI: 10.12073/j.hjxb.20221126001
    [2]WANG Lei, LI He, HUANG Yong, WANG Kehong, ZHOU Qi. Phase field investigation on solidification cracking susceptibility in the molten pool under different anisotropy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2021, 42(12): 83-86. DOI: 10.12073/j.hjxb.20210309001
    [3]ZHANG Yong, YE Wu, ZHOU Yunyun, XIE Hongxia, ZHANG Zhihan, CHU Qiang, LI Wenya. Defect repair of resistance spot welded aluminum alloy joint by friction stirring[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2017, 38(3): 17-21.
    [4]WU Song, WANG Min, KONG Liang, Gao Boen, SUN You. Mechanism and suppression of cracking in 5052-O aluminum alloy resistance spot weld[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(9): 92-96.
    [5]DONG Zhibo, ZHAN Xiaohong, WEI Yanhong, LU Yafeng, GUO Ping, YANG Yongfu. Pre-processing software for three-dimensional simulation and prediction of weld solidification cracks[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2009, (8): 21-24.
    [6]LIU Ren-pei, DONG Zu-jue, PAN Yong-ming. Dynamic cracking behaviors of weld solidification cracks for aluminum alloys at elevated temperature[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2005, (10): 9-13.
    [7]WANG Ya-rong, ZHANG Zhong-dian, FENG Ji-cai, Liu Hui, ZOU Li-jing. Effects of surface conditions on spot welded joint of magnesium alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2004, (3): 27-30.
    [8]WEI Yan hong, XU Wen li, LIU Ren pei, DONG Zu jie, PENG Bo. Post treatment system of temperature fields for welding solidification crack simulation[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (3): 72-74.
    [9]WEI Yan-hong, LIU Ren-pei, DONG Zu-jue. Simulated Stress-strain Distributions for Weld Metal Solidification Cracking in Stainless Steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2000, (2): 36-38.
    [10]Wu Aiping, Ren Jialie, Lu Anli. Prevention of solidification cracking with auxiliary heat source[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1993, (1): 7-11.

Catalog

    Get Citation
    PDF
    XML
    Article views (195) PDF downloads (61) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    Related Articles

    Website Copyright © Editorial Office of Transactions of the China Welding Institution, Welding Journals Publishing HouseTel：0451-86323218Address：No. 2077, Chuangxin Road, Songbei District, Harbin

    Supported by: Beijing Renhe Information Technology Co. Ltd    Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return