FENG Ji-cai, JING Xiang-meng, ZHANG Li-xia, LIU Hong. Interface structure and bonding strength of brazed joint of TiC cermet/steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (1): 5-8.
Citation: FENG Ji-cai, JING Xiang-meng, ZHANG Li-xia, LIU Hong. Interface structure and bonding strength of brazed joint of TiC cermet/steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (1): 5-8.
shu

Interface structure and bonding strength of brazed joint of TiC cermet/steel

  • National Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 150001, China

More Information
  • Received Date: June 15, 2004
    Graphical Abstract
    • Abstract
  • The vacuum brazing of TiC cermet(synthesized by SHS) to medium carbon steel was carried out with BAg45CuZn brazing filler metal,and the interface structure and shear strength of the joints were also investigated by means of SEM,EPMA and XRD.The experimental results showed that the bonding of TiC cermet to medium steel can be performed with BAg45CuZn filler metal.The interface structure of the joint is TiC cermet/(Cu,Ni)/Ag(s,s)+Cu(s,s)/(Cu,Ni)/(Cu,Ni)+(Fe,Ni)/medium carbon steel.The maximum shear strength of the joint brazed at 850℃ for 10 min is up to 121 MPa at room temperature.
    • FullText(HTML)
    • References (0)
    • Related Articles

  • Related Articles

    [1]WANG Tao, XUE Gang, YANG Jianguo, FANG Hongyuan. Equal load carrying capacity design system of joint based on stress intensity factor[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2013, (8): 101-104.
    [2]WANG Tao, YANG Jianguo, LIU Xuesong, FANG Hongyuan, ZHOU Lipeng. Influence of joint geometric parameters on shape factor of under-matched butt joint with center crack[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (1): 101-104.
    [3]XU Lianyong, JING Hongyang. Stress intensity factor of interfacial crack between metal-base ceramic coating and steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (3): 84-88.
    [4]YU Ping, TIAN Zhiling, PAN Chuan, XUE Zhenkui. Gas in weld for self-shielded flux-cored arc welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2007, (2): 67-70.
    [5]SUI Yong-li, DU Ze-yu, HUANG Fu-xiang, TIAN Liang. Influence of hydrogen on weld metal toughness by self-shielded flux-cored wire welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (12): 74-76.
    [6]WANG Bao, YANG Lin, WANG Yong. Observation and analysis of metal transfer phenomena for flux-cored electrodes in CO2 arc welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (7): 77-80.
    [7]ZHANG Zhong-ping, HUO Li-xing, WANG Dong-po, ZHANG Yu-feng. Effect of sprayed coatings on stress intensity factor of weld toe crack of cruciform welded joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (2): 85-88.
    [8]WANG Fu-de, LI Zhi-yuan, YOU Min. Abrasive Wear of Cladding Metal of YDCrMoV CO2 Shielded Flux-cored Wire[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2000, (4): 46-49.
    [9]Zhang Wenyue, Yang Qingxia, Xu Yuhuan. Research on hardening factor of welding HAZ[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1991, (4): 195-200.
    [10]Zhang Wenyue, Zhu Meili, Qin Boxiong. Research on effective diffusive hydrogen and hydrogen diffusive factor of welding cold cracking susceptibility[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1991, (3): 129-135.

Catalog

    Get Citation
    PDF
    XML
    Article views (231) PDF downloads (55) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    Related Articles

    Website Copyright © Editorial Office of Transactions of the China Welding Institution, Welding Journals Publishing HouseTel：0451-86323218Address：No. 2077, Chuangxin Road, Songbei District, Harbin

    Supported by: Beijing Renhe Information Technology Co. Ltd    Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return