Effects of surface state of C/SiC composites on brazing of C/SiC to Nb

  • State Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 15001, China

More Information
  • Received Date: February 07, 2010
    Graphical Abstract
    • Abstract
  • C/SiC composites and Nb were brazed with equiatomic ratio Ti-Ni composite foils in vacuum,and the effects of surface state of C/SiC composites on the microstructure and property of the brazing joints were investigated.The results showed that the(Ti,Nb) C reaction layer between C/SiC and filler metal in the brazing joint was serrate when the C/SiC surface state was cut by the electric spark linear cutting machine,but the(Ti,Nb) C layers were both flat when the surface of C/SiC were polished and sanded before brazing.The serrate reaction layer decreased the stress concentration at the C/SiC-filler metal interface and was benefit for the joint.The shear strength of brazing joints of Nb and C/SiC at spark cutting state reached 188 MPa,which is much higher than that at polishing and sanding states.The fracture of brazing joints of Nb and C/SiC at spark cutting state took place at C/SiC base material,C/SiC-filler metal interface and filler metal,but that of the other two kinds of joints mainly occurred at the C/SiC-filler metal interface.
    • FullText(HTML)
    • References (0)
    • Related Articles

  • Related Articles

    [1]ZHANG Yukun, CHEN Jichun, ZHANG Jinsong. Microstructure and shear strength of the C/SiC and Q235 brazing joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2020, 41(7): 78-82. DOI: 10.12073/j.hjxb.20191010001
    [2]MA Qunshuang, LI Yajiang, WANG Juan, DUAN Huming, XU Guangyuan. Microstructure characteristics and shear strength of wide-band laser clad Ni60 composite coatings reinforced with WC particle[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2016, 37(12): 49-52.
    [3]XU Yuanyuan, YAN Yanfu, FENG Lifang, . Effect of content of Ni on wettability and shear strength of BiSbSnNi solder alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(7): 31-34.
    [4]WU Na, LI Yajiang, WANG Juan. Microstructure and shear strength of high-temperature brazed joint of Super-Ni/NiCr laminated composite using Ni-Cr-Si-B filler metal[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(1): 9-12,36.
    [5]GAO Lili, XUE Songbai, WANG Bo. Effect of Nd addition on microstructure and mechanical property of Sn3.8Ag0.7Cu solder joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2011, (12): 73-76.
    [6]LU Wei, ZHANG Ning, SHI Yaowu, LEI Yongping. Effect of loading rate on shear strength of SnAgCu solder joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2010, (9): 57-60.
    [7]MENG Gongge, LI Zhengping. Shear strength and fracture surface analysis of BiAgNiCuGe/Cujoint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2009, (10): 45-48.
    [8]WANG Juan, LI Yajiang, S. A. GERASIMOV. Microstructure and shear strength of diffusion brazed Al2O3-TiC/Q235 joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (12): 25-28.
    [9]XUE Song-bai, HU Yong-fang, YU Sheng-lin, WU Yu-xiu. Effects of thermal cycling on shear strength and microstructures of soldered joints of ceramic ball grid array package[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (6): 1-4.
    [10]WANG Juan, LI Ya-jiang, LIU Peng. Shear strength and microstructure in Fe3Al/Q235 diffusion bonded joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (5): 81-84.

Catalog

    Get Citation
    PDF
    XML
    Article views (177) PDF downloads (83) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    Related Articles

    Website Copyright © Editorial Office of Transactions of the China Welding Institution, Welding Journals Publishing HouseTel：0451-86323218Address：No. 2077, Chuangxin Road, Songbei District, Harbin

    Supported by: Beijing Renhe Information Technology Co. Ltd    Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return