WANG Xingxing, SHANGGUAN Linjian, HE Peng, LONG Weimin, WU Shengjin. Quantitative characterization of brazability for Sn-plated Ag brazing filler metals based on entropy model[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2020, 41(1): 18-22. DOI: 10.12073/j.hjxb.20190702001
Citation: WANG Xingxing, SHANGGUAN Linjian, HE Peng, LONG Weimin, WU Shengjin. Quantitative characterization of brazability for Sn-plated Ag brazing filler metals based on entropy model[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2020, 41(1): 18-22. DOI: 10.12073/j.hjxb.20190702001

Quantitative characterization of brazability for Sn-plated Ag brazing filler metals based on entropy model

More Information
  • Received Date: July 01, 2019
  • Available Online: July 12, 2020
  • Two types of Sn-plated AgCuZnSn brazing filler metals were prepared by a combinative process of electroplating and thermal diffusion using BAg50CuZn and BAg34CuZnSn brazing filler metal. The comprehensive thermal analyzer, wetting test furnace and universal tensile testing machine were applied to analyze the melting temperature range, wetting area and tensile strength. The mathematical model of the filler metals wetting entropy and the joint strength entropy were established, and compared with the traditional brazing filler metal prepared by melting alloying under the same condition of Sn content. The wetting entropy of the Sn-plated Ag brazing alloys are smaller than the traditional brazing filler metals, and its joint strength entropy value is slightly higher than the latter. The wetting entropy value of the Sn-electroplated brazing alloys and traditional filler metal are similar to the change trend of the wetting area for those filler metals on the surface of the 316LN stainless steel. The change trend of the brazed joint strength entropy value with those filler metals are basically the same as the tensile strength of the 316LN stainless steel joint with the increase of the Sn content. The experimental results show that the mathematical model of the wetting entropy and the joint strength entropy can quantitatively predict the brazing process and mechanical properties of the Sn-electroplated Ag brazing alloys to a certain extent.
  • Long W M, Zhang G X, Zhang Q K. Insitu synthesis of high strength Ag brazing filler metals during induction brazing process[J]. Scripta Materialia, 2016, 110: 41 − 43. doi: 10.1016/j.scriptamat.2015.07.041
    Ma Chaoli, Xue Songbai, Wang Bo. Study on novel Ag-Cu-Zn-Sn brazing filler metal bearing Ga[J]. Journal of Alloys and Compounds, 2016, 688: 854 − 862. doi: 10.1016/j.jallcom.2016.07.255
    Li Z R, Cao J, Liu B, et al. Effect of La content on microstructure evolution of 20Ag-Cu-Zn-Sn-P-La filler metals and properties of joints[J]. Science and Technology of Welding & Joining, 2010, 15(1): 59 − 63.
    Khorunov V F, Stefaniv B V, Maksymova S V. Effect of nickel and manganese on structure of Ag-Cu-Zn-Sn system alloys and strength of brazed joints[J]. Paton Welding Journal, 2014, 4: 22 − 25.
    Li M G, Sun D Q, Qiu X M, et al. Effect of tin on melting temperature and microstructure of Ag-Cu-Zn-Sn filler metals[J]. Materials Science and Technology(United Kingdom), 2005, 21(11): 1318 − 1322.
    Lai Zhongmin, Xue Songbai, Han Xianpeng, et al. Study on microstructure and property of brazed joint of AgCuZn-X(Ga, Sn, In, Ni) brazing alloy[J]. Rare Metal Materials and Engineering, 2010, 39(3): 397 − 400. doi: 10.1016/S1875-5372(10)60087-2
    Winiowski A, Rózanski M. Impact of tin and nickel on the brazing properties of silver filler metals and on the strength of brazed joints made of stainless steels[J]. Archives of Metallurgy and Materials, 2013, 58(4): 1007 − 1011. doi: 10.2478/amm-2013-0118
    龙伟民, 张冠星, 张青科, 等. 钎焊过程原位合成高强度银钎料[J]. 焊接学报, 2015, 36(11): 1 − 4.

    Long Weimin, Zhang Guanxing, Zhang Qingke, et al. In-situ synthesis of high strength Ag brazing filler metals during brazing process[J]. Transactions of the China Welding Institution, 2015, 36(11): 1 − 4.
    高歌, 胡建华, 程呈, 等. 电磁压制多元金属混合粉末的压型方程[J]. 中国有色金属学报, 2015, 25(7): 1937 − 1942.

    Gao Ge, Hu Jianhua, Cheng Cheng, et al. Forming equation about multivariate mixed metal powder by electromagnetic compaction[J]. The Chinese Journal of Nonferrous Metals, 2015, 25(7): 1937 − 1942.
    王星星, 李帅, 彭进, 等. 基于镀锡银钎料焊304不锈钢接头的腐蚀行为[J]. 焊接学报, 2018, 39(4): 63 − 66.

    Wang Xingxing, Li Shuai, Peng Jin, et al. Corrosion behaviors of 304 stainless steel joints brazed with Sn-electroplated Ag brazing alloys[J]. Transactions of the China Welding Institution, 2018, 39(4): 63 − 66.
    Benisek A, Dachs E. A relationship to estimate the excess entropy of mixing: application in silicate solid solutions and binary alloys[J]. Journal of Alloys and Compounds, 2012, 527: 127 − 131. doi: 10.1016/j.jallcom.2012.03.007
    Carvalhoa A M, Coelhob A A, Von Rankec P J, et al. The isothermal variation of the entropy (ΔST)may be miscalculated from magnetization isotherms in some cases: MnAs and Gd5Ge2Si2 compounds as examples[J]. Journal of Alloys and Compounds, 2011, 509: 3452 − 3456. doi: 10.1016/j.jallcom.2010.12.088
    Ming Zhu, Wang Kehong, Qu Tianpeng, et al. Thermodynamic study on welding wire design of high nitrogen austenitic stainless steel[J]. China Welding (English Edition), 2019, 28(1): 49 − 55.
    王星星, 龙伟民, 何鹏, 等. 时效处理对镍/巴氏合金界面组织及性能的影响[J]. 焊接学报, 2019, 40(8): 113 − 117.

    Wang Xingxing, Long Weimin, He Peng, et al. Effect of aging treatment on interfacial microstructure and mechanical properties of Ni/babbitt alloy[J]. Transactions of the China Welding Institution, 2019, 40(8): 113 − 117.
    Wang Xingxing, Peng Jin, Cui Datian. Microstructure and mechanical properties of stainless steel/brass joints brazed by Sn-electroplated Ag brazing filler metals[J]. Journal of Materials Engineering and Performance, 2018, 27(5): 2233 − 2238.
    纠永涛, 轩庆庆, 高雅, 等. 银基钎料铸锭微区成分及组织的变化规律[J]. 焊接学报, 2018, 39(5): 82 − 86.

    Jiu Yongtao, Xuan Qingqing, Gao Ya, et al. Change laws of micro-composition and microstructure of silver-based brazing filler metal ingot[J]. Transactions of the China Welding Institution, 2018, 39(5): 82 − 86.
  • Related Articles

    [1]XU Yuanzhao, LUO Jiutian, FANG Naiwen, FENG Zhiqiang, WU Pengbo, LI Quan. Image processing technology for ship plate melt pool based on MS-FCM algorithm[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2024, 45(3): 82-90. DOI: 10.12073/j.hjxb.20231010001
    [2]XIAO Yang, GAO Weixin, DENG Guohao. Recognition algorithm of small-diameter tube X-ray welding defect image[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2024, 45(2): 82-88. DOI: 10.12073/j.hjxb.20230228001
    [3]TANG Quan, SHI Zhixin, MAO Zhiwei. Spatter analysis of rotating arc image based on multi threshold and neural network[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2022, 43(12): 41-46. DOI: 10.12073/j.hjxb.20211219001
    [4]CHI Dazhao, GANG Tie. Defect detection method based on 2D entropy image segmentation[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2016, 37(12): 25-28.
    [5]ZHAO Huihuang, ZHOU Dejian, WU Zhaohua, LI Chunquan, LI Kangman. SMT soldering image denoising based on wavelet packet transform and adaptive threshold[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2011, (11): 73-76.
    [6]LIU Suyi, LI Bing, ZHANG Hua, JIA Jianping. Feature extraction and image processing for underwater weld with laser vision[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2011, (9): 45-48.
    [7]HUANG Minshuang, HUANG Junfen, TANG Jian, JIANG Lipei. All-fiber optic integration type of weld seam image sensing system[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2009, (6): 63-66.
    [8]WANG Mingquan, CHAI Li. Application of an improved watershed algorithm in welding image segmentation[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2007, (7): 13-16.
    [9]WANG Qing-xiang, SUN Bing-da, LI Di. Image processing method for recognizing position of welding seam[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2005, (2): 59-63.
    [10]WU Lin, DAI Ming, LI Yan. Weld Area Extracting and weld Defect Fidelity Getting for Image of Aluminum Weld Seam[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2001, (2): 1-4.

Catalog

    Article views (357) PDF downloads (18) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return