JIN Yuhua, HUO Renjie, LI Changfeng, WANG Xijing. Influence of rotational speed on fracture characteristics of 7055 aluminum alloy friction stir welded joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2017, 38(2): 10-13,18.
Citation: JIN Yuhua, HUO Renjie, LI Changfeng, WANG Xijing. Influence of rotational speed on fracture characteristics of 7055 aluminum alloy friction stir welded joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2017, 38(2): 10-13,18.

Influence of rotational speed on fracture characteristics of 7055 aluminum alloy friction stir welded joints

More Information
  • Received Date: February 04, 2015
  • The butt welding process of friction stir welding was used on 5 mm thick 7055 aluminum alloy. The characteristics of fracture locations, microstructures of fracture cross-section and fracture surfaces of different rotational speed were investigated by tensile test. The results shows that with the increase of rotational speed, the weak zone has shifted. When rotational speed was 700~800 r/min, The fracture occurs in the heat affected zone (HAZ) was 45°shear fracture; With the rotational speed increased from 900~1 100 r/min, the fracture morphologies on the joint cross-section which fraction occurs in the nugget zone (NZ) was "S-type" fracture. Furthermore, when the rotational speed increased from 1 200~1 400 r/min, fracture occurred in the thermo-mechanically affected zone (TMAZ) of advancing side or at the border between the TMAZ of advancing side and the nugget zone. Fracture morphology analysis shows that big and deep dimples were found in the HAZ, small and shallow dimples were found in the NZ,both of them belong to the ductile fracture of eaem. The mixed ductile brittle fracture characteristic was performed in the TMAZ boundary.
  • 邓运来, 万 里, 李 鑫, 等. 7055铝合金晶界η相回归阶段的粗化动力学[J]. 中国有色金属学报, 2014, 24(4):888-893. Deng Yunlai, Wan Li, Li Xin, et al. Coarsening kinetics of grain boundary precipitates in 7055aluminium alloy[J]. TheChineseJournal ofNonferrous Metals, 2014, 24(4):888-893.
    陈军洲. AA7055铝合金的时效析出行为与力学性能[D]. 哈尔滨:哈尔滨工业大学, 2009.
    Sivaraj P, Kanagarajan D, Balasubramanian V. Effect of post weld heat treatment on tensile properties and microstructure characteristics offriction stir welded armour gradeAA7075-T651aluminium alloy[J]. DefenceTechnology, 2014, 10(1):1-8.
    佟建华, 张 坤, 林 松, 等. 搅拌摩擦焊和熔化极气体保护焊6082铝合金疲劳性能分析[J]. 焊接学报, 2015, 36(7):90-94. Tong Jianhua, Zhang Kun, Lin Song, et al.Comparison offatigue property of6082aluminum alloy joint by friction stir welding and metal inert-gas welding[J]. Transactions of theChinaWelding Institution, 2015, 36(7):90-94.
    李 达, 孙明辉, 崔占全. 工艺参数对铝镁搅拌摩擦焊焊缝成形质量的影响[J]. 焊接学报, 2011, 32(8):97-100. Li Da, Sun Minghui, Cui Zhanquan. Effect of parameters on friction stir welding joint of7075Al and AZ31BMg[J]. Transactions of theChinaWelding Institution, 2011, 32(8):97-100.
    严 铿, 刘 俊, 史 超. 喷射成形7055铝合金FSW焊工艺与性能[J]. 焊接学报, 2012, 33(6):50-54. Yan Keng, LiuJun, Shi Chao. Study on process and property ofFSW of spray formed 7055aluminum alloy[J]. Transactions of theChinaWelding Institution, 2012, 33(6):50-54.
    Dixit M, MishraRS, Sankaran KK. Structure-property correlations in Al 7050and Al 7055 high-strength aluminum alloys[J]. Materials Scienceand Engineering:A, 2008, 478(1):163-172.
    许俊华, 赵立军, 施林波, 等. 喷射成形7055铝合金搅拌摩擦焊的焊缝组织与力学性能[J]. 粉末冶金材料科学与工程, 2011, 16(4):547-552. XuJunhua, Zhao Lijun, Shi Linbo, et al. Microstructureand mechanical properties of joints offriction stir welding 7055Al alloys by spray formation[J]. Materials Scienceand Engineering ofPowder Metallurgy, 2011, 16(4):547-552.
    Hovanski Y, Carsley J, ClarkeK, et al. Friction-stir welding and processing[J]. TheMinerals, Metals & Materials Society, 2015, 67(5):996-999.
  • Related Articles

    [1]MA Qunshuang, LI Yajiang, WANG Juan, DUAN Huming, XU Guangyuan. Microstructure characteristics and shear strength of wide-band laser clad Ni60 composite coatings reinforced with WC particle[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2016, 37(12): 49-52.
    [2]DAI Wei, XUE Songbai, JIANG Shiqin, LOU Jiyuan, LOU Yingbing, WANG Shuiqing. Microstructure and mechanical properties of 6061 Al joints brazed with a low-melting point filler[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (6): 105-108.
    [3]LI Xiaoquan, CHU Yajie, YANG Zonghui, HE Xiancong. Effect of hot extrusion deformation on microstructure and fracture morphology of AZ31B magnesium alloy TIG weld seam[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (3): 1-4.
    [4]MENG Gongge, LI Dan, LI Zhengping, WANG Yanpeng, CHEN Leida. Effects of aging on shearing strength and fracture surface characteristics of SnCuSb/Cu soldering joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2010, (6): 85-88.
    [5]MENG Gongge, LI Zhengping. Shear strength and fracture surface analysis of BiAgNiCuGe/Cujoint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2009, (10): 45-48.
    [6]MENG Gongge, LI Caifu, YANG Tuoyu, CHEN Leida. Effect of germanium on shearing strength and fracture surface of SnAgCu/Cu soldering joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (9): 59-62.
    [7]ZHANG Liang, XUE Songbai, HAN Zongjie, YU Shenglin, SHENG Zhong. Investigation of mechanical property and fracture morphology of lead-free soldered joints of fine pitch devices[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (9): 35-38.
    [8]ZHOU Peng-zhan, ZHONG Jue, HE Di-qiu, SHU Xia-yun. Microstructure-property and fracture behavior of friction-stir welded 2519 aluminium alloy plate[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (4): 33-36.
    [9]Yang Shijie, Meng Qingsen, Lu Wenxiong. Fracture morphology of solidification crack and crack resisting property of austenitic stainless steel deposited metal[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1995, (2): 62-67.
    [10]Xu Yuhuan, Zhang Wenyue, Du Zeyu, Zhao Zhong, Chen Banggu. FRACTOGRAPHIC ANALYSIS OF WELDING COLD CRACK[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1985, (4): 163-170.
  • Cited by

    Periodical cited type(4)

    1. 周金旭,王东辉,叶树茂,刘迪,金鑫,恒俊楠. 铝合金薄板脉冲激光焊接工艺及接头组织特征研究. 有色金属加工. 2025(02): 34-40 .
    2. 苗晓军,韩丽娟,李凯,王磊,姜来合格,廖伟,高明. 铝合金高频振荡扫描激光-电弧复合焊缝成形规律与预测. 焊接学报. 2024(07): 83-91 . 本站查看
    3. 陈健豪,何志强,蒯夕伟,孟燕菲,邓礼兵. 储能电池用铝合金环形激光焊接特性研究. 机电工程技术. 2024(09): 135-139 .
    4. 郭克星. 铝合金激光焊接技术研究进展. 热处理. 2024(06): 1-7 .

    Other cited types(2)

Catalog

    Article views (298) PDF downloads (149) Cited by(6)

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return