SONG Gang, WANG Jie, YU Jingwei, LIU Liming. Analysis of AZ31B/Q235 bonding interface by laser-induced arc welding with filler wire[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2016, 37(7): 93-96.
Citation: SONG Gang, WANG Jie, YU Jingwei, LIU Liming. Analysis of AZ31B/Q235 bonding interface by laser-induced arc welding with filler wire[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2016, 37(7): 93-96.
shu

Analysis of AZ31B/Q235 bonding interface by laser-induced arc welding with filler wire

  • Key Laboratory of Liaoning Advanced Welding and Joining Technology, School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China

More Information
  • Received Date: January 09, 2016
    Graphical Abstract
    • Abstract
  • Butt welding of AZ31B magnesium alloy to Q235 steel sheets was conducted by utilizing laser-induced TIG heat source and AZ61 magnesium filler wire. The elemental distribution and tensile strength of the joint were examined by scanning electron microscopy (SEM), electron probe microscope analysis (EPMA), electronic tension machine and optical microscopy. The results show that a satisfied and continuous butt joint of AZ31B magnesium alloy to Q235 steel sheets was obtained. The average tensile load of the joint could reach 3.13 kN/cm, 95% of Q235 base metal. Meanwhile, the interface in the joint mainly consisted of two parts:the middle part of welded seam with diffusion between Mg and Fe; upper and lower surfaces of the steel with wetting as the main form of connection. The diffusion reaction played an important role in bonded interface of magnesium/steel dissimilar metal joint.
    • FullText(HTML)
    • References (8)
  • 李亚江.先进材料焊接技术[M].北京:化学工业出版社,2012.
    陈祝年.焊接工程师手册(第二版)[M].北京:机械工业出版社,2009.
    Waled M Elthalabawy,Tahir I Khan.Microstructural development of diffusion brazed austenitic stainless steel to magnesium alloy using a nickel interlayer[J].Materials Characterization,2010,61:703-712.
    L Liu,L Xiao.The mechanisms of resistance spot welding of magnesium to steel[J].Metallurgical and Materials Transactions A,2010,41A:2651-2661.
    Li L,Tan C,Chen Y,et al.Comparative study on microstructure and mechanical properties of laser welded-brazed Mg/mild steel and Mg/stainless steel joints[J].Materials and Design,2013,43:59-65.
    曹睿,余建永,陈剑虹,等.镁/镀锌钢板CMT熔钎焊连接机制分析[J].焊接学报,2013,34(9):21-24.Cao Rui,Yu Jianyong,Chen Jianhong,et al.Bonding mechanism of CMT fusion-brazed joints between magnesium and galvanized steel[J].Transactions of the China Welding Institution,2013,34(9):21-24.
    Song Gang,An Guangye,Liu Liming.Effect of gradient thermal distribution on butt joining of magnesium alloy to steel with Cu-Zn alloy interlayer by hybrid laser-tungsten inert gas welding[J].Materials and Design,2012,35:323-329.
    宋刚,胡广龙,任大鑫,等.镁/钢填镍夹层激光-电弧复合对接熔化焊特性[J].焊接学报,2015,36(1):43-46.Song Gang,Hu Guanglong,Ren Daxin,et al.Study on butt fusion welding characteristics of AZ31B magnesium alloy to steel by hybrid laser-TIG welding with Ni interlayer[J].Transactions of the China Welding Institution,2015,36(1):43-46.
    • Related Articles

  • Related Articles

    [1]SUI Chufan, LIU Zhengjun, AI Xingyu. Effect of ultrasonic vibration on welding hot crack of 6061 aluminum alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2023, 44(1): 122-128. DOI: 10.12073/j.hjxb.20220106002
    [2]CHEN Genyu, ZHANG Yan, LEI Ran. Testing of hot crack using laser-MAG combined welding for 42CrMo steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2019, 40(7): 61-66. DOI: 10.12073/j.hjxb.2019400182
    [3]YU Hanchen<sup>1</sup>, YAN Han<sup>2</sup>, LUAN Tianmin<sup>1</sup>, FAN Wei<sup>1</sup>, ZHANG Huiwen<sup>3</sup>. Investigation on the cause of the hot cracking in GTA welding of thick copper plates[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2018, 39(8): 87-91. DOI: 10.12073/j.hjxb.2018390207
    [4]GONG Lian, ZHU Liang, ZHOU Chao. Effects of welding parameters on ultra-narrow gap welding hot cracking[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2016, 37(10): 93-96.
    [5]LI Yinan, YAN Jiuchun, GUO Feng, PENG Zilong. Formation process of hot cracking in copper He shielding gas tungsten welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(8): 43-47.
    [6]LI Jun, YANG Jianguo, TAN Xing, FANG Hongyuan. Experimental investigation on controlling welding hot crack with welding with trailing rotating extrusion[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2010, (12): 45-48.
    [7]Liu Weiping, Tian Xitang, Zhang Xiuzhi. A new method for prevention of weld hot cracking[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1995, (2): 106-111.
    [8]Si Zhongyao, Yu Erjing, Ying Huiyun, Liu Xingzhi, Liu Quan. STUDY OF THE TEMPERATURE RAGES OF HOT CRACKING FORMATION IN THE WELD METAL OF LOW-CARBON STEEL[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1989, (2): 87-94.
    [9]Gu Yuxi, Qi Fuguo, Yin Yousheng, Ding Hongtai, Zheng Zhongjian, Shi Lianying. EFFECTS OF ALLOY ELEMENTS ON WELD HOT CRACKING SUSCEPTIBILITY IN THE SUBMERGED ARC WELDING OF 12SiMoVNb HYDROGEN-RESISTANT STEEL[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1984, (4): 179-187.
    [10]Zhang Yansheng, Zhong Zugui. THE METALLURGICAL AND TECHNOLOGICAL FACTORS AFFECTING THE HOT CRACKING IN TIG WELDING OF SUPERALLOYS[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1982, (2): 57-64.

Catalog

    Get Citation
    PDF
    XML
    Article views (494) PDF downloads (208) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    References
    Related Articles

    Website Copyright © Editorial Office of Transactions of the China Welding Institution, Welding Journals Publishing HouseTel：0451-86323218Address：No. 2077, Chuangxin Road, Songbei District, Harbin

    Supported by: Beijing Renhe Information Technology Co. Ltd    Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return