SHI Yunzhe, WANG Gangang, CHENG Peng, ZHANG Wei, ZHAO Jiancang, SONG Libin. Influence of heat affected zone microstructure of 12Cr1MoVG reheat cracking susceptibility[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2015, 36(11): 65-68.
Citation: SHI Yunzhe, WANG Gangang, CHENG Peng, ZHANG Wei, ZHAO Jiancang, SONG Libin. Influence of heat affected zone microstructure of 12Cr1MoVG reheat cracking susceptibility[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2015, 36(11): 65-68.

Influence of heat affected zone microstructure of 12Cr1MoVG reheat cracking susceptibility

More Information
  • Received Date: February 13, 2014
  • The heat affected zone (HAZ) simulation test was done on two sorts of 12Cr1MoVG specimen. One of which was ferrite and pearlite for base metal and bainite for the other, by using Gleeble Thermal-force simulation machine. Then, for studying the reheat cracking susceptibility in the two different weld structures, the tensile test was done on the two different HAZ structures at different high temperatures slowly. The result showed that when HAZ structure is ferrite and bainite,its reheat cracking sensitive temperature range is 640-760 ℃ and the most sensitive point is 690 ℃ in our study. When HAZ structure is bainite,reheat cracking tendency is obvious after 650 ℃, especially at 690 ℃.Analysis result showed that when bainite exists in HAZ,its reheat cracking susceptibility is high. However, 5% to 8% ferrite exists in HAZ can reduce the reheat cracking sensitivity.
  • 迟露鑫, 孙昭藩, 伍光凤. 12Cr1MoV耐热钢管焊接温度场模拟与试验验证[J]. 焊接学报, 2014, 35(10): 89-92. Chi Luxin, Sun Zhaofan, Wu Guangfeng. Numerical simulation and test verification of welding temperature field of 12Cr1MoV heat-resistant steel pipe[J]. Transactions of the China Welding Institution, 2014, 35(10): 89-92.
    陈忠兵, 赵彦芬, 赵建仓, 等. 厚壁12Cr1MoVG钢焊接接头裂纹分析及其控制[J]. 中国电机工程学报, 2012, 32(35): 137-143. Chen Zhongbing, Zhao Yanfen, Zhao Jiancang, et al. Analysis and controlling for cracks in welded joint of thick walled steel 12Cr1MoVG[J]. Proceedings of the CSEE, 2012, 32(35): 137-143.
    刘俊松, 陈学东, 卜华全, 等. 热模拟法研究07MnNiCrMo VDR钢再热裂纹敏感性[J]. 热加工工艺, 2012, 41(17): 19-21. Liu Junsong, Chen Xuedong, Bu Huaquan, et al. Study on reheating crack susceptibility of 07MnNiCrMo VDR steel by thermo-mechanical simulator[J]. Hot Working Technology, 2012, 41(17): 19-21.
    Cédric Chauvy, Sylvain Pillot. Prevention of weld metal reheat cracking during Cr-Mo-V heavy reactors fabrication[C]// Prague, Proceedings of the ASME 2009 Pressure Vessels and Piping Division Conference PVP, 2009: 26-30.
    American Welding Society. Welding handbook, Vol.1[M]. 8th edition. Miami: American Welding Society, 1991.
    钟群鹏, 赵子华. 断口学[M]. 北京: 高等教育出版社, 2006.
    姚 钦. HQ-80钢再热裂纹机理[J]. 焊接学报, 2004, 25(6): 77-81. Yao Qin. Mechanism of HQ-80 steel reheat crack[J]. Transactions of the China Welding Institution, 2004, 25(6): 77-81.
  • Related Articles

    [1]CHEN Qianqian, LI Dong, HE Congcong, YU Zhishui. Microstructure difference analysis of large thickness welded joint with EBW[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2015, 36(9): 79-82.
    [2]ZHENG Kai, ZHAO Dajun, ZHANG Xuelian. Performance of dissimilar metal weld between SA335P91 and 12Cr1MoV steels in ultra(ultra)supercritical thermal power units[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (8): 77-80.
    [3]GONG Jianxun, XIAO Yifeng, ZHANG Qinghui, Ma Mo. Fe-Cr-V wear resistant hardfacing alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (7): 73-76.
    [4]YU Sheng fu, YU Yang chun, XIE Ming li, LI Zhi yuan. Effect of secondary thermal cycle on intragranular ferrite[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (2): 89-92,96.
    [5]Li Yajiang, Zhang Yonglan. Microstructural characteristics in heat-affected zone of Crl8Mo2 ferritic stainless steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1995, (3): 130-134.
    [6]Ke Liming. Influence of ferrite contents in duplex stainless steel weld metal on hydrogen cracking susceptibility[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1993, (3): 179-185.
    [7]Wang Shiliang, Hu Weiping, Tang Bogang. INCLUSIONS AND NUCLEATION OF ACICULAR FERRITE IN WELD METALS IN HSLA[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1990, (2): 81-90.
    [8]Li Ailing, Zhai Yang, Yan Cheng, Chen Jianhong, Nobuya lwamoto. THE INFLUENCE OF ALLOY ELEMENTS ON THE FORMATION OF ACICULAR FERRITE IN WELD METAL[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1989, (3): 163-171.
    [9]Liu Tingcai. WELDABILITY OF DUPLEX FERRITIC-AUSTENITIC STAINLESS STEELS[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1988, (4): 213-222.
    [10]Xu Xiangxing, Su Yi, Hou Chunxiao, Zhou Wei, Wu Tongru, Sun Ming, Li Xuguang. INFLUENCE OF SMALL AMOUNT OF NICKEL ON THE BRITTLE TRANSITION TEMPERATCURE OF GRANULAR BAINITIC WELDS[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1988, (3): 141-146.

Catalog

    Article views (370) PDF downloads (221) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return