LIU Xuesong, LI Shuqi, WANG Ping, MENG Lichun, Lü Renyuan. Fatigue failure analysis of 6N01-T5 aluminum alloy welded joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2009, (10): 25-28.
Citation: LIU Xuesong, LI Shuqi, WANG Ping, MENG Lichun, Lü Renyuan. Fatigue failure analysis of 6N01-T5 aluminum alloy welded joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2009, (10): 25-28.

Fatigue failure analysis of 6N01-T5 aluminum alloy welded joints

More Information
  • Received Date: June 01, 2009
  • To identify the main cause of fatigue failures of welded joints of 6N01-T5 aluminum alloy extrusions, fatigue tests were carried out upon 6N01-T5 aluminum alloy extrusions and their weld joints, and S-N curves and conditional fatigue limits of them were obtained.Microstructure and mechanical properties of the welded joints were investigated.The fatigue fractures of the joints were analyzed and thereby the characteristics of them were obtained.The results show that the microscopic structure of the joints is α-Al and pseudo eutectic made up of α-Al and Mg2Si;the defects of the joints are mainly gas cavities;there is a soften zone between HAZ and base metal which lead to fracture under dead-load but hardly to fracture failure;the main influence factors of fatigue performance are defects on the surface of weld and the surface condition of the weldment.
  • Related Articles

    [1]WEI Wei, MA Minze, ZHANG He, ZHAO Xingming, YANG Xinhua. Construction of the S-N curve evaluation model based on entropy for welded joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION. DOI: 10.12073/j.hjxb.20240909002
    [2]ZHOU Shaoze, GUO Shuo, CHEN Bingzhi, ZHANG Jun, ZHAO Wenzhong. Master S-N curve fitting and life prediction method for very high cycle fatigue of welded structures[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2022, 43(5): 76-82. DOI: 10.12073/j.hjxb.20211116002
    [3]WEI Guoqian, YUE Xudong, DANG Zhang, HE Yibin. S-N and IEFM combined fatigue life analysis for welded structures[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2017, 38(2): 23-27.
    [4]JI Kai, ZHANG Jing, XU Yusong. Fatigue properties of welded joints of New 6005A alloy with high copper content[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2017, 38(1): 95-98.
    [5]DAI Qilei, MENG Lichun, LIANG Zhifang, WU Jianjun, SHI Qingyu. Comparison of fatigue crack propagation behavior of friction stir welded and metal inert-gas welded A6N01 joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2015, 36(9): 9-12,38.
    [6]FAN Wenxue, CHEN Furong, XIE Ruijun, TANG Dafu. Analysis of vibration fatigue S-N curve on Q235B steel butt welded joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(8): 39-42.
    [7]ZHU Guoren, CHEN Song, WANG Zhenbao. Optimization of transition in stainless steel welding joints S-N curve breaking point[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(8): 35-38.
    [8]ZHAO Wenzhong, WEI Hongliang, FANG Ji, LI Jitao. The theory and application of the virtual fatigue test of welded structures based on the master S-N curve method[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(5): 75-78.
    [9]FAN Wenxue, CHEN Furong, XIE Ruijun, GAO Jian. Fatigue life prediction of transverse cross welded joint based on different S - N curve[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2013, (11): 69-72.
    [10]WANG Dong-po, WANG Ting, HUO Li-xing, ZHANG Yu-feng. Fatigue design curve of tubular joints treated by ultrasonic peening[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (3): 34-38.

Catalog

    Article views (315) PDF downloads (594) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return