BO Chunyu, YANG Yuting, CHOU Shuguo, ZHOU Shifeng. Solidification cracking mechanism of 690 nickeil-based alloy surfacing metal[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2007, (10): 69-72.
Citation: BO Chunyu, YANG Yuting, CHOU Shuguo, ZHOU Shifeng. Solidification cracking mechanism of 690 nickeil-based alloy surfacing metal[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2007, (10): 69-72.
shu

Solidification cracking mechanism of 690 nickeil-based alloy surfacing metal

  • Harbin Welding Institute, China Academy of Machinery Science and Technology, Harbin 150080, China

More Information
  • Received Date: May 23, 2007
    Graphical Abstract
    • Abstract
  • Trans-varestraint test was used to investigate the solidification cracking mechanism of 690 nickel-based alloy surfacing metal.Results show that, the solidification cracking susceptibility of 690 nickel-based alloy surfacing metal is closely correlated with the segregation process during welding, which is greatly influenced by Nb.The solidification temperature of 690 nickel-based alloy surfacing metal falls when the Ni, Nb-rich phases segregate on the grain boundary or subgrain boundary, which induces that the ductility decreases and the appearance is fined.Then, cracking initiates and expands along the finer grain boundary or subgrain boundary during the solidification process.Furthermore, in 690 nickel-based alloy surfacing metal, Mn weakens the negative influence of Nb on solidification cracking resistance to some extent by restraining the segregation effect of Nb, and then the cracking resistance is improved.
    • FullText(HTML)
    • References (0)
    • Related Articles

  • Related Articles

    [1]GUO Xiao, GU Yu, HAN Ying, XU Kai, WANG Yan, JIANG Yinglong. Study on cracking mechanism of Inconel 625 alloy surfacing metal[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2023, 44(11): 117-123. DOI: 10.12073/j.hjxb.20230403001
    [2]YANG Wenyan, FAN Ding, ZHANG Junxi. Formation mechanism and influencing factors of unstable metal transfer in high current MAG welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2023, 44(11): 110-116. DOI: 10.12073/j.hjxb.20230131001
    [3]TANG Wenshen, YANG Xinqi, LI Shengli, LI Huijun. Investigation on friction stir welding process of ferritic stainless steel and mechanism of defect formation[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2019, 40(6): 87-93,111. DOI: 10.12073/j.hjxb.2019400160
    [4]CHENG Shili, ZHONG Lisheng, BI Xiaojing. In-situ preparation and formation mechanism of dense WC reinforced iron-based composite layer[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2016, 37(3): 1-4.
    [5]LI Hui, CHENG Xiaonong, XIE Chunsheng, XIANG Hongfu, WANG Jiheng. Phase composition and formation mechanism of NiAl coating on CuCo2Be alloy by plasma spraying[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(6): 95-99.
    [6]LIU Duo, LANG Bo, SUN Daqian, YUAN Shidong. Mechanism of solidification cracking of resistance spot welded magnesium alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(5): 109-112.
    [7]FENG Guangjie, LI Zhuoran, Xu Kai, LIU Wenbo. Interface microstructure and mechanism of SiC ceramic vacuum brazed joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(1): 13-16.
    [8]PAN Chuan, YU Ping, XUE Zhenkui, TIAN Zhiling. Mechanism and influencing factors of spatter formation with self-shielded flux cored wire[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2007, (8): 108-112.
    [9]WANG Xue, GE Zao-xiang, CHEN Fang-yu, LI Chao-zhi. Fracture mechanism of 12Cr2WMoVTiB steel joint in low-temperature reheater tubes[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (9): 89-92,98.
    [10]ZHOU Fang-ming, QIAN Yi-yu, ZHANG Jing, LI GUI-peng. Grain refinement mechanism of gas tungsten arc welded joint of tantalum thin walled tube[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (6): 41-44,48.

Catalog

    Get Citation
    PDF
    XML
    Article views (236) PDF downloads (109) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    Related Articles

    Website Copyright © Editorial Office of Transactions of the China Welding Institution, Welding Journals Publishing HouseTel：0451-86323218Address：No. 2077, Chuangxin Road, Songbei District, Harbin

    Supported by: Beijing Renhe Information Technology Co. Ltd    Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return