WANG Xue, SHI Yu-xiang, REN Yao-yao, LAI Jing-ping. Study of cold cracking susceptibility of CO2 gas shielded arc welded SA106C cast steel using implant tests[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2004, (4): 77-80.
Citation: WANG Xue, SHI Yu-xiang, REN Yao-yao, LAI Jing-ping. Study of cold cracking susceptibility of CO2 gas shielded arc welded SA106C cast steel using implant tests[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2004, (4): 77-80.

Study of cold cracking susceptibility of CO2 gas shielded arc welded SA106C cast steel using implant tests

More Information
  • Received Date: February 15, 2004
  • Implant tests were performed on the SA106C cast steel welded using CO2 gas shielded arc welding,which intended to investigate the susceptibility of cold cracking (CR) and the fracture morphology.The results show that in the case of heat input being 16 kJ/cm and no preheating,the critical fracture stress of implant is 560 MPa,near to the value of tensile strength,consequently,its resistance to CR is so high that it can be welded without preheating.If the restraint stress is higer than tensile strength,the fracture will occur.The features of the fracture is typical hydrogen-induced crack (HIC).The rupture mode of the fracture is found to consist of sugar like intergrannular (IG) and quasi-cleavage (QCHE),some sharp,perfectly straight,short sub-crack can be also observed additionally.With the crack propagating,the content of hydrogen is cut down,as a result,the proportion of IG decrease,wheras those of QCHE and sub-crack increase signifcantly,and more plastic deformation appears clue in QCHE.The reason for high resistance to CR of SA106C cast steel is mainly due to the lower content of hydrogen of CO2 arc welding process,and also related to the microstructures and as-quenched hadness of over heated zone near the weld interface,which is largely bainite with hardness of 321 HV,less than critical hardness of 350 HV.
  • Related Articles

    [1]ZHANG Qunbing, NIU Jing, ZHAO Pengfei, HUANG Yong, LI Zhigang, ZHANG Jianxun. Influence of preheating temperature on cold cracking sensitivity of 12Cr10Co3W2Mo heat resistant steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2015, 36(4): 87-91.
    [2]LI Yajuan, JIA Peng, LI Wushen, XIE Qi. Establishment of cold cracking susceptibility criterion for X80 pipeline steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (4): 85-88.
    [3]YANG Jianguo, HUANG Luyong, ZHANG Yong, FANG Hongyuan. Mechanism of cold welding cracks in 30CrMnSi steel joints welded by TIG method[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2011, (12): 13-16.
    [4]TENG Bin, LI Xiaoyu, LEI Zhen, WANG Xuyou. Analysis on cold crack sensitivity of low alloy high strength steel weld by laser-arc hybrid welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2010, (11): 61-64.
    [5]HUANG Fuxiang, DU Zeyu, SUI Yongli, ZENG Huilin, GUO Xiaojiang. Study on cold cracking susceptibility of domestic X80 pipeline steel using implant tests[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2009, (4): 89-92.
    [6]ZHANG Guang-xian, ZHOU Zeng-da, CHEN Ren-fu, YIN Hai, LIU Ming-zhi. Research on simulation for surface tension transformation in CO2 arc welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (4): 68-72.
    [7]REN Zhen-an, ZHOU Zhen-feng, SUN Da-qian. Advance of Researches on the Cold Cracking of the Gray Cast Iron Cold-welding with Homogenous Welding Consumables[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2001, (1): 91-96.
    [8]HUANG Peng-fei, LU Zhen-yang, CHEN Shu-jun, YIN Shu-yan. Functions of Output Filter Inductor in CO2 Gas Shielded Arc Welding Inverteer[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2000, (2): 81-84.
    [9]Ren Zhenan, Sun Daqian, Zhou Zhenfeng. Microscopic Redistribution Behaviours and Bubbling-up Characteristic of Residual Diffusible Hydrogen in the Grey Iron Weldment[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1998, (4): 36-41.
    [10]Zhang Bingfan, Ma Yuanlin, Zeng Yuejian, Li Wushen. Effects of weld metals on cold crack resistance in HAZ for high strength steels[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1991, (1): 31-38.

Catalog

    Article views (225) PDF downloads (61) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return