ZHOU Li, ZHAO Hongyun, SHU Fengyuan, FENG Jicai. Numerical simulation of stress and strain during single-pass laser cladding copper on AlN base plate[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(9): 57-60.
Citation: ZHOU Li, ZHAO Hongyun, SHU Fengyuan, FENG Jicai. Numerical simulation of stress and strain during single-pass laser cladding copper on AlN base plate[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(9): 57-60.
shu

Numerical simulation of stress and strain during single-pass laser cladding copper on AlN base plate

  • 1.

    Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209, China;School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, China

  • 2.

    Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209, China

More Information
  • Received Date: March 21, 2013
    Graphical Abstract
    • Abstract
  • Cooling effect of shielding gas should not be neglected during laser cladding process. The fluid model was simplified by transforming thermal and convection problems into hydromechanics and conduction problems, respectively. Cooling type of shielding gas was investigated and the heat dissipation was quantitatively characterized. It was found that convection coefficient was several hundreds times of conduction coefficient.The evaluation results were adopted for calculation of stress and strain of copper powder and AlN matrix exposed to single-pass laser cladding. According to the first and third strength theory, three kinds of cracks were obviously found, including tear cracks in the interface, pull cracks on the upper surface of the base metal and transverse cracks in the cladding layer perpendicular to laser scanning direction. The forming mechanism of cracks was analyzed and the guidance for optimizing process parameters was proposed.
    • FullText(HTML)
    • References (0)
    • Related Articles

  • Related Articles

    [1]KONG Liang<sup>1,2</sup>, LING Zhanxiang<sup>1</sup>, WANG Ze<sup>2</sup>, WANG Min<sup>1,2</sup>, PAN Hua<sup>3</sup>, LEI Ming<sup>3</sup>. Study on influence factors of liquid metal embrittlement cracks in resistance spot welded joints of galvanized Q & P980 steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2018, 39(7): 37-41. DOI: 10.12073/j.hjxb.2018390171
    [2]WANG Bingying, YIN Yu, GAO Zhiwei, WANG Yaru. Effect of ultrasonic surface rolling processing on stress field at crack tip of pipeline steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2017, 38(1): 27-30.
    [3]ZHENG Shiqing, WEN Peng, SHAN Jiguo. Crack tendency and mechanical properties of ductile cast iron joint by fiber laser-MIG hybrid welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (8): 29-32.
    [4]HE Jun, ZHANG Binggang, ZHENG Kun, CHEN Guoqing. Niobium alloy electron beam surface cladding silicide coating crack control[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (6): 109-112.
    [5]LI Chao, LIANG Yuanyuan, SHEN Canduo, ZHU Sheng. Cracking formation mechanism of mild steel parts fabricated by surfacing rapid forming[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2010, (9): 53-56.
    [6]LIU Ji-xiong, LI Ping-he, WANG Yu-tao, CHEN Xiao. Analysis of crack produced in automatic SAW welding test of high-perfect fire-resistant and weathering resistant construction steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (6): 89-93.
    [7]Kang Jidong, Zhang Yufeng, Huo Lixing. Investigation on Crack Tip Strain Field of Welded Joint by Moire Interferometry[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1996, (2): 99-103.
    [8]Wang Shaoqing, Zhang Baochang, Jiao Wei, Ge Zhaoxiang. Cause of cracks in welded joints of higher-pressure deaerator made of 16MnR steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1994, (1): 16-22.
    [9]Chen Bingsen, Ma Weidian, Su Yi. FRACTURE PARAMETERS FOR A JOINT CONTAINING A TRANSVERSE CRACK IN THE LONGITUDINAT OVERMATCHED WELD[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1989, (3): 200-207.
    [10]Gu Jingjing, Wu Zuqian. CHEVRON CRACKING IN MEDIUM STRENGTH LOW ALLOY STEEL WELDS[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 1988, (1): 30-36.

Catalog

    Get Citation
    PDF
    XML
    Article views (261) PDF downloads (93) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    Related Articles

    Website Copyright © Editorial Office of Transactions of the China Welding Institution, Welding Journals Publishing HouseTel：0451-86323218Address：No. 2077, Chuangxin Road, Songbei District, Harbin

    Supported by: Beijing Renhe Information Technology Co. Ltd    Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return