LANG Bo, HOU Jinbao, WU Song. Microstructure and mechanical properties of IC10 single crystal superalloy transient liquid phase diffusion bonding joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (8): 109-112.
Citation: LANG Bo, HOU Jinbao, WU Song. Microstructure and mechanical properties of IC10 single crystal superalloy transient liquid phase diffusion bonding joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (8): 109-112.

Microstructure and mechanical properties of IC10 single crystal superalloy transient liquid phase diffusion bonding joint

More Information
  • Received Date: May 29, 2011
  • Microstructural evolution of transient liquid phase(TLP) diffusion bonding joint of IC10 single crystal superalloy was investigated with scanning electron microscopy(SEM) and energy-dispersive spectrum(EDS).The results show that the joint contained bonding zone and base material zone.The bonding zone consisted of isothermal solidification zone and rapid solidification zone.Rapid solidification zone could be eliminated by increasing welding time.The size of γ' phase in the base material reached 0.9 μm when the welding time increased from 2 h to 8 h.The mechanical properties of the joints can be effectively improved by restraining formation of grain boundary in TLP diffusion bonding joint and postweld solution treatment.The average tensile strength of the joints was 507 MPa at 1 000℃.The creep rupture life of the joints reached 120 h under the condition of 144 MPa stress at 1 000℃.
  • Related Articles

    [1]ZHANG Yongzhi, WANG Wei, HUANG Zhengqin, HUANG Jiahua. Effect of tungsten on microstructure and mechanical properties of nickel-based single crystal superalloy TLP diffusion bonding joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2024, 45(5): 98-104. DOI: 10.12073/j.hjxb.20230809003
    [2]LI Qi, LIU Fengmei, YUE Xiong, XIONG Min, YI Yaoyong, GAO Haitao. Effect of heat treatment on microstructure and high temperature properties of IC10 superalloy TLP diffusion welding under 80 μm gap[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2021, 42(5): 36-44. DOI: 10.12073/j.hjxb.20201209003
    [3]CHAI Lu, HOU Jinbao, ZHANG Sheng. Influence of process parameters on microstructure and properties of IC10 single crystal TLP joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2018, 39(8): 114-118. DOI: 10.12073/j.hjxb.2018390212
    [4]LANG Bo, HOU Jinbao, GUO Delun, WU Song. Transient liquid phase (TLP) diffusion bonded single crystal superalloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2015, 36(12): 93-96.
    [5]JING Yongjuan, LI Xiaohong, HOU Jinbao, YUE Xishan. Microstructure evolution of TLP bonding interface for Ti3Al based alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2013, (2): 71-74.
    [6]LI Xiaohong, MAO Wei, ZHONG Qunpeng, CAO Chunxiao, XIONG Huaping. Microstructure and stress-rupture property of TLP diffusion bonded DD3 single crystal superalloy joints[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (7): 1-4.
    [7]WU Song, HOU Jinbao, LANG Bo. Transient liquild phase diffusion bonding processing of Ni3Al single crystal superalloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2012, (2): 105-108.
    [8]CAO Jian, SONG Xiaoguo, ZHENG Zujin, FENG Jicai. Effect of diffusion time on interfacial microstructure of TLP joints of DD6 single crystal superalloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2011, (7): 13-16.
    [9]HOU Jinbao, ZHANG Lei, WEI Youhui. Microstructure and strength analysis of IC10 alloy TLP-DB joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (3): 89-92.
    [10]CHEN Si-jie, JING Xiao-tian, LI Xin-geng. Microstructure and properties of the T91 TLP bonded joint with different interlayer[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2006, (2): 77-82.

Catalog

    Article views (191) PDF downloads (86) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return