LI Sheng, ZENG Xiaoyan, HU Qianwu. The mechanism of strengthening and toughening of crack-free Fe-based alloy with high hardness for laser cladding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (7): 101-104.
Citation: LI Sheng, ZENG Xiaoyan, HU Qianwu. The mechanism of strengthening and toughening of crack-free Fe-based alloy with high hardness for laser cladding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (7): 101-104.

The mechanism of strengthening and toughening of crack-free Fe-based alloy with high hardness for laser cladding

More Information
  • Received Date: January 23, 2008
  • Crack-free laser-cladding layers with high hardness were obtained by using self-made Fe-based alloy powders for laser cladding without preheating and tempering.This paper revealed the mechanism of strengthening and toughening of the developed Febased alloy.The mixed martensite with medium carbon content contributes high hardness and high strength, as well as somewhat toughness; the retained austenite, which is distributed along grain boundaries, contributes excellent plasticity and toughness.The retained austenite can absorb and reduce the stress of the layers, and decrease the cracking susceptibility while it will not obviously decrease the hardness and strength of the cladding layers.
  • Related Articles

    [1]CAO Zhilong, ZHU Hao, AN Tongbang, WANG Chenji, MA Chengyong, PENG Yun. Analysis of the strengthening and toughening mechanism of deposited metal of 1000 MPa grade high strength steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2023, 44(7): 116-122. DOI: 10.12073/j.hjxb.20220609002
    [2]YIN Yan, PAN Cunliang, ZHAO Chao, ZHANG Ruihua, QU Yuebo. Formation mechanism of microstructure of laser cladding high chromium Fe-based alloy and its effect on microhardness[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2019, 40(7): 114-120. DOI: 10.12073/j.hjxb.2019400192
    [3]LIU Zhengjun, QIU Rongpeng, WU Dan, SU Yunhai. Research on toughening mechanism of weld metal with metal powder flux-cored wire for 960 MPa high strength steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2018, 39(1): 102-106. DOI: 10.12073/j.hjxb.2018390023
    [4]ZHANG Chunhua, LIU Jie, WU Chenliang, ZHANG Song, GUANG Meng, TAN Junzhe. Microstructue and zinc corrosion mechanism of laser cladding Co-based alloy on 316L stainless steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2015, 36(1): 19-22.
    [5]LI Meiyan, HAN Bin, GAO Ning, WANG Yong, SONG Lixin. Strengthening and toughening mechanism of laser cladding Fe-based coating on plunger surface[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2014, 35(2): 19-22.
    [6]LI Chonggui, FENG Xiaosong, LU Qinghua, ZHANG Peilei, YU Zhishui, WANG You. Strength and toughness of laser-remelted Al2O3-TiO2 coatings[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2013, (9): 63-66.
    [7]NIE Binying, YAO Chengwu. Effect of alloy elements on microstructure and phase structure of laser cladding Fe-based coatings[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2013, (1): 85-88.
    [8]ZHU Qingjun, ZOU Zengda, WANG Xinhong, QU Shiyao. Influence of rare earths on Fe-based amorphous composite coatings by laser cladding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (2): 57-60.
    [9]SHAN Ji-guo, DING Jian-chun, REN Jia-lie. Microstructure and Strengthening Mechanism of Light Beam Cladding Layer with Iron-based Self-fluxing Alloy Powder[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2001, (4): 1-4.
    [10]Huang Xuqiang, L× Chaoyang. A Study of Glass-Forming Conditions of Laser-Surface-Melted Fe-Ni-Si-B-V Alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2000, (1): 64-67.

Catalog

    Article views (303) PDF downloads (110) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return