WANG Ke-hong, ZHANG Chun-yang, ZHU Ping, Gu Min-le, ZHU Wu-ying. Interface strengthening process of Cr plating layer by plasma beam[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2005, (10): 75-77.
Citation: WANG Ke-hong, ZHANG Chun-yang, ZHU Ping, Gu Min-le, ZHU Wu-ying. Interface strengthening process of Cr plating layer by plasma beam[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2005, (10): 75-77.

Interface strengthening process of Cr plating layer by plasma beam

More Information
  • Received Date: July 28, 2005
  • One technological problem about the weak combination of interface between Cr plating layer and substrate which was strengthened by plasma had been put forward according to the application state of under serious ablation and erosion by hot chemical airflow.The technology using distransfer plasma to heat the steel workpiece with Cr plating layer at high speed was used to strengthen interface bonding between Cr plating layer and substrate.The principle of strengthening with plasma was introduced in this paper and the process experiment of strengthening with plasma arc was carried out.The experimental results measurement and analysis show that the metallurgical bonding has occurred between Cr plating layer and substrate and the strengthening of interface bonding between Cr plating layer and substrate is improved remarkablely.
  • Cited by

    Periodical cited type(1)

    1. 邵文东,赵尚超,李强,裴宪军,马巧艳,李向伟. 低周疲劳的结构应变法在铁路货车上的工程应用. 焊接学报. 2024(02): 113-120+135-136 . 本站查看

    Other cited types(3)

Catalog

    Article views (196) PDF downloads (63) Cited by(4)
    Turn off MathJax
    Article Contents

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return