XUE Song bai, DONG Jian, LÜ Xiao chun, QIAN Yi yu. Brazing technology of LY12 Al-alloy at middle temperature[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (3): 21-22,51.
Citation:
XUE Song bai, DONG Jian, LÜ Xiao chun, QIAN Yi yu. Brazing technology of LY12 Al-alloy at middle temperature[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (3): 21-22,51.
XUE Song bai, DONG Jian, LÜ Xiao chun, QIAN Yi yu. Brazing technology of LY12 Al-alloy at middle temperature[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (3): 21-22,51.
Citation:
XUE Song bai, DONG Jian, LÜ Xiao chun, QIAN Yi yu. Brazing technology of LY12 Al-alloy at middle temperature[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (3): 21-22,51.
Brazing technology of LY12 Al-alloy at middle temperature
The technology for brazing LY12 Al-alloy at middle temperature is realized by improved KF-CsF-AlF3 flux matching Ag-Al-Cu-Zn filler metal.The τ and σb strength values of brazed joints,are about 80% and 70% respectirely as compared with the base metal.A way out of the conclusion is found that heat-treated Al-alloy could not be brazed under normal conditions by the results.