ZHANG He, JIN Jun, JIANG Ping, ZHANG Fengdong, ZHANG Zhenpeng, ZHOU Zhikai. Study on microstructure and mechanical properties of 6061 aluminum alloy prepared by oscillating laser-arc hybrid welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2024, 45(1): 94-102. DOI: 10.12073/j.hjxb.20230205001
|
The oscillating laser-arc welding was carried out on the 6mm thick 6061 aluminum alloy locked bottom butt joint commonly used for the roof of high-speed rail, and the effect of oscillating frequency on the microstructure and mechanical properties of the weld was systematically studied based on SEM, EBSD and other characterization methods together with the penetration and porosity of the weld as indicators. The results showed that the porosity of the joint was reduced to less than 1% when the oscillating frequency sharply increased to 250 Hz. The weld area near the fusion line was primarily arranged with columnar dendritic structures, while the central arc region of the weld was chiefly composed of equiaxed dendritic structures. Laser oscillating frequency could affect the beam advance distance in per unit cycle, which posed a significant impact on the stirring action of laser beam behind the molten pool. With the increase of the oscillating frequency, the stirring effect of the molten pool was enhanced, which effectively refined the central equiaxed structures and dropped the dendrite sizes from 68 μm to 44 μm. The tensile strength reached their maximum value at the oscillating frequency of 250 Hz, with a maximum tensile strength of 229 MPa, which was about 73% of that of the base metal. Both the reduction of the porosity and the refined dendrites structures of the weld largely created favorable conditions for the improved tensile strength.
| [1] |
Bumgardner C H, Croom B P, Song N N, et al. Low energy electroplasticity in aluminum alloys[J]. Materials Science and Engineering:A, 2020, 798: 140235. doi: 10.1016/j.msea.2020.140235
|
| [2] |
蔡创, 谢佳, 刘致杰, 等. 铝合金摆动激光-MIG复合焊接特性及气孔控制[J]. 中国激光, 2021, 48(18): 17 − 26.
Cai Chuang, Xie Jia, Liu Zhijie, et al. Welding characteristics and porosity control of weaving laser-MIG hybrid welding of aluminum alloys[J]. Chinese Journal of Lasers, 2021, 48(18): 17 − 26.
|
| [3] |
Enz J, Kumar M, Riekehr S, et al. Mechanical properties of laser beam welded similar and dissimilar aluminum alloys[J]. Journal of Manufacturing Processes, 2017, 29: 272 − 280. doi: 10.1016/j.jmapro.2017.07.030
|
| [4] |
陈纪城, 陈小梅, 常怡婷, 等. 5056铝合金稳恒磁控激光深熔焊接过程熔池流动与传热行为分析[J]. 焊接学报, 2021, 42(3): 63 − 69.
Chen Jicheng, Chen Xiaomei, Chang Yiting, et al. Melt flow and thermal transfer of welding pool during static magnetic field supported deep-penetration laser beam welding of 5056 aluminum alloy[J]. Transactions of the China Welding Institution, 2021, 42(3): 63 − 69.
|
| [5] |
Song M J, Wu L S, Liu J M, et al. Effects of laser cladding on crack resistance improvement for aluminum alloy used in aircraft skin[J]. Optics & Laser Technology, 2021, 133: 106531.
|
| [6] |
Li S R, Mi G Y, Wang C M. A study on laser beam oscillating welding characteristics for the 5083 aluminum alloy: Morphology, microstructure and mechanical properties[J]. Journal of Manufacturing Processes, 2020, 53: 12 − 20. doi: 10.1016/j.jmapro.2020.01.018
|
| [7] |
Tao W, Yang S L. Weld zone porosity elimination process in remote laser welding of AA5182-O aluminum alloy lap-joints[J]. Journal of Materials Processing Technology, 2020, 286: 116826. doi: 10.1016/j.jmatprotec.2020.116826
|
| [8] |
Katayama S, Naito Y, Uchiumi S, et al. Physical phenomena and porosity prevention mechanism in laser-arc hybrid welding[J]. Welding International, 2007, 21(1): 25 − 31. doi: 10.1533/wint.2007.3680
|
| [9] |
张臣. 铝合金激光-电弧复合焊接等离子体光谱诊断及接头强化机制研究[D]. 武汉: 华中科技大学, 2014.
Zhang Chen. Spectrum diagnostic of plasma and joint performance improving mechanism of laser-arc hybrid welding of aluminium alloys[D]. Wuhan: Huazhong University of Science & Technology, 2014.
|
| [10] |
Fetzer F, Sommer M, Weber R, et al. Reduction of pores by means of laser beam oscillation during remote welding of AlMgSi[J]. Optics and Lasers in Engineering, 2018, 108: 68 − 77. doi: 10.1016/j.optlaseng.2018.04.012
|
| [11] |
Hu K, Muneer W, Zhang J H, et al. Effect of beam oscillating frequency on the microstructure and mechanical properties of dissimilar laser welding of AA2060 and AA6061 alloy[J]. Materials Science and Engineering:A, 2022, 832: 142431. doi: 10.1016/j.msea.2021.142431
|
| [12] |
祁小勇, 周京, 刘硕夫, 等. 5083铝合金摆动激光电弧复合焊工艺研究[J]. 航空制造技术, 2019, 62(6): 71 − 78. doi: 10.16080/j.issn1671-833x.2019.06.071
Qi Xiaoyong, Zhou Jing, Liu Shuofu, et al. Research on wobbling laser-arc hybrid welding of 5083 aluminum alloy[J]. Aeronautical Manufacturing Technology, 2019, 62(6): 71 − 78. doi: 10.16080/j.issn1671-833x.2019.06.071
|
| [13] |
Wang L, Liu Y, Yang C G, et al. Study of porosity suppression in oscillating laser-MIG hybrid welding of AA6082 aluminum alloy[J]. Journal of Materials Processing Technology, 2021, 292: 117053. doi: 10.1016/j.jmatprotec.2021.117053
|
| [14] |
杨文, 耿韶宁, 蒋平, 等. 铝合金中厚板高功率激光搅拌焊气孔缺陷工艺调控[J]. 焊接学报, 2021, 42(12): 26 − 33.
Yang Wen, Geng Shaoning, Jiang Ping, et al. Process control of the porosity defects in high power oscillating laser welding of medium-thick aluminum alloy plates[J]. Transactions of the China Welding Institution, 2021, 42(12): 26 − 33.
|
| [15] |
王磊. 高强铝合金振荡扫描激光束-电弧复合焊接工艺与机理研究[D]. 武汉: 华中科技大学, 2018.
Wang Lei. Oscillating laser beam-arc hybrid welding of high strength aluminium alloy[D]. Wuhan: Huazhong University of Science & Technology, 2018.
|
| [16] |
Chen L, Wang C M, Mi G Y, et al. Effects of laser oscillating frequency on energy distribution, molten pool morphology and grain structure of AA6061/AA5182 aluminum alloys lap welding[J]. Journal of Materials Research and Technology, 2021, 15: 3133 − 3148. doi: 10.1016/j.jmrt.2021.09.141
|
| [17] |
Han C, Jiang P, Geng S N, et al. Nucleation mechanisms of equiaxed grains in the fusion zone of aluminum-lithium alloys by laser welding[J]. Journal of Materials Research and Technology, 2021, 14: 2219 − 2232. doi: 10.1016/j.jmrt.2021.07.150
|
| [1] | WANG Xiaowei, ZHANG Bin, ZENG Ruchuan, YAN Zhaoyang, CHEN Shujun. Microstructure and mechanical properties of welds at keyhole closures in variable-polarity plasma arc welding of Al alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2024, 45(3): 1-6. DOI: 10.12073/j.hjxb.20230402001 |
| [2] | JIN Xiaokun, ZHANG Shichao, DIAO Wangzhan, DU Jinfeng, LIANG Jun, ZHANG Zheng. Effect of aging time on the microstructure and mechanical properties of the SP2215 steel welded joint[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2023, 44(9): 95-105. DOI: 10.12073/j.hjxb.20221028006 |
| [3] | LIU Jun, MENG Xianguo, LI Chenxi, LI Shuangji, SUN Zerui, LIU Hong. Microstructure and properties of 2219-T651 aluminum alloy welded joint by laser oscillating welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2023, 44(4): 7-13. DOI: 10.12073/j.hjxb.20220507001 |
| [4] | GUO Shun, WANG Pengkun, GU Jieren, PENG Yong, XU Junqiang, ZHOU Qi. Microstructure and mechanical properties of Ti6Al4V/B4C composite prepared by arc melting[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2022, 43(9): 62-68. DOI: 10.12073/j.hjxb.20220403002 |
| [5] | LIU Huijie, GAO Yisong, ZHANG Quansheng, ZHAO Huihui. Microstructure and mechanical properties of friction stir welded joint of 2A14-T4 aluminum alloy thick plate[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2022, 43(6): 20-24, 42. DOI: 10.12073/j.hjxb.20210615001 |
| [6] | WANG Hu, JIN Likun, PENG Yun. Microstructure and mechanical properties of joints of a new Al-Mg-Mn-Er alloy by TIG welding[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2020, 41(3): 74-79. DOI: 10.12073/j.hjxb.20190924002 |
| [7] | GAO Chong, LI Shulei, LIU Zhenshan, ZHAO Jingwei, ZHAO Pizhi. Effect of travel speeds on microstructures and mechanical properties of friction-stir welded 5754 aluminum alloy sheets[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2020, 41(2): 80-86. DOI: 10.12073/j.hjxb.20190921002 |
| [8] | ZHOU Li, ZHANG Renxiao, SHU Fengyuan, HUANG Yongxian, FENG Jicai. Microstructure and mechanical properties of friction stir welded joint of Q235 steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2019, 40(3): 80-84. DOI: 10.12073/j.hjxb.2019400076 |
| [9] | QIAO Jisen, YU Jiangrui, GOU Ningnian, YUAN Xiaoer. Development of microstructure influence on mechanical properties of fusion welding joints of aluminium alloy 2A12[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2011, (9): 5-8. |
| [10] | YANG Yang, CHEN Zhongping, LI Dahe, LIU Xiaohui. Microstructure and mechanical properties of Monel alloy copper explosive clad interface[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2008, (8): 53-56. |
Supported by:
Beijing Renhe Information Technology Co. Ltd
DownLoad: