7050铝合金搅拌摩擦焊接头超高周疲劳性能
Research on ultra-high-cycle fatigue properties of 7050 aluminum alloy FSW welded joints
-
摘要: 采用超高周疲劳试验系统研究7050-T7451铝合金搅拌摩擦焊接头的超高周疲劳性能. 试验结果表明，焊接接头在107周次以上仍然会发生疲劳失效，S-N曲线在108周次左右出现转折点，呈折线型下降；通过SEM对超高周疲劳断口形貌进行观察发现，当应力范围较高时，试件的疲劳裂纹往往在表面萌生，随着应力范围的降低，裂纹有亚表面和内部萌生的倾向；裂纹萌生位置取决于表面起裂和内部起裂相互竞争的结果；试件的断裂位置多为焊接接头的热力影响区和热影响区，EBSD和接头硬度的分析结果表明断裂位置与接头组织不均匀密切相关.
-
关键词:
- 铝合金|搅拌摩擦焊|超高周疲劳|断裂位置
Abstract: Ultra high cycle fatigue tests were used to test the fatigue property of 7050 aluminum alloy friction stir welding joint in the very high cycle regime. The results show that fracture still occurs in the welded joints after 107 cycles, and the S-N curves present multi-stage decreasing shapes with the turning point at about 108 cycles. The fatigue fracture morphology of specimen was observed by scanning electron microscope. It is found that fatigue cracks always initiated at the surface under the condition of high stress. However, fatigue crack initiation sites were inclined to transform from surface to subsurface or interior as cyclic loading decreased. The actual initiation sites depend on the competition mechanism of crack initiation from surface, subsurface or interior. Most of the specimens fractured at thermo- mechanical affected zone (TMAZ) and heat affected zone(HAZ). The fracture location is closely related to inhomogeneous microstructure of FSW joint through the EBSD and hardness analysis . -
-
[1] 佟建华, 张 坤, 林 松, 等. 搅拌摩擦焊和熔化极气体保护焊6082铝合金疲劳性能分析[J]. 焊接学报, 2015, 36(7): 105 ? 108
Tong Jianhua, Zhang Kun, Lin Song, et al. Comparison of fatigue property of 6082 aluminum alloy joint by friction stir welding and metal inert-gas welding[J]. Transactions of the China Welding Institution, 2015, 36(7): 105 ? 108[2] 何 超, 崔仕明, 刘永杰, 等. 气孔对铝合金焊接接头超长疲劳寿命的影响[J]. 焊接学报, 2014, 35(11): 18 ? 22
He Chao, Cui Shiming, Liu Yongjie, et al. Effect of pore on super long fatigue life of aluminum alloy welded joint[J]. Transactions of the China Welding Institution, 2014, 35(11): 18 ? 22[3] 王清远. 超高周加速疲劳实验研究[J]. 四川大学学报, 2002, 34(3): 6 ? 11
Wang Qingyuan. Accelerated fatigue testing by ultrasonic loading[J]. Journal of Sichuan University (Engineering Science Edition), 2002, 34(3): 6 ? 11[4] Mishra R S, Ma Z Y. Friction stir welding and processing[J]. Materials Science & Engineering R Reports, 2005, 50(1): 1 ? 78. [5] Sillapasa K, Surapunt S, Miyashita Y, et al. Tensile and fatigue behavior of SZ, HAZ and BM in friction stir welded joint of rolled 6N01 aluminum alloy plate[J]. International Journal of Fatigue, 2014, 63(63): 162 ? 170. [6] 吴良晨, 王东坡, 邓彩艳, 等. 超长寿命区间16Mn钢焊接接头疲劳性能[J]. 焊接学报, 2008, 29(3): 117 ? 120
Wu Liangchen, Wang Dongpo, Deng Caiyan, et al. Fatigue properties of welded joints of 16Mn steel in super long life region[J]. Transactions of the China Welding Institution, 2008, 29(3): 117 ? 120[7] Mughrabi H. On ‘multi-stage’ fatigue life diagrams and the relevant life-controlling mechanisms in ultrahigh-cycle fatigue[J]. Fatigue & Fracture of Engineering Materials & Structures, 2002, 25(8-9): 755 ? 764. [8] Takahashi Y, Yoshitake H, Nakamichi R, et al. Fatigue limit investigation of 6061-T6 aluminum alloy in giga-cycle regime[J]. Materials Science & Engineering A, 2014, 614(614): 243 ? 249. [9] Schwerdt D, Pyttel B, Berger C. Fatigue strength and failure mechanisms of wrought aluminium alloys in the VHCF-region considering material and component relevant influencing factors[J]. International Journal of Fatigue, 2011, 33(1): 33 ? 41. [10] Deng C, Wang H, Gong B, et al. Effects of microstructural heterogeneity on very high cycle fatigue properties of 7050-T7451 aluminum alloy friction stir butt welds[J]. International Journal of Fatigue, 2016, 83: 100 ? 108. -
期刊类型引用(11)
1. 庞嘉尧，程伟. 铝合金搅拌摩擦焊接头疲劳性能研究进展. 兵器材料科学与工程. 2025(01): 164-175 . 
百度学术
2. 金玉花，邢逸初，周子正，吴博. 喷丸改性对7050铝合金FSW接头性能的影响. 材料导报. 2023(10): 169-173 . 百度学术
3. 王龙权，周海涛. 7xxx高强铝合金搅拌摩擦焊研究进展. 焊接. 2023(10): 47-54 . 百度学术
4. 周韶泽，郭硕，陈秉智，张军，兆文忠. 焊接结构超高周疲劳主S-N曲线拟合及寿命预测方法. 焊接学报. 2022(05): 76-82+118 . 本站查看
5. 米鹏，王瑞杰，杨庆鹤. 5083铝合金带吻接FSW接头疲劳强度分析. 机械科学与技术. 2021(03): 463-469 . 百度学术
6. 张龙，陈东高，张迎迎，戴宇，马良超，王大锋，郭庆虎，何逸凡. 7B52-T6叠层铝合金焊接接头组织及疲劳损伤行为. 兵器材料科学与工程. 2021(02): 126-130 . 百度学术
7. 王池权，石亮，张祥春，刘志毅，邵成伟. 焊接缺陷对异种铝合金TIG对接接头疲劳行为的影响. 北京航空航天大学学报. 2021(07): 1505-1514 . 百度学术
8. 韦旭，汪建利，汪洪峰. 5052铝合金搅拌摩擦焊接的组织和力学性能. 兵器材料科学与工程. 2020(04): 77-80 . 百度学术
9. 马青娜，邵飞，白林越，徐倩. 7075铝合金FSW接头腐蚀疲劳性能及断裂特征. 焊接学报. 2020(06): 72-77+101 . 本站查看
10. 杨立恒，刘建军，张建国，陈大兵，李成钢. 浅析母线伸缩节焊接接头质量. 焊接技术. 2020(S1): 156-160 . 百度学术
11. 张铁浩，杨志斌，张志毅，张海军，史春元. MIG焊叠加对6A01-T5铝合金FSW焊接头组织及性能的影响. 焊接学报. 2020(09): 81-88+96+101 . 本站查看
其他类型引用(5)
计量
- 文章访问数: 743
- HTML全文浏览量: 6
- PDF下载量: 0
- 被引次数: 16
下载: