镀锌Q & P980钢电阻点焊接头液态金属脆裂纹的影响因素分析

孔谅1,2,凌展翔1,王泽2,王敏1,2,潘华3,雷鸣3

孔谅1,2,凌展翔1,王泽2,王敏1,2,潘华3,雷鸣3. 镀锌Q & P980钢电阻点焊接头液态金属脆裂纹的影响因素分析[J]. 焊接学报, 2018, 39(7): 37-41. DOI: 10.12073/j.hjxb.2018390171
引用本文: 孔谅1,2,凌展翔1,王泽2,王敏1,2,潘华3,雷鸣3. 镀锌Q & P980钢电阻点焊接头液态金属脆裂纹的影响因素分析[J]. 焊接学报, 2018, 39(7): 37-41. DOI: 10.12073/j.hjxb.2018390171
shu
KONG Liang1,2, LING Zhanxiang1, WANG Ze2, WANG Min1,2, PAN Hua3, LEI Ming3. Study on influence factors of liquid metal embrittlement cracks in resistance spot welded joints of galvanized Q & P980 steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2018, 39(7): 37-41. DOI: 10.12073/j.hjxb.2018390171
Citation: KONG Liang1,2, LING Zhanxiang1, WANG Ze2, WANG Min1,2, PAN Hua3, LEI Ming3. Study on influence factors of liquid metal embrittlement cracks in resistance spot welded joints of galvanized Q & P980 steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2018, 39(7): 37-41. DOI: 10.12073/j.hjxb.2018390171
shu

镀锌Q & P980钢电阻点焊接头液态金属脆裂纹的影响因素分析

  • 1. 上海交通大学 上海市激光制造与材料改性重点实验室, 上海 200240;
    2. 高新船舶与深海开发装备协同创新中心, 上海 200240;
    3. 宝钢研究院汽车用钢研究所 宝山钢铁股份有限公司, 上海 201900

基金项目: 国家重点研发计划资助（2017YFB0304400）

Study on influence factors of liquid metal embrittlement cracks in resistance spot welded joints of galvanized Q & P980 steel

  • 1. Shanghai Key Laboratory of Materials Laser Processing and Modification, Shanghai Jiaotong University, Shanghai 200240, China;
    2. Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai 200240, China;
    3. Baosteel Central Research Institute, Baosteel Group Corporation, Shanghai 201900, China

摘要

    摘要
  • 摘要: 新一代超高强Q&P淬火延性钢在具有高强度的同时具有较好的断后伸长率，在车身制造中具有广阔的应用前景.然而在对镀锌Q&P980钢进行电阻点焊试验后，在焊接接头中发现了表面裂纹，前期研究表明该表面裂纹是由液态金属脆化机制所引起的，即钢板在液态锌和应力的共同作用下发生的沿晶界开裂.结果表明，点焊中的工艺参数，包括焊接电流、焊接时间及电极压力、以及加工条件，包括电极端面形状、加压模式、电极对中度均会对接头中的液态金属脆裂纹产生不同程度的影响，因此可以通过调整工艺参数及加工条件来降低裂纹的敏感性.
    Abstract: The new generation ultrahigh strength Q & P (Quenching and Partitioning) steel owns both high strength and fine ductility, it has wide application prospect in automobile industry. However, after carrying out resistance spot welding experiment on the galvanized high strength Q & P980 steel plates, cracks were detected on the surface of joint, former researches showed that the cracks were caused by liquid metal embrittlement (LME), that was the steel plates were intergranular fractured under the effect of liquid zinc and stress. Experiment results indicated that process parameters (including welding current, welding time and electrode force) and process conditions (including electrode morphology, pressure mode and electrode alignment) were found to have influence on the LME cracks of joints. Thus, there is a possibility to reduce the crack sensibility by adjusting the process parameters and conditions.
    • HTML全文
    • 参考文献(5)
  • [1] 刁可山, 蒋浩民, 陈新平. 基于成形特性的宝钢QP980试验研究及典型应用[J]. 锻压技术, 2012, 37(6):113-115. Diao Keshan, Jiang Haomin, Chen Xinping. Research and typical application of QP980 steel produced by BaoSteel based on formability[J]. Forging & Stamping Technology, 2012, 37(6):113-115.[DOI: 10.3969/j.issn.1000-3940.2012.06.029]
    [2] Pouranvari M, Marashi S P H. Critical review of automotive steels spot welding:process, structure and properties[J]. Science and Technology of Welding and Joining, 2013, 18(5):361-403.[DOI: 10.1179/1362171813Y.0000000120]
    [3] Kim Y G, Kim I J, Kim J S, et al. Evaluation of surface crack in resistance spot welds of Zn-coated steel[J]. Materials Transactions, 2014, 55(1), 171-175.[DOI: 10.2320/matertrans.M2013244]
    [4] Ashiri R, Haque M A, Ji C W, et al. Supercritical area and critical nugget diameter for liquid metal embrittlement of Zn-coated twining induced plasticity steels[J]. Scripta Materialia, 2015, 109, 6-10.[DOI: 10.1016/j.scriptamat.2015.07.006]
    [5] Ashiri R, Shamanian M, Salimijazi H R, et al. Liquid metal embrittlement-free welds of Zn-coated twinning induced plasticity steels[J]. Scripta Materialia, 2016, 114, 41-47.[DOI: 10.1016/j.scriptamat.2015.11.027]
    • 相关文章
    • 施引文献(30)

  • 期刊类型引用(20)

    1. 李碧晗，王亦奇，汪瑞军. 微弧离子沉积技术研究现状与应用进展. 焊接. 2025(02): 55-65 . 百度学术
    2. 王明伟，高磊，郭昊亮，张文超. 纳米碳化钨涂层电火花沉积工艺参数试验研究. 热加工工艺. 2024(18): 74-78 . 百度学术
    3. 李梦楠，韩红彪，李世康，侯玉杰. 旋转电极接触力对电火花沉积放电过程参数和材料转移的影响. 焊接学报. 2023(01): 71-77+132-133 . 本站查看
    4. 李忠盛，吴护林，陈海涛，丛大龙，张敏，何庆兵，彭冬. 钢表面电火花沉积合成W-Mo高熔点复合涂层. 表面技术. 2023(10): 250-258 . 百度学术
    5. 张孟卓，姚利松，何星. 电火花沉积在金属耐磨防腐领域的应用研究进展. 材料保护. 2023(11): 102-117 . 百度学术
    6. 王彦芳，潘辰妍，石志强，何艳玲，韩彬. 块体高熵非晶合金的制备与表征综合实验教学探索与实践. 实验技术与管理. 2022(04): 142-146 . 百度学术
    7. 郝丽敏，葛志宏，都宇. 内圆表面的电火花合金化强化修复装置研究. 现代制造工程. 2022(06): 63-67+84 . 百度学术
    8. 何艳玲，王彦芳，斯佳佳，石志强. 电火花沉积Invar/非晶复合涂层的组织与性能. 金属热处理. 2022(11): 238-244 . 百度学术
    9. 田芳，纪秀林，严春妍，赵建华. 循环气压结合超声辅助封孔剂封孔处理对铁基非晶合金涂层摩擦磨损性能的影响. 腐蚀与防护. 2022(11): 1-6+53 . 百度学术
    10. 张勇，李丽，常青，王晓明，赵阳，朱胜，徐安阳，高宪伟. 电火花沉积技术研究现状与展望. 表面技术. 2021(01): 150-161 . 百度学术
    11. 高继文，李永彬，黄晓望. 超声波冲击法对微弧火花沉积涂层性能的影响. 焊接. 2021(02): 52-56+64 . 百度学术
    12. 王顺，童金钟，韩红彪. 一种电火花沉积接触力自动控制装置和沉积试验. 焊接学报. 2021(03): 42-47+100 . 本站查看
    13. 王顺，韩红彪，李世康，李梦楠. 基于正交试验的圆柱电极参数对电火花沉积质量影响分析. 焊接学报. 2021(07): 37-43+100 . 本站查看
    14. 刘宇，刘国良，苏全宁，曲嘉伟，王紫光，张生芳. 钛合金表面电火花沉积NiCr-3涂层性能的工艺规律研究. 电加工与模具. 2021(06): 26-30 . 百度学术
    15. 赵航，高畅，伍晓宇，徐斌，雷建国. 超声辅助电火花粉末沉积WC-Ni金属陶瓷涂层的微观结构及摩擦学性能. 机械工程学报. 2021(23): 252-261 . 百度学术
    16. 张建斌，张雷雷，刘航，容煜，焦凯，石玗. 电火花沉积修复铝合金组织与可降解性能. 表面技术. 2020(10): 224-232 . 百度学术
    17. 葛志宏，邓静. 用于回转体外表面的电火花强化修复装置研究. 电加工与模具. 2020(06): 29-31+47 . 百度学术
    18. 王彦芳，闫晗，李娟，孙胜越，宋增金，石志强. 电火花沉积FeCoCrNiCu高熵合金涂层的组织结构与耐蚀性. 表面技术. 2019(06): 144-149 . 百度学术
    19. 马焰议，王海燕，张宇鹏，易耀勇，董福宇. Zr_(67.8)Cu_(24.7)Al_(3.43)Ni_(4.07)非晶合金激光焊接晶化控制及组织性能分析. 焊接学报. 2019(12): 138-142+167 . 本站查看
    20. 钟鹏，司爽爽，宋增金，孙旭，石志强，王彦芳. 工艺参数对电火花沉积非晶层表面质量的影响. 热加工工艺. 2018(18): 125-128 . 百度学术

    其他类型引用(10)

    • 资源附件(0)
计量
  • 文章访问数:  956
  • HTML全文浏览量:  8
  • PDF下载量:  104
  • 被引次数: 30
出版历程
  • 收稿日期:  2017-09-18

目录

摘要
HTML全文
    参考文献(5)
    相关文章
    施引文献(30)
    资源附件(0)

    /

    返回文章
    返回

    网站版权 © 焊接杂志社焊接学报编辑部电话：0451-86323218地址：哈尔滨市松北区创新路2077号

    本系统由 北京仁和汇智信息技术有限公司 开发  百度统计