6061-T6铝合金的静止轴肩搅拌摩擦焊工艺及组织性能
Microstructures and mechanical properties of 6061-T6 aluminum alloy welded by stationary shoulder friction stir welding process
-
摘要: 采用自主研制的静止轴肩搅拌摩擦焊工具系统成功获得了6061-T6铝合金的对接接头. 对该接头的焊缝成形、显微组织、硬度分布以及拉伸性能分别进行了试验研究. 结果表明,SSFSW工艺所得6061-T6铝合金接头具有非常美观的焊缝成形,与常规的FSW工艺相比,几乎没有出现焊缝减薄的现象;焊缝组织分区也有明显的不同,TMAZ非常窄,只有几百微米;接头的硬度呈"W"形分布;在转速1 000 r/min,焊速为200 mm/min时,接头的抗拉强度和断后伸长率达到最大,分别为母材的71.5%和44.6%;拉伸试样均断裂在热影响区,它是接头发生断裂的最薄弱区域.Abstract: 6061-T6 aluminum alloy butt joints were successfully obtained by stationary shoulder friction stir welding SSFSW process using the self-developed tool system. Welding surfaces, microstructures, hardness profiles and tensile properties of the obtained joints were measured and studied, respectively. The results show that the obtained joints by SSFSW process had nice-looking appearances and smooth surfaces. Compared with conventional FSW, the phenomenon of the weld thickness reduction was almost eliminated. The microstructures of SSFSW joints were also significantly different. The thermomechanically affected zone was quite narrow, whose width was only a few hundred micrometers. The hardness profiles of obtained joints presented "W" shape. At the tool rotation speed of 1 000 rpm and the welding speed of 200mm/min, both the tensile strength and the elongation reached the maximum, which were up to 71.5% and 44.6% of the base material, respectively. All the joints were fractured at the heat affected zone, which was the weakest region.
-
-
[1] Martin J P, Stanhope C, Gascoyne S. Novel techniques for corner joints using friction stir welding[C]. Friction Stir welding and Processing VI. The TMS 2011 Annual Meeting and Exhibition. San Diego, California, USA. A John Wiley and sons lnc Publication. 2011: 179-188. [2] 刘会杰, 李金全, 段卫军. 静止轴肩搅拌摩擦焊的研究进展[J]. 焊接学报, 2012, 33(5): 108-112. Liu Huijie, Li Jinquan, Duan Weijun. Progress in the stationary shoulder friction stir welding[J]. Transactions of the China Welding Institution, 2012, 33(5): 108-112. [3] Davies P S, Wynne B P, Rainforth W M, et al. Development of microstructure and crystallographic texture during stationary shoulder friction stir welding of Ti-6Al-4V[J]. Metallurgical and Materials Transactions A, 2011, 42(8): 2278-2289. [4] Ahmed M M Z, Wynne B P, Rainforth W M, et al. Through-thickness crystallographic texture of stationary shoulder friction stir welded aluminium[J]. Scripta Materialia, 2011, 64(1): 45-48. [5] Widener C A, Talia J E, Tweedy B M, et al. High-rotational speed friction stir welding with a fixed shoulder[C]// Proceedings of the 6th International Symposium on Friction Stir Welding, Montreal. 2006. [6] Buffa G, Fratini L, Arregi B, et al. A new friction stir welding based technique for corner fillet joints: experimental and numerical study[J]. International Journal of Material Forming, 2010, 3(1): 1039-1042. [7] Li J Q, Liu H J. Design of tool system for the external nonrotational shoulder assisted friction stir welding and its experimental validations on 2219-T6 aluminum alloy[J]. The International Journal of Advanced Manufacturing Technology, 2013, 66(5-8): 623-634. [8] Li J Q, Liu H J. Effects of tool rotation speed on microstructures and mechanical properties of AA2219-T6 welded by the external non-rotational shoulder assisted friction stir welding[J]. Materials Design, 2013, 43: 299-306. -
期刊类型引用(22)
1. 顾苏怡,闵娜,詹恒辉. ZL101/6061铝合金搅拌摩擦焊接头组织及性能研究. 兵器材料科学与工程. 2024(05): 39-44 . 百度学术
2. 鲁克锋,殷凤仕,王文宇,滕涛,樊世冲,刘亚凡,王鸿琪,朱建,任智强. 铝合金搅拌摩擦焊接头缺陷及焊件结构问题控制策略的研究进展. 表面技术. 2023(07): 55-79 . 百度学术
3. 李充,田亚林,齐振国,王崴,杨彦龙,王依敬. 6082-T6铝合金无减薄搅拌摩擦焊接头组织与性能. 焊接学报. 2022(06): 102-107+119 . 本站查看
4. 杨新岐,元惠新,孙转平,闫新中,赵慧慧. 铝合金厚板静止轴肩搅拌摩擦焊接头组织及性能. 材料工程. 2022(07): 128-138 . 百度学术
5. 付文侦,贺地求,王海军,赖瑞林. 静止轴肩搅拌摩擦焊技术研究现状. 热加工工艺. 2022(15): 7-13 . 百度学术
6. 张军,王稳,王健,金涛涛,田志鹏. 静轴肩摩擦搅拌焊温度场仿真分析与参数优化. 中国机械工程. 2022(17): 2115-2124 . 百度学术
7. 朱志,郑森木,欧晓琴,余超,王向东,宋海滨,唐帅,苏乂南. 2219铝合金机器人静轴肩搅拌摩擦焊工艺研究. 航天制造技术. 2022(05): 25-29 . 百度学术
8. 祝宗煌,左立生,李泽阳,左敦稳. 一种搅拌头轴肩临界值的计算方法. 机械制造与自动化. 2021(01): 66-69 . 百度学术
9. 贺地求,刘朋,王海军,王东曜,赖瑞林. 2219-T6静轴肩辅助搅拌摩擦焊组织与性能分析. 湖南大学学报(自然科学版). 2021(08): 11-18 . 百度学术
10. 宋刚,程继文,刘振夫. 基于“热导拘束+局部变形强化”的铝合金焊轧复合成形方法. 机械工程学报. 2020(08): 85-91 . 百度学术
11. 牛海侠,朱松波,张琼,李蕾. A357铝合金的半固态触变压缩力学行为研究. 黄河科技学院学报. 2020(05): 41-46 . 百度学术
12. 褚强,郝思洁,Devang Sejani,Vivek Patel,李文亚. 静止轴肩搅拌摩擦焊接研究进展及展望. 电焊机. 2020(09): 44-52 . 百度学术
13. 姜月,柴玮,刘家伦,朱浩,王军. 7075铝合金搅拌摩擦焊接头变形行为及等效模型. 热加工工艺. 2019(09): 215-219 . 百度学术
14. 孙舒蕾,张会杰,赵晟伟,谢胜楠,吕洋. 搅拌摩擦焊焊缝表面凹陷现象控制方法研究现状. 精密成形工程. 2019(03): 138-143 . 百度学术
15. 郝云飞,马建波,毕煌圣,李超,王国庆. 铝合金T形接头静止轴肩搅拌摩擦焊接及组织性能分析. 焊接学报. 2019(07): 48-54+163 . 本站查看
16. 曾申波,陈高强,张弓,史清宇. T形接头角接静轴肩搅拌摩擦焊三维流动特征. 焊接学报. 2019(12): 1-5+161 . 本站查看
17. 王瑾,李送斌,张妍,陆艺. 焊接工艺参数对6061-T6铝合金静止轴肩搅拌摩擦焊组织及力学性能的影响. 焊接. 2019(11): 33-38+67 . 百度学术
18. 张铁浩,刘雪松,邢艳双. 搅拌摩擦焊修复ZL210铸造铝合金组织与性能分析. 焊接学报. 2018(04): 115-118+134 . 本站查看
19. 李丰,党鹏飞,刘雪松. 基于不旋转轴肩的铝镁异种材料搅拌摩擦焊. 焊接学报. 2018(05): 55-58+131 . 本站查看
20. 张华,赵常宇,林三宝,石功奇. 7050-T7451铝合金静轴肩搅拌摩擦焊接头组织与性能研究. 焊接. 2018(09): 5-9+65 . 百度学术
21. 李金全,刘会杰. 2219-T6铝合金静止轴肩搅拌摩擦焊接工艺及接头组织性能. 航天制造技术. 2017(06): 1-6+11 . 百度学术
22. 王敏,张会杰,张骁,于涛,杨广新. 一种新型零减薄搅拌摩擦焊工艺. 焊接学报. 2016(10): 37-40+131 . 本站查看
其他类型引用(15)
计量
- 文章访问数: 702
- HTML全文浏览量: 21
- PDF下载量: 316
- 被引次数: 37