Microstructure and properties of dual-wire arc additive manufacturing of Al-Mg-Zn-Cu-Sc alloy
-
摘要: 为改善Al-Zn-Mg-Cu铝合金电弧增材过程中出现的工艺和缺陷问题，利用双丝电弧增材技术，制备了Al-Mg-Zn-Cu-Sc合金. 根据电弧增材过程中的工艺以及成形情况，对该工艺中的送丝位置，送丝速度以及变极性频率等工艺参数进行分析. 通过工艺试验得到气孔含量较少和成型情况较好的参数并进行双丝电弧增材制造. 分析了不同扫描速度下的制备的Al-Mg-Zn-Cu-Sc合金组织以及力学性能，对微观组织和试样失效区域进行观察，确认了断裂类型和组织特点. 最终得到双丝电弧增材技术制备Al-Mg-Zn-Cu-Sc铝合金的工艺区间，明确了沉积态Al-Mg-Zn-Cu-Sc铝合金的基本组织特点.Abstract: The Al-Mg-Zn-Cu-Sc alloy was fabricated via dual-wire arc additive manufacturing to improve the processing and defect problem. According to the process stability and forming conditions and microstructure, the process parameters such as wire feeding position, wire feeding speed, and variable polarity frequency were studied. The parameters with less porosity and better forming conditions were obtained. The microstructure and mechanical properties of Al-Mg-Zn-Cu-Sc alloy prepared at different scanning speeds were analyzed. The microstructure and failure zone of the sample were observed, and the fracture types and microstructure characteristics were confirmed. Finally, the process range of Al-Mg-Zn-Cu-Sc aluminum alloy prepared by dual-wire arc additive manufacturing was obtained, and the basic microstructure characteristics of deposited Al-Mg-Zn-Cu-Sc aluminum alloy were defined.
-
0. 序言
在工件表面制备抗磨涂层是提高工件耐磨性的重要技术手段，而涂层的抗磨性取决于其化学成分和微观组织. 在涂层中添加增强相能够有效的提高涂层的耐磨性，因而成为研究的热点[1]. 目前，在涂层组织中作为增强相的颗粒主要有TiC，TiB2，TiN，NbC等，而颗粒的添加方式有外部添加和原位自生. 原位自生颗粒增强相因其具有界面干净、颗粒与基体结合力强、不容易脱落等优点，越来越引起研究者的重视[2-4]. 但原位自生颗粒增强相也存在着颗粒相团聚导致性能下降现象. 稀土具有改善组织、减少颗粒团聚的特性，能够提高材料的物理和化学性能，因而在冶金、铸造等领域应用广泛[5]. He和Feng等人[6-7]研究发现，在熔覆涂层中添加适量的稀土氧化物能有效的减少颗粒的团聚现象. Li等人[8]利用激光熔敷在Q235钢表面制备含有稀土CeO2的Co基熔覆层，试验结果表明，稀土CeO2含量为1.5%(质量分数)时，熔覆涂层耐磨性最佳；当稀土含量增加时，熔覆层耐磨性下降；Zhang等人[9]利用激光熔敷在Q235钢表面添加不同尺寸的CeO2的Ni基熔敷层，结果表明添加纳米CeO2熔覆层的硬度和耐磨性要高于添加微米CeO2的熔覆层. 文中利用氩弧熔覆技术，在原位自生TiC增强Ni基熔覆层中添加稀土Y2O3氧化物，探讨稀土Y2O3对熔覆层组织的影响规律，以提高熔覆层的性能.
1. 试验方法
1.1 涂层的制备
制备涂层选用的基体材料为热轧的16Mn钢，试样尺寸为100 mm×10 mm×10 mm，涂层材料选用的是Ni60A粉末(表1)、Ti粉、C粉、Y2O3粉末，涂层材料的成分配比见表2，粉末在研磨钵中研磨均匀. 采用丙酮对16Mn钢的表面进行去油处理，然后利用胶水作为粘结剂，将涂层粉末材料涂覆在预处理好的16Mn钢基材表面. 预制好涂层后，在100 ℃的RT3-15-9型电炉中烘干2 h. 采用氩弧熔覆方法制备熔覆涂层，氩弧熔覆利用MW3000型数字式焊机，熔覆工艺为：电流115 ~ 125 A，熔覆速度为3 mm/s，氩气流量10 L/min左右.
表 1 Ni60A自熔合金粉成分(质量分数，%)Table 1. Composition of Ni60A self-fluxing alloy powderCr Si B C Ni 7 ~ 18 3.5 ~ 5.5 3.0 ~ 4.5 0.5 ~ 1.0 余量 表 2 熔覆材料成分配比(质量分数，%)Table 2. Composition proportion of clad materials成分 Ni60A Ti粉 C粉 Y2O3 1 80 16 4 − 2 79 16 4 1 3 78 16 4 2 4 77 16 4 3 1.2 涂层的微观组织表征
将熔覆试件沿垂直于涂层的方向进行切割后制备金相观察试件，涂层的微观组织形貌采用MX2600型扫描电子显微镜(SEM)观察，并用其附带的OXFORD能谱分析仪分析相成分、结合区与基体、结合区与熔敷区的界面元素分布；采用RigakuD/max2200型X射线衍射仪(XRD)扫描涂层表面，测定涂层的物相组成.
1.3 涂层的性能测试
利用MHV2000型显微硬度仪在金相试件上测量由涂层到基体的显微硬度分布. 在MMS-2B磨损试验机测试摩擦磨损性能，试验参数为：磨损试验力为200 N，对磨环转速为200 r/min，磨损时间为40 min.
2. 结果与分析
2.1 涂层的物相组成和组织形态分析
原位自生TiC增强Ni基熔覆涂层的宏观形貌见图1所示，涂层与基体的截面能谱扫描如2所示，由图1和图2可以看出，涂层与基体之间的结合处无气孔、裂纹等缺陷，同时涂层与基体之间发生了Ti，Ni，Fe等元素的相互扩散，涂层与基体之间实现了冶金结合.
![]()
图 2 熔覆涂层与基体间界面线扫描Figure 2. Line scaning morphology of interface between cladding coat and base metalNi60A粉末、Ti粉、C粉在电弧高温的作用下可以生成多种化合物相，运用“无机热化学数据库(ITDB)”进行热力学数据检索和系列热力学计算结果如图3所示. 由图3可知，反应生成自由能小于TiC自由能的各相有Cr23C6，TiB2，Cr7C3，Cr5Si3，Ni4B等.
![]()
图 3 合金系中生成相自由能随温度的变化Figure 3. Free energy changes of forming phases with the temperature in alloy system对未加稀土Y2O3和添加2%稀土Y2O3的熔覆涂层的物相分析结果如图4所示. 两种复合涂层的物相均为γ-Ni，Cr23C6和TiC相，添加Y2O3后并没有新相生成. TiC相的存在说明氩弧熔覆过程中C和Ti元素原位反应生成了TiC. Ni60A合金粉中Cr含量较高，而且Cr23C6的反应生成自由能最低，所以很容易生成Cr23C6. 由于涂层材料中B，Si元素的含量较低，且反应生成自由能相对较高，在涂层中形成的含B，Si元素的化合物相的量很少，未被X-ray检测到. 虽然添加Y2O3后并没有新相生成，但是衍射峰值有所变化，添加稀土Y2O3后TiC和Cr23C6峰值有所增加，主要原因为稀土Y2O3促进形核所致.
![]()
图 4 氩弧熔覆涂层的XRD衍射图Figure 4. XRD patterns of cladding coatings by argon arc. (a) without Y2O3; (b) adding 2% Y2O3为确定涂层的微观组织，将添加2%Y2O3的熔覆涂层局部放大并进行能谱分析，如图5所示. 由图5可知，涂层的微观组织由黑色颗粒相(B)、灰色块状相(C)、黑白相间的网状组织(D)组成，部分黑色颗粒相中还存在白色的点状物(A). 不同物相的成分能谱分析的结果见表3. 结合物相分析黑色颗粒相为TiC，黑色颗粒中间的白色点为稀土Y，灰色块状相为γ-Ni基体，基体之间分布的网状为γ-Ni与Cr23C6共晶产物[10]. 从图可以看出，熔覆涂层的合金体系的组织形态为亚共晶组织形貌，先结晶相呈黑色形态. 随着结晶温度的降低，发生共晶反应生成灰白色基体上分布着黑色颗粒状的共晶组织.
表 3 不同位置颗粒相成分(质量分数，%)Table 3. Tab2 Composition of the particles phase in the coating位置 C Si Y Ti Cr Fe Ni A 28.45 2.02 33.24 30.19 1.84 3.07 1.20 B 27.22 0.93 2.15 62.31 2.39 3.71 1.30 C 5.73 1.35 − 0.82 3.66 15.81 72.64 D 5.94 0.50 − 1.08 10.38 5.78 76.32 2.2 Y2O3对涂层微观组织的影响
图6为不同稀土含量熔覆涂层的背散射组织形貌. 从图中可以看出，加入Y2O3后，涂层的组织形貌明显改善，Y2O3加入后，氩弧熔覆层中的TiC陶瓷相细小、分布较均匀. 相比而言，含2% Y2O3的涂层组织最为细小，硬质相TiC含量最多. 分析认为，氩弧熔覆凝固过程中，Y2O3的加入，改变了固液界面前沿的浓度分布，造成严重的成分过冷，进而改变了固液前沿的温度梯度，形成近枝晶形态的γ-Ni相. 同时Y2O3也会改变固态的熔点，在枝晶处富集的稀土会降低固溶体熔点，使枝晶熔断，在凝固过程中成为新的晶核而长大，从而细化晶粒. 另外，稀土元素在基体中的固溶度较小，化学活性较强，容易与Ni60A中的B，Si等元素发生化学反应形成稳定的化合物，增加熔覆层中TiC的形核质点，提高形核率，从而细化晶粒使其呈等轴状(图6c). 同时稀土元素对碳化物长大过程中相界面起到钉扎作用，阻碍其长大；稀土还会降低界面张力，减少晶粒长大的驱动力，导致晶粒长大速度减慢，从而也细化组织[11]. 但当Y2O3含量的添加量为3%时，熔覆涂层的组织形貌反而变差，TiC颗粒含量减少并出现团聚现象. 分析原因认为Y2O3加入过量时，稀土偏聚在TiC颗粒界面处，降低合金系的熔点[11]，在氩弧加热条件下，稀土偏聚处会加速TiC颗粒表面的熔化和分解，造成TiC颗粒烧损(图6d)，颗粒相的含量减少. 同时，稀土过量后TiC颗粒与基体界面过冷度会小，根据凝固理论，过冷度小，形核率小，长大速度快，所以TiC颗粒尺寸增大. TiC的生长基元为八面体，长大方式为棱边连接或顶角连接，在温度高即过冷度较小的条件下，晶体以二维形核方式长大会降低其表面能，所以TiC颗粒出现棱边连接或顶角连接长大，即团聚现象.
![]()
图 6 氩弧熔覆TiC增强Ni基涂层的组织形貌Figure 6. Structure of TiC coating by argon arc cladding. (a) 0%Y2O3; (b) 1%Y2O3; (c) 2%Y2O3; (d) 3%Y2O32.3 Y2O3对涂层性能的影响
图7为不同成分氩弧熔覆涂层从涂层到基体的显微硬度分布曲线. 由图可见，熔覆涂层的显微硬度最高，沿基体方向呈阶梯状递减，熔覆涂层显微硬度较基体提高3 ~ 7倍. 熔覆涂层之所以具有较高的显微硬度，首先是因为具有较高硬度的TiC陶瓷颗粒均匀而细小的分布在熔覆层中，其次是作为熔覆层基体的镍基固溶了大量的合金元素，起到明显的固溶强化作用. 由硬度分布曲线来看，距表面0 ~ 1.5 mm范围内的熔覆涂层具有较高的硬度，过渡区域在距涂层表面1.8 ~ 2.0 mm处. 从图中可以明显的看出Y2O3的加入量不同，涂层的硬度提高的程度亦不同. Y2O3含量2%的涂层硬度最高，硬度值大概为基体的4倍左右，也表现出优异的耐磨性能(如图8所示，磨损量最小). 涂层表现出的较高硬度及优异的耐磨性能主要与其中分布均匀而致密的TiC有关. 结合组织分析(图6)可以看出，加入Y2O3后涂层的组织细化，颗粒相含量有所增加，添加1%Y2O3的涂层中，颗粒相尺寸和含量明显优于没有添加Y2O3的涂层. 添加2%Y2O3的熔覆涂层的组织相比添加1%Y2O3的熔覆涂层组织更为细小，加之原位自生颗粒TiC与基体界面结合更为牢固，在摩擦磨损过程中不容易脱落，起到良好的支撑和耐磨作用，所以这两种涂层具有较高的硬度和耐磨性，添加2%Y2O3熔覆涂层的耐磨性较未添加Y2O3涂层提高0.5倍，较基体提高11倍. 但当添加3% Y2O3时，涂层的硬度值和耐磨性较未添加Y2O3的熔覆涂层有所降低，耐磨性较未添加Y2O3的熔覆涂层降低1.2倍，较基体提高2.6倍，主要原因为过多的稀土会降低氩弧熔覆熔池中液态合金的流动性，导致熔池中液体金属对流速度减慢，而且稀土较多时TiC颗粒大量烧损，颗粒相含量降低，并且TiC颗粒发生团聚现象(图6d)，导致熔覆涂层表面硬度和耐磨性较未添加稀土熔覆涂层的有所降低.
![]()
图 7 氩弧熔覆涂层的显微硬度Figure 7. Microhardness distribution of coatings by argon arc cladding![]()
图 8 不同Y2O3含量熔覆涂层的耐磨性能Figure 8. Wear resistance of cladding coatings with different Y2O3 contents3. 结论
(1) 原位自生TiC增强Ni基涂层的微观组织由TiC颗粒相、Ni基固溶体、γ-Ni与Cr23C6共晶相组成，添加Y2O3没有改变熔覆涂层中的物相组成.
(2) 在涂层材料中添加2%Y2O3能够使涂层组织细化、TiC颗粒分布均匀；过量的Y2O3使TiC颗粒团聚.
(3) 涂层材料中添加2%Y2O3，熔覆涂层具有较高的显微硬度，并且耐磨性能优异.
-
![]()
图 7 不同变极性频率下的孔隙占比变化
Figure 7. Variation of pore area percentage at different variable polarity frequencies
![]()
图 10 双丝电弧增材制备的Al-Mg-Zn-Cu-Sc合金微观组织
Figure 10. Microstructure of Al-Mg-Zn-Cu-Sc alloy prepared by dual wire arc additive manufacturing. (a) the microstructure of Al-Mg-Zn-Cu-Sc; (b) eutectic second phase in grains boundaries; (c) distribution of Al3Sc particles
![]()
图 12 不同扫描速度下的微观组织
Figure 12. Microstructures at different scanning speeds. (a) 100 mm/min; (b) 200 mm/min; (c) 300 mm/min
![]()
图 13 拉伸断口的表面
Figure 13. The fracture surface of the tensile tested sample. (a) characteristics of fracture; (b) the microstructure of fracture surfaces; (c) dimples in the fracture surface
表 1 焊接工艺参数
Table 1 Welding process parameters
等效电
流I/A电弧长度
h/mm层冷温
度T/℃扫描速度
v /(cm·min−1)变极性频率
f/Hz正负半
波比B(%)105 4 100 10 100 70 105 4 100 20 100 70 105 4 100 30 100 70 
下载: 导出CSV
表 2 丝材和基板成分(质量分数，%)
Table 2 Composition of welding wire and substrate
丝材 Al Zn Mg Cu Sc Mn Al-Zn-Mg-Cu 87.7 8 2 2.3 — — Al-Mg-Sc 92.7 — 6.3 — 0.3 0.7 基板 92.2 — 6.3 — — 0.5
下载: 导出CSV
-
[1] 王建国, 王祝堂. 航空航天变形铝合金的进展(3)[J]. 轻合金加工技术, 2013, 41(10): 1 − 14. doi: 10.13979/j.1007-7235.2013.10.020 Wang Jianguo, Wang Zhutang. Advancement in aerospace wrought aluminium alloys(3)[J]. Light Alloy Fabrication Technology, 2013, 41(10): 1 − 14. doi: 10.13979/j.1007-7235.2013.10.020
[2] Li Xiaoping, Liu Xiao, Li Runzhou, et al. Micrcstructure and property research on welded joints of 7XXX alumium alloy welding wire TIG for 7075 aluminum alloy[J]. China Welding, 2021, 30(4): 58 − 64.
[3] Zuo H, Li H, Qi L, et al. Influence of interfacial bonding between metal droplets on tensile properties of 7075 aluminum billets by additive manufacturing technique[J]. Journal of Materials Science & Technology, 2016, 32: 485 − 488.
[4] Kaufmann N, Imran M, Wischeropp T M, et al. Influence of process parameters on the quality of aluminium alloy EN AW 7075 using selective laser melting (SLM)[J]. Physics Procedia, 2016, 83: 918 − 926. doi: 10.1016/j.phpro.2016.08.096
[5] Martin J H, Yahata B D, Hundley J M, et al. 3D printing of high-strength aluminum alloys[J]. Nature, 2017, 549: 365 − 369. doi: 10.1038/nature23894
[6] Dong B L, Cai X Y, Lin S, et al. Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties[J]. Additive Manufacturing, 2020, 36: 101447. doi: 10.1016/j.addma.2020.101447
[7] Shao-Lu L, Pan Q, Chen X. Effect of Sc and Ti additions on microstructures and tensile properties of Al-Mg alloys[J]. Ordnance Material Science and Engineering, 2003, 01: 11 − 15.
[8] Milman Y V, Sirko A I, Lotsko D V, et al. Microstructure and mechanical properties of cast and wrought Al-Zn-Mg-Cu alloys modified with Zr and Sc[C]/Trans Tech Publications, Cambridge, 2002: 1217 − 1222.
[9] Zhu Z, Ng F L, Hang L S, et al. Superior mechanical properties of a selective-laser-melted AlZnMgCuScZr alloy enabled by a tunable hierarchical microstructure and dual-nanoprecipitation[J]. Materials Today, 2022, 52: 90 − 101. doi: 10.1016/j.mattod.2021.11.019
[10] Wang Z, Lin X, Kang N, et al. Making selective-laser-melted high-strength Al–Mg–Sc–Zr alloy tough via ultrafine and heterogeneous microstructure[J]. Scripta Materialia, 2021, 203(1-2): 114052.
[11] 潘伟. 原位强化的梯度钛合金电弧增材制造工艺及组织性能研究[D]. 兰州: 兰州理工大学, 2019. Wei P. Study on microstructure and properties of in-situ reinforced gradient titanium alloy by arc additive manufacturing[D]. Lanzhou: Lanzhou University of Technology, 2019.
[12] Bermingham M J, Kent D, Zhan H, et al. Controlling the microstructure and properties of wire arc additive manufactured Ti–6Al–4V with trace boron additions[J]. Acta Materialia, 2015, 91: 289 − 303. doi: 10.1016/j.actamat.2015.03.035
[13] Yu Z, Yuan T, Xu M, et al. Microstructure and mechanical properties of Al-Zn-Mg-Cu alloy fabricated by wire + arc additive manufacturing[J]. Journal of Manufacturing Processes, 2021, 62: 430 − 439. doi: 10.1016/j.jmapro.2020.12.045
[14] 何杰, 冯曰海, 张林, 等. 高强Al-Mg合金钨极氩弧双丝增材制造工艺与组织性能[J]. 焊接学报, 2019, 40(7): 109 − 113. doi: 10.12073/j.hjxb.2019400191 He J, Feng Y H, Zhang L et al. Research on microstructure and mechanical properties of high strength Al-Mg alloy fabricated by double-wire and gas tungsten arc additive manufacturing process[J]. Transactions of the China Welding Institution, 2019, 40(7): 109 − 113. doi: 10.12073/j.hjxb.2019400191
[15] Cai X Y, Dong B L, Yin X L, et al. Wire arc additive manufacturing of titanium aluminide alloys using two-wire TOP-TIG welding: Processing, microstructures, and mechanical properties[J]. Additive Manufacturing, 2020, 35: 101344.
[16] Li T X, Wang Z J, Zhen W Y, et al. Fabrication and characterization of stainless steel 308 L/Inconel 625 functionally graded material with continuous change in composition by dual-wire arc additive manufacturing[J]. Journal of Alloys and Compounds, 2022: 165398.
-
期刊类型引用(2)
1. 王永东，王金宇，常萌阳. Y_2O_3对原位自生TiC-TiB_2增强镍基复合涂层组织与性能的影响. 黑龙江科技大学学报. 2024(02): 230-236 . 
百度学术
2. 张宇鹏，王永东，徐刚，宫书林，汤明日，王磊. 石墨烯对激光熔覆Ti-C-Nb增强Ni基涂层组织与性能的影响. 激光与光电子学进展. 2022(01): 208-216 . 百度学术
其他类型引用(1)