Microstructure and properties of Fe-Cr-C-B-W alloy by self-shielded flux-cored wire open-arc surfacing
-
摘要: 采用自保护药芯焊丝明弧堆焊技术制备五组不同钨含量的Fe-Cr-C-B-W合金. 借助金相显微镜、扫描电子显微镜、X射线衍射仪、洛氏硬度计和磨损试验机分析堆焊合金的组织及性能. 结果表明，合金的显微组织由马氏体、残余奥氏体、M7(C,B)3，M3(C,B)，Fe3W3C和WC组成. 大部分钨元素被迁移到晶界生成了比WC稳定性更好的Fe3W3C缺碳复合相，堆焊层中没有典型的初生WC硬质相颗粒生成. 随着钨添加量的增多，共晶硬质相M7(C,B)3，M3(C,B)和Fe3W3C随之增多，间距减小，呈连续网状均匀分布. 当钨的添加量为12%时，堆焊层的耐磨性达到最佳.
-
关键词:
- 自保护药芯焊丝 /
- 明弧堆焊 /
- Fe-Cr-C-B-W合金 /
- 组织及性能
Abstract: Five Fe-Cr-C-B-W alloy samples with different W contents were prepared by self-shielded flux cored wire arc surfacing technology. Microstructure and properties of surfacing alloys were analyzed by metallographic microscope, scanning electron microscope, X-ray diffractometer, Rockwell hardness tester and wear tester. The results show that the microstructure of the surfacing alloy consists of martensite, retained austenite, M7(C,B)3, M3(C,B), Fe3W3C and WC. Most of W is migrated to the grain boundary to produce Fe3W3C C deficiency composite phase which is more stable than the WC. There are no typical primary WC hard phase particles in the surfacing layer. With the increase of W content, the eutectic hard phase M7(C,B)3, M3(C,B) and Fe3W3C increase, and the spacing decreases. And they are continuous and evenly distributed. When the addition amount of W is 12%, the wear resistance of the surfacing layer is the best. -
0. 序言
增材制造(additive manufacturing, AM)，也称3D打印，它结合了计算机辅助设计技术、材料加工和成形技术，利用软件和数控系统，基于数字模型文件快速制造实体物品[1-3]. 增材制造作为一种“自下而上”的制造技术，使过去受传统制造方法限制而无法实现的复杂结构件的制造成为可能. 近年来，增材制造得到了快速发展，在航空、航天、汽车、生物医学等领域得到了广泛应用[4]，其中，选区激光熔化、电子束熔化成形和激光烧结成形已经实现了商业化应用.然而，这些技术中使用的高能激光或电子束会熔化材料，导致许多问题，如氧化、晶粒粗大、残余拉应力等，严重影响其实际应用的发展[5].
冷喷涂(cold spraying, CS)作为一种新型的表面涂层技术，20世纪80年代由前苏联科学院西伯利亚分院理论与应用力学研究所发明，自2000年以来受到了越来越广泛的关注[6-9]. 冷喷涂过程中，金属粉末随着送粉气体和加热气体混合，经过专用Laval喷枪，被加速到300 ~ 1500 m/s后撞击在基体上产生剧烈的塑性变形实现颗粒和基体的有效结合.由于喷涂过程温度低于金属熔点，避免了原材料的相变、氧化、分解等问题. 大量研究表明，冷喷涂技术具有沉积效率高、沉积速度快等优点，不仅可以用于制备高性能涂层，而且在零件修复及块材制备方面也有独特的应用[10]，因此在2013年前后国际上出现了冷喷涂增材制造(cold spray additive manufacturing, CSAM)的说法[11-13]，后进一步称为冷喷涂固态增材制造.
目前，传统的增材制造已经可以实现产品较为精确的形貌控制[14-15]，但是CSAM并未像传统增材制造得到广泛应用，其中一个重要原因就是CSAM形貌控制研究的匮乏[16-18]. 基于实际应用中对产品精度和路径规划的需求，研究人员开始尝试解决形貌控制的问题[19-21]. CSAM的难点在于：①冷喷涂的主要结合方式为机械咬合[22-23]，喷涂颗粒只有在法向方向上的速度达到或超过临界速度Vcr时才能实现有效沉积[24-26]，喷涂角度的改变会引起法向速度的剧烈变化，当喷涂角度小于70°时往往难以实现有效喷涂[27]，然而在实际喷涂过程中，非垂直喷涂十分常见，如何根据所需形貌选择合适的喷涂角度是一个亟待解决的难题；②由于冷喷涂过程中颗粒分布的不均匀性，单道沉积体的厚度分布往往是中间厚边缘薄，因此沉积体表面经常会出现波浪状起伏，会引起沉积体性能的各向异性和表面精度的缺失；③传统增材制造对STL文件的切片路径规划并不能满足CSAM工艺过程，需要新的理论支撑和计算结果进行更为有效的路径规划.
CSAM沉积体形貌模拟的研究重点在于单道次喷涂下不同喷涂条件下的沉积体截面形貌拟合，以及复杂喷涂路径下高厚度沉积体形貌预测. 一般情况下，喷涂角度、喷涂距离、喷枪移动速度和基体表面形貌是CSAM形貌控制中最值得研究的方向[28]，用于研究CSAM沉积体形貌模拟与控制的数值模拟方法分为“试验法”和“模拟法”两种[29]. 试验法利用大量喷涂数据，分别分析各种喷涂条件的影响，总结喷涂条件与最终形貌的关系，然后再用于指导后续试验.模拟法通过建立合适的模型利用仿真软件数值模拟出最终沉积体形貌，如果预测准确的话就可以用于沉积体形貌控制.具体方法主要有以下4种：高斯法(Gaussian Model, GM)、人工神经网络法(Artificial Neural Network, ANN)、热喷涂工具包法(Thermal Spray Toolkit, TST)和克林科夫法(Klinkov Model, KM).还有一些方法研究较少，如卷积法(Convolution Method)和计算流体动力学法(Computational Fluid Dynamics, CFD)等. 通过对冷喷涂沉积体形貌的有效模拟，可以实现对目标复杂沉积体形状的合理喷涂路径规划，为制造独立成形的冷喷涂固态增材制造提供坚实基础.
1. 冷喷涂增材制造沉积体形貌模拟方法
1.1 高斯法
高斯法基于试验单点喷涂沉积体形貌进行函数拟合与模型假设，选择合适的函数类型和适当的沉积体累积方式，在连续移动喷涂时通过测量沉积体表面的平整度来反应拟合函数的准确性与累积方式的适用性，此模拟过程大多依托MATLAB平台实现.单点喷涂的沉积体形貌拟合函数集中于选择空间对称，如：高斯分布函数、柯西分布函数、β分布函数、抛物线分布函数和椭圆双β分布函数分别为
$$ f(x) = \frac{1}{{\sqrt {2\text{π} } \sigma }}{{\rm{e}}^{ - \tfrac{{{{(x - \mu )}^2}}}{{2{\sigma ^2}}}}} $$ (1) $$ f(x) = \frac{1}{\text{π} }\left[ {\frac{\gamma }{{{{(x - {x_0})}^2} + {\gamma ^2}}}} \right] $$ (2) $$ f(x) = \frac{1}{{B(\alpha ,\beta )}}{x^{\alpha - 1}}{(1 - x)^{\beta - 1}} $$ (3) $$ f(x) = C{\left( {1 - \frac{{4{x^2}}}{{{w^2}}}} \right)^{\beta - 1}} $$ (4) $$ f(x,y) = C{\left( {1 - \frac{{{x^2}}}{{{a^2}}}} \right)^{{\beta _1} - 1}}{\left[ {1 - \frac{{{y^2}}}{{{b^2}{{\left( {1 - \dfrac{{{x^2}}}{{{a^2}}}} \right)}^2}}}} \right]^{{y^{{\beta _2} - 1}}}} $$ (5) 式中：x，y分别为横、纵坐标；μ为均值；σ为标准差；x0为定义分布峰值位置的位置参数；γ，α，β，C，w为形状参数.沉积体累积方式研究重点在于，根据单点沉积形貌选择相邻喷涂道次合适的重叠率，与根据工件形貌进行合适的路径规划.
Chen等人[30]使用高斯法和任意拉格朗日欧拉法(Arbitrary Lagrangian-Eulerian, ALE)研究了沉积体累积模型和瞬时温度变化情况(图1)，沉积体累积模型采用考虑了喷枪移动速度、喷涂角度、相邻喷涂道次重叠率的优化后的高斯型分布.为了获得最佳相邻喷涂道次重叠率，施栩等人[31]使用牛顿迭代法，使得涂层厚度最大值和最小值的差值最小；王战中等人[32]在加入修正系数后得出喷涂轨迹重叠率在58.6%时沉积体表面最均匀；吴洪键等人[33]则假定轮廓拟合函数的二阶导数为零，此时重叠率约为66.7%. 董慧芬和冯浩等人[34-35]运用极坐标对球面喷涂进行了研究，同时使用遗传算法进行修正，为有限区域曲面喷涂提供了有效的仿真思路，霍平等人[36]也运用相似的解法在复杂曲面上得出一致结果.
![]()
图 1 喷涂时瞬时沉积体形貌与温度分布[30]Figure 1. Transient deposits profile and temperature distribution. (a) t = 3 s; (b) t = 6 s; (c) t = 8 s; (d) t = 9.6 s; (e) t = 14.6 s; (f) t = 33 sDuncan等人[37]通过抽样理论把喷涂路径规划问题转化成为空间频域，并证明倾斜光栅图案也可以形成连续的路径，当喷涂颗粒的分布改变时此种方法较为适用. Tzinava等人[38]基于MATLAB平台编程出一款适用范围广泛的喷涂模拟器，算法运用目前增材制造三维模型的STL文件保存模型的顶点与位矢信息，分别计算STL文件中每个表面三角形法向量和喷枪位置向量的关系来实现表面沉积判断，算法流程如图2所示，其中使用的拟合函数为高斯分布函数，同时可以实现喷涂路径中遮挡物的有效判断，初步为表面修复提供有效依据.Nault等人[39]假设冷喷涂沉积体为层层连续沉积形成，并使用速度补偿对基体表面曲率改变时的沉积体厚度进行修正，实现了任意凸起表面的沉积，如图3所示，优化后的沉积体形貌明显与实际喷涂效果更加接近.
![]()
图 3 凸起表面基体沉积[39]Figure 3. Deposits on substrate convex angle. (a) deposits on substrate with 30° corner; (b) comparison of deposits profile under different spraying strategies高斯法的优势在于对于沉积体表面形貌模拟非常直接，并且在试验数据拟合的基础上可以达到99%的准确性，不需要进行复杂的理论推导，且操作简单，但是其缺点则更为明显.首先，在实际喷涂过程中，连续移动喷涂的沉积体形貌应由单点喷涂积分而来或推导而来，但是在实际研究中常常将单点喷涂的形貌和连续移动喷涂的沉积体形貌混淆，并且由于沉积效率在喷涂过程中会发生剧烈改变，更加大了实际形貌与模拟形貌的差异；其次，对于相邻喷涂道次重叠率优化研究的准确性存疑，先喷涂的沉积体会影响后续喷涂的基体表面形貌，但是冷喷涂的沉积效果对于基体表面形貌十分敏感，因此单纯的将两个喷涂道次叠加并不合适，而且缺少试验验证；最后，高斯法并不能描述沉积体形貌演变情况，特别是出现非对称的形貌轮廓时，难以用函数进行拟合.由于以上缺点的存在，使得高斯法对于冷喷涂沉积体形貌模拟的准确性存在先天不足，然而由于其简单易操作，喷涂路径规划的模拟与优化往往会选择高斯法作为沉积体形貌的试验算法，大大提高了计算效率.
1.2 人工神经网络法
ANN是由大量神经元相互连接而成的运算模型，通过模拟神经元信息传递的方式来反应不同影响因素对最终结果的影响水平，在面对非线性运算的预测具有独特优势. ANN通常分为以下3个层次：输入层、隐藏层和输出层，如图4所示[40]，其中xn为输入向量的各个分量，hk为隐藏层的神经元，ym为输出向量的各个分量，wjn为权重，b为偏置向量，f为激励函数，每个神经元代表一个特定的输出函数(激励函数)，由不同权重连接. 对于冷喷涂而言，通过改变不同喷涂条件的权重与迭代次数，使模拟结果与实际喷涂收集到的数据相符，可以直观地反映各喷涂条件的影响水平，并在条件改变时对沉积体形貌进行预测.
Ikeuchi等人[41-42]首先将ANN应用到冷喷涂沉积体形貌的预测中，并成功地模拟出了喷涂角度、喷枪移动速度和喷涂距离的影响，以不同喷涂条件的沉积体形貌轮廓作为原始数据库(即输入层)，如图5所示. 当喷涂角度86°、喷涂速度75 mm/s、喷涂距离45 mm 时37号样品和当喷涂角度48°、喷涂速度34 mm/s、喷涂距离41 mm时39号样品的输出结果如图6所示，其中黑色线条为实际喷涂沉积体轮廓形貌，红色线条为ANN法模拟出的沉积体轮廓形貌，与高斯法的蓝色线条相比，ANN更能够对喷涂轨迹进行有效预测，特别在边缘区域的预测更为贴近实际形貌，在喷涂角度改变时会更加明显，有效展现出ANN方法在对非对称轮廓形貌预测的先进性，且相关系数R2 = 0.9493，展现出足够的有效性与稳定性.
![]()
图 5 不同喷涂条件对沉积体形貌的影响[42]Figure 5. Influence of different spraying conditions on the profile of deposit. (a) spraying angle; (b) traversing speed; (c) standoff distance![]()
图 6 不同喷涂条件下沉积体实际形貌与人工神经网络法及高斯法模拟形貌对比[42]Figure 6. Comparison of deposits profile between ANN method and Gaussian Model under different spraying conditions. (a) sample 37; (b) sample 39得益于人工智能的快速发展，在证明了ANN法的可行性后，后续对ANN的研究中，学者们倾向于优化隐藏层对数据的处理方式，通常有两种优化方向：提高数据的利用效率和算法优化. 对于提高数据的利用效率，即使得输入层数据的利用更加合理，如Mahapatra等人[43]利用反向传播算法(Back Propagation Algorithm)对脉冲激光粉末沉积的非线性多元沉积过程进行了有效模拟，Xiong等人[44]使用二阶回归模型(Second-Order Regression Model)对丝材电弧增材制造过程进行了模拟，结果表明，通过对原始输入层数据利用的优化可获得更加准确的结果. Chen等人[45]通过结合高斯法，加入拟合沉积效率函数来提高输入层数据的利用效率，有效研究了喷涂角度和喷枪移动速度对沉积体形貌的影响，结果表明，随着喷涂角度由垂直转向非垂直，厚度最高点出现了明显的偏移，并且沉积效率逐渐下降，整体厚度出现逐渐降低的趋势，如图7所示. 而随着喷枪移动速度的增加，整体厚度同样出现逐渐降低的趋势，但厚度最高点并不会出现偏移，如图8所示. Ikeuchi等人[41]证明除了喷涂角度和喷枪移动速度外，喷涂距离仍然适用于此方法，并且发现ANN法和高斯法的复合方法具有更高的精度.对于算法优化，董一萱等人[46]将海洋捕食者算法(Marine Predators Algorithm, MPA)结合ANN方法，通过建立与ANN方法的并行架构，对ANN模型隐藏层中的权重和阈值进行优化，在降低了迭代次数，大大提高运行速度和运行效率的同时，最终运算结果相关系数达到0.9986，证明MPA-ANN方法对于冷喷涂沉积形貌预测具有更佳的准确性.
![]()
图 7 不同喷涂角度下单点沉积体形貌轮廓试验结果与ANN方法模拟结果对比[45]Figure 7. Profile comparison of single spot spraying deposit between experiments and ANN method at different spray angles. (a) spraying angle of 90°; (b) spraying angle of 80°; (c) spraying angle of 70°; (d) spraying angle of 60°![]()
图 8 不同喷枪移动速度单道沉积体形貌轮廓实验结果与ANN方法模拟结果对比[45]Figure 8. Comparison of deposits profile between experiments and ANN method under different traversing speed. (a) traversing speed 300 mm/s; (b) traversing speed 200 mm/s; (c) traversing speed 150 mm/s; (d) traversing speed 100 mm/s; (e) traversing speed 50 mm/s; (f) deposits thicknessANN方法的优势在于结果导向，操作逻辑较为简单，不需要对具体喷涂过程进行较为复杂的研究，研究的重点在于如何提高数据利用效率和优化算法以获得更优的结果，第二是可以有效模拟出喷涂过程中沉积体形貌的演变过程.劣势在于，首先，在使用ANN方法前需要收集足够的样本数据，会耗费大量的工作，Liu等人[47]通过测量实时形貌作为新的样本数据填充到数据库之中，大大的扩充了样本数据量，然而仍旧不能解决样本数据难以收集的问题；其次，在增材制造应用中，立体成形十分常见，而三维形貌模拟势必是发展的重点，而ANN模型只对输出二维模拟结果较为有效；此外，神经网络模型的另一个劣势是缺乏合适的物理基础，因此，当实际喷涂时出现遮挡物，或者需要对喷涂路径进行规划时，ANN法无法进行有效处理；最后，目前的算法容易陷入局部最优解，仍需优化.
1.3 热喷涂工具包法
热喷涂工具包法是基于ABB公司发布的RobotStudioTM平台，用C#语言开发的插件工具包，本身分为3个模块：路径工具包(PathKit)、形貌工具包(ProfileKit)和监控工具包(MonitorKit)[48-49]. PathKit依托RobotStudioTM平台强大的机器人仿真能力，用于对喷涂路径进行规划和仿真，ProfileKit用于对喷涂沉积体形貌仿真，MonitorKit则是对喷涂轨迹进行实时监控.一般情况下，在ProfileKit中通过改变沉积体形貌的物理模型可以获得不同的沉积体形貌，后续学者对TST方法的研究也大多集中于对此模块的优化.
TST方法原本是为热喷涂而设计的，如Deng等人[50]利用TST工具包在复杂曲面上应用机器人离线编程实现热喷涂仿真，Cai等人[51]首次将该方法应用于冷喷涂沉积体形貌的预测，并提出除了单点喷涂沉积体形貌的影响因素，如：喷涂角度、喷涂距离、基体特点等，会影响连续移动喷涂时的沉积体形貌，同时喷涂机器人运动学参数如：喷枪移动速度，喷涂路径规划也具有重要影响，成功在2D条件下，总结出喷涂路径规划和喷涂距离对沉积体表面平整度的影响. 目前TST方法在研究方向集中于实现沉积体形貌的三维仿真，实际喷涂过程仿真(如喷涂路径出现遮挡)以及沉积体形貌控制与优化. Chen等人[45]将TST方法从2D拓展到3D，成功模拟出喷涂角度对对沉积体形貌的影响，如图9所示，当喷涂角度开始减小，厚度分布出现偏移，沉积效率下降，并在试验中得到了验证，除此之外，Chen等人[45]还对沉积体表面平整度进行了模拟研究，结果表明当相邻喷涂道次重叠率减小时，能有效提高沉积体表面平整度.Wu等人[18]通过对单点喷涂的轮廓进行高斯分布拟合并进行分块化处理(图10)，实现了复杂曲面的喷涂，如图11所示. 另外，当喷涂路径出现遮挡物后，运用此方法也可以实现有效模拟，使得TST方法能够在复杂的阶梯表面，当存在阴影遮挡效应时准确预测冷喷涂沉积体形貌的演变，如图12所示.
![]()
图 9 不同喷涂角度沉积体形貌3D模拟[45]Figure 9. 3D simulation of single spot deposit profile at different spray angles. (a) θ = 90°; (b) θ = 80°; (c) θ = 70°; (d) θ = 60°![]()
图 10 沉积形貌预测流程[18]Figure 10. Schematic diagram of depositing process. (a) planar creation of rays and intersection; (b) planar creation of cylinders; (c) planar single deposit profile; (d) non-planar creation of rays and intersection; (e) non-planar creation of cylinders; (f) non-planar single deposit profile![]()
图 11 复杂曲面冷喷涂[18]Figure 11. Complex surface spraying. (a) discrete single deposit profile while overlapping; (b) continuous single deposit profile on flat surface; (c) continuous single deposit profile on curved surface; (d) continuous single deposit profile on complex stair surface![]()
图 12 阶梯状连续冷喷涂[18]Figure 12. Continuous deposition on stair-like substrate with shadow effect. (a) actual profile; (b) simulation profileTST方法的优点如下：①在于能够对整个喷涂过程进行有效仿真，特别是对于喷涂机器人运动学参数监控十分有效，使得仿真过程更加贴近实际喷涂过程；②ProfileKit模块是基于合适的物理模型，因此相比较于ANN方法，TST方法的适用性更强；③TST方法能够实现3D模拟，可以更加直观的展示沉积体形貌，而其它方法目前则大多为2D或者准3D的.TST方法的缺点：①由于提前对单点喷涂沉积体形貌进行了函数拟合和假设，因此，缺乏足够的实验验证，准确性不如ANN方法，并且对于非对称分布的轮廓形貌无法处理；②在于TST方法的平台局限性，其只能在RobotStudioTM平台实现，学者对于后续的优化以及编程开发会十分困难.
1.4 克林科夫法
从本质上讲，克林科夫法是在平面冷喷涂过程中的数学推导模型，成功地从解析方面描述了喷涂沉积体形貌随喷涂角度变化的规律. Klinkov等人[52-53]认为喷涂角度是沉积效率最大的影响因素，因此可以把沉积效率看作以喷涂角度为自变量的函数，更准确一些，沉积体的厚度增长速率是沉积体表面的斜率和颗粒分布的函数，即
$$ \frac{{\partial y}}{{\partial t}} = ag\left( {\frac{{\partial y}}{{\partial x}}} \right)h(x,{x_0}) $$ (6) 式中：
$y$ 为沉积体厚度；$t$ 为时间；$a$ 为系数；$g\left( {{{\partial y} \mathord{\left/ {\vphantom {{\partial y} {\partial x}}} \right. } {\partial x}}} \right)$ 为关于涂层斜率的函数；$h\left( {x,x_0} \right)$ 为颗粒分布函数. 当颗粒分布为高斯分布时，通过微分方程求解.$$ {{DE}}(\tan\varphi ) = \left\{ \begin{array}{l} \frac{{{{\rm{e}}^{ - k{{\left( {\dfrac{{\tan\varphi }}{{\tan{\varphi _m}}}} \right)}^2} - {{\rm{e}}^{ - k}}}}}}{{1 - {{\rm{e}}^{ - k}}}},\tan\varphi < \tan{\varphi _m} \\ 0{\text{ }},\tan\varphi \geqslant \tan{\varphi _m} \end{array} \right. $$ (7) 式中：
${{DE}}$ 为沉积效率函数；$\tan\varphi = \partial y/\partial x$ ，${\varphi _m}$ = 50°为临界沉积角度，此时$\tan{\varphi _m} = 1.2$ ，$k = 4.5$ 为通过试验测量的公认经验系数. 此方法给出了平面喷涂的二维解析解，结果显示随着喷涂角度的改变，沉积体厚度分布产生了明显倾斜，数值解与解析解相统一，如图13所示，初始轮廓为高斯型分布的数值解(黑色)，初始轮廓为抛物线分布的解析解(红色)，其中1为喷枪方向. Klinkov等人[52-53]也利用这一结果为增材制造提供了路径规划的思路，如：对于垂直墙壁的增材制造可以首先在基体上垂直喷涂，之后倾斜喷枪分别在沉积体的侧面进行倾斜喷涂，以此循环可实现薄壁的有效沉积.克林科夫法从数学建模的角度出发，给出了冷喷涂沉积过程的解析解，具有很强的物理基础. 尽管该模型足够严谨，但其缺点限制了此方法的广泛应用.首先，基体表面必须为平面. 当喷嘴与喷涂表面之间存在遮挡时，阴影遮挡效应的存在使得克林科夫法无法应用. 其次，克林科夫法的推导是建立在颗粒分布为高斯分布的基础上，求解过程使用的函数简化技巧对其他分布情况难以适用.由于这些原因，克林科夫法大多被认为是冷喷涂沉积形貌演化过程的数学或物理推导模型，可以为其他的模拟方法提供理论基础. 如Vanerio等人[54]以克林科夫法为推导基础，有效地模拟了冷喷涂沉积过程中沉积体准3D形貌的演变过程，分别实现了喷涂沉积次数、喷涂距离、喷枪移动速度、基体表面形状对沉积体形貌的影响，并且克服了在非平面基板上无法实现阴影遮挡效应的难点，如图14所示.
![]()
图 14 阴影遮挡效应的实现[54]Figure 14. Shadow effect. (a) geometric shape of the substrate; (b) schematic diagram of spraying; (c) comparison of profile after 20 passes; (d) cross-sectional view after 20 passes; (e) side view of deposits; (f) profile of deposits1.5 不同形貌模拟方法对比
高斯法的优势在于计算方法简洁高效，常常作为其它方法的沉积体轮廓假设基础，大大提高了计算效率，但是由于高斯法的研究基础是基于理想条件下，因此面对形貌演变、复杂曲面喷涂和非空间对称的颗粒分布情况则较为受限，同时局限于2D模拟很能推广到3D. ANN方法以大量的试验数据为基础，具有十分强大的准确性与数据支撑，然而物理模型的缺失使得此方法拓展到不同应用情况时十分困难，而且同样不能进行3D模拟. TST方法在喷涂时充分考虑了喷涂机器人动态参数，有效反应了实际喷涂情况，可以实现复杂曲面的喷涂和3D仿真，但是编程的困难与平台的制约导致了目前的轮廓假设仅限于高斯型分布，需要后续对ProfileKit模块更详细的拓展. 克林科夫法作为一种解析方法，以物理建模为根本详细的揭示形貌演变情况，但是求解的困难阻碍了复杂曲面喷涂和非高斯型分布的应用.表1总结了各方法的特点.
表 1 不同方法特点对比Table 1. Comparison of characteristics of different methods特点 高斯法 ANN TST 克林科夫法 3D — — √ — 物理模型 √ — — √ 复杂曲面喷涂 — — √ — 形貌演变 — — √ √ 数据支撑 √ √ — — 试验验证 — √ √ √ 非空间对称颗粒分布 — — — — 2. 结束语
作为新型增材制造技术，冷喷涂固态增材制造已经逐步成为研究热点，基于实际应用中对形貌控制的需求，沉积体形貌模拟研究正在蓬勃发展，并通过多种方法或模型实现了有效的仿真和预测.目前，不同学者重点研究了喷涂角度、喷涂距离、喷枪移动速度、基体表面形貌这4个影响因素，此外也根据实际冷喷涂的限制要求，实现了喷涂时遮挡物的有效识别，为合理的喷涂路径规划提供理论依据.在未来的发展中，仍有以下挑战需要深入探索.
(1) 目前的所有方法都必须假设喷涂颗粒分布作为起始条件.试验结果表明，在沉积层数较少的情况下，选择不同的颗粒分布函数没有显著差异.然而，当沉积层数足够大时，就会出现明显的差异，其中一些开始与实际情况产生明显偏差.而且，选择合理的颗粒分布的原则尚未确定，如何避免理想状态下的颗粒分布假设是亟待解决的问题.
(2) 大量学者已经对沉积体形貌预测的精度进行了研究，但对形貌演变的终止条件没有给出明确定义.在实际冷喷涂过程中，临界速度的存在及影响因素多导致喷涂颗粒无法实现无限沉积，而模拟仿真方面对此没有限制，势必影响最终结果的准确性.
(3) 单点喷涂和连续移动喷涂之间的关系不明确.从喷涂原理来看，连续移动喷涂的形貌应由单点喷涂推导得出，但目前的研究常常将单点喷涂形貌和连续移动喷涂形貌相混淆.此外，受相邻喷涂道次重叠率的影响，对于减弱或消除沉积体表面波浪状起伏的模拟的准确性，尚未得到有效验证.
(4) 根据沉积体形貌的模拟结果对于喷涂路径规划并未有详细的研究.冷喷涂路径规划仍处于定性研究的阶段，虽然一些研究已经制备出了薄壁或规则形状的沉积体，但是对于典型问题的研究还未形成解决方法的共识，如：直角转弯的优化，沉积体边缘效应损失的补偿等.形成喷涂路径规划的原则将对冷喷涂增材制造的推广应用具有深远意义.
-
![]()
图 1 钨的添加量为12%时堆焊层的XRD衍射图谱
Figure 1. XRD diffraction patterns of surfacing layer with different W contents additions
![]()
图 2 不同钨添加量时堆焊层的金相组织形貌
Figure 2. Metallographic structure of surfacing layer with different W contents additions. (a) 3% W; (b) 6% W; (c) 9% W; (d) 12% W; (e) 15% W
![]()
图 3 钨添加量为12%时堆焊层的面扫描图片
Figure 3. Surface scanning image of surfacing layer for W content is 12%. (a) scanning microstru cture; (b) W element; (c) C element; (d) Cr element; (e) Fe element
![]()
图 4 钨添加量为12%时堆焊层的扫描组织形貌
Figure 4. SEM morphologies of surfacing layer for W content is 12%
![]()
图 5 不同钨添加量时堆焊层硬度和磨损量的变化曲线
Figure 5. Variation curves of hardness and wear of surfacing layer with different W contents additions
表 1 不同钨添加量时堆焊层的化学成分(质量分数，%)
Table 1 Chemical compositions of surfacing layer with different W contents additions
钨添加量w(%) Cr C B W Fe 3 13.31 1.47 0.52 0.84 余量 6 13.55 1.52 0.51 1.71 余量 9 12.79 1.54 0.52 2.55 余量 12 12.94 1.51 0.55 3.47 余量 15 13.48 1.54 0.53 4.29 余量 
下载: 导出CSV
-
[1] 张冀, 陈金梅, 冉申, 等. 碳化硅增强金属基复合材料的新型制备工艺[J]. 航空制造技术, 2014(6): 109 − 112. doi: 10.3969/j.issn.1671-833X.2014.06.023 Zhang Ji, Chen Jinmei, Ran Shen, et al. New preparation technology of silicon carbide particles reinforced metal matrix composites[J]. Aeronautical Manufacturing Technology, 2014(6): 109 − 112. doi: 10.3969/j.issn.1671-833X.2014.06.023
[2] Tang S L, Gao Y M, Li Y F. Recent developments in fabrication of ceramic particle reinforced iron matrix wear resistant surface composite using infiltration casting technology[J]. Ironmaking and Steelmaking, 2014, 41(8): 633 − 640. doi: 10.1179/1743281213Y.0000000175
[3] Ma Y P, Li X L, Wang C H, et al. Microstructure and impact wear resistance of Ti N reinforced high manganese steel matrix[J]. Journal of Iron and Steel Research International, 2012, 19(7): 60 − 65. doi: 10.1016/S1006-706X(12)60114-9
[4] 宗琳, 郭宁, 张晓玲. 原位合成(Ti, V)C增强铁基耐磨复合材料的研制[J]. 焊接学报, 2017, 38(8): 10 − 14. doi: 10.12073/j.hjxb.20150911001 Zong Lin, Guo Ning, Zhang Xiaoling. Investigation on wear resistance of in-situ (Ti, V)C reinforced Fe-based composite material[J]. Transactions of the China Welding Institution, 2017, 38(8): 10 − 14. doi: 10.12073/j.hjxb.20150911001
[5] 刘政军, 勾健, 贾华, 等. Fe-Cr-C-B-Nb堆焊合金的显微组织和耐磨性[J]. 焊接学报, 2018, 39(3): 75 − 78. doi: 10.12073/j.hjxb.2018390072 Liu Zengjun, Gou Jian, Jia Hua, et al. Microstructure and wear resistance of Fe-Cr-C-B-Nb hardfacing alloy[J]. Transactions of the China Welding Institution, 2018, 39(3): 75 − 78. doi: 10.12073/j.hjxb.2018390072
[6] Liu Z J, Su J G, Liu D, et al. Influence of magnetic field on microstructure and properties of Ni60 plasma surfacing layer[J]. China Welding, 2005, 14(2): 145 − 148.
[7] He Yanan, Song Qiang, Sun Kang, et al. Microstructure and properties of in-situ chromium carbide composite coating by laser cladding[J]. China Welding, 2018, 27(4): 10 − 17.
[8] 王智慧, 杨爱弟, 贺定勇, 等. 真空熔覆镍基合金涂层中碳化钨颗粒转变行为[J]. 稀有金属材料与工程, 2008, 37(10): 1869 − 1871. doi: 10.3321/j.issn:1002-185X.2008.10.039 Wang Zhuhui, Yang Aidi, He Dingyong, et al. The transformation of WC in Ni-based alloy coating by vacuum melting[J]. Rare Metal Materials and Engineering, 2008, 37(10): 1869 − 1871. doi: 10.3321/j.issn:1002-185X.2008.10.039
[9] 袁有录, 李铸国. 原位自生WC增强Fe基涂层的组织及干滑动摩擦磨损性能[J]. 材料工程, 2016, 44(5): 47 − 53. doi: 10.11868/j.issn.1001-4381.2016.05.008 Yuan Youlu, Li Zhuguo. Microstructure and dry sliding friction and wear properties of in-situ synthesized WC reinforced Fe-based coating[J]. Journal of Materials Engineering, 2016, 44(5): 47 − 53. doi: 10.11868/j.issn.1001-4381.2016.05.008
[10] 李震, 孙荣禄. 激光功率对Ni基WC熔覆层组织和性能的影响[J]. 金属热处理, 2016, 41(9): 107 − 110. Li Zhen, Sun Ronglu. Influence of laser power on microstructure and properties of Ni-based WC clad layer[J]. Heat Treatment of Metals, 2016, 41(9): 107 − 110.
[11] 徐卫仙, 张群莉, 姚建华. 热锻模激光熔覆Co基WC涂层的高温磨损性能研究[J]. 应用激光, 2013, 33(4): 370 − 375. doi: 10.3788/AL20133304.0370 Xu Weixian, Zhang Qunli, Yao Jianhua. Research on high-temperature wear resistance of laser cladding Co-based WC composite coating on hot-forging die[J]. Applied Laser, 2013, 33(4): 370 − 375. doi: 10.3788/AL20133304.0370
[12] 吴慧剑, 龚建勋, 刘江晴, 等. WC含量对明弧堆焊奥氏体合金显微组织及耐磨性的影响[J]. 粉末冶金材料科学与工程, 2016, 21(4): 562 − 568. doi: 10.3969/j.issn.1673-0224.2016.04.008 Wu Huijian, Gong Jianxun, Liu Jiangqing, et al. Effects of WC content on the microstructure and abrasion wear of open arc hardfacing austenitic alloy[J]. Materials Science and Engineering of Powder Metallurgy, 2016, 21(4): 562 − 568. doi: 10.3969/j.issn.1673-0224.2016.04.008
[13] Berndt A F. Binary phase diagrams[J]. Journal of Chemical Education, 2001, 46(46): 3733 − 3736.
-
期刊类型引用(0)
其他类型引用(1)
计量
- 文章访问数: 382
- HTML全文浏览量: 26
- PDF下载量: 16
- 被引次数: 1