镁锂合金搅拌摩擦焊接工艺特性分析

张婧, 封小松, 张成聪, 黄珲

张婧, 封小松, 张成聪, 黄珲. 镁锂合金搅拌摩擦焊接工艺特性分析[J]. 焊接学报, 2017, 38(4): 119-123. DOI: 10.12073/j.hjxb.20170428
引用本文: 张婧, 封小松, 张成聪, 黄珲. 镁锂合金搅拌摩擦焊接工艺特性分析[J]. 焊接学报, 2017, 38(4): 119-123. DOI: 10.12073/j.hjxb.20170428
shu
ZHANG Jing, FENG Xiaosong, ZHANG Chengcong, HUANG Hui. Investigation on friction stir welding of Mg-Li Alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2017, 38(4): 119-123. DOI: 10.12073/j.hjxb.20170428
Citation: ZHANG Jing, FENG Xiaosong, ZHANG Chengcong, HUANG Hui. Investigation on friction stir welding of Mg-Li Alloy[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2017, 38(4): 119-123. DOI: 10.12073/j.hjxb.20170428
shu

镁锂合金搅拌摩擦焊接工艺特性分析

  • 上海航天装备制造总厂, 上海 200245

Investigation on friction stir welding of Mg-Li Alloy

  • Shanghai Aerospace Equipments Manufacturer, Shanghai 200245, China

摘要

    摘要
  • 摘要: 针对退火态的MBLS10-200镁锂合金，分析了搅拌工具、焊接工艺参数对焊缝成形、接头组织特征及力学性能的影响，并对接头的塑性损失机理及提升技术进行分析.结果表明，在焊缝成形良好的工艺参数范围内（转速800~1 600 r/min、焊接速度200~500 mm/min），接头大多断在母材，强度与母材相当，而断后伸长率则有显著的降低，仅为母材的8%~57%.焊核及热力影响区与母材性能的差异使接头在受拉时产生各区域变形不协调是导致断后伸长率下降的根本原因.采用退火处理可以在接头强度不下降的同时，有效提升接头断后伸长率，可达到母材的96%.
    Abstract: The friction stir welding of MBL10-200 Mg-Li alloy with a thickness of 3 mm was investigated. Concentrating on the process characteristics, the effects of friction tools, welding parameters on weld appearance, and mechanical properties of the joints were studied. The mechanism and solution of joint ductility loss were both investigated. The results show that with relatively wide process window (rotation speed 800~1 600 r/min, welding speed 200~500 mm/min), welds with good appearance can be obtained. Joints under most welding parameters fracture at base metal, and shows comparable strength with base metal. The joint elongation shows apparent decrease, 8%~57% of base metal under varied welding parameters. The non-uniform deformation of WNZ, TMAZ and base metal in the joint is the main reason of ductility loss. Annealing of the welded joints can effectively increase the elongation, nearly 96% of base metal.
    • HTML全文
    • 参考文献(11)
  • [1] Wu R Z, Deng Y S, Zhang M L. Microstructure and mechanical properties of Mg-5Li-3Al-2Zn-xRE alloys[J]. Journal of Materials Science, 2009, 44(15): 4132-4139.
    [2] Haferkamp H, Niemeryer M, Boehem R, et al. Development, processing and application range of magnesium lithium alloys [J]. Material Science Forum, 2000, 350: 31-41.
    [3] Aghion E, Bronfin B. Magnesium alloys development towards the 21st century [J]. Material Science Forum, 2006, 171(2): 188-204.
    [4] Cao X, Jahazi M, Immarigeon J, et al. A review of laser welding techniques for magnesium alloys[J]. Journal of Materials Processing Technology, 2006, 58(8): 188-204.
    [5] Su S, Huang J, Lin H. Electron-beam welding behavior in Mg-Al based alloys[J]. Metallurgical and Materials Transactions, 2002, 33(5): 1641-1673.
    [6] Marya M, Edwards G L S. An investigation on the effects of gasses in GTA welding of a wrought AZ80 magnesium alloy[J]. Welding Journal, 2004, 83(7): 203-212.
    [7] Asahing T, Tokisuje H, Katoh K. Solidification crack sensitivity of TIG welded AZ31 magnesium alloy[J]. Journal Japan Institute of Light Metals, 1999, 49(12): 595-599.
    [8] Liu X H, Gu S H, Wu R Z,et al. Microstructure and mechanical properties of Mg-Li alloy after TIG welding [J]. Transactions of Nonferrous Metals Society of China, 2011(21): 477-481.
    [9] 邢 丽, 柯黎明, 孙德超, 等. 镁合金薄板的搅拌摩擦焊工艺[J]. 焊接学报, 2001, 22(6): 18-21. Xing Li, Ke Liming, Sun Dechao, et al. Friction stir welding of MB8 magnesium alloy sheet[J]. Transactions of the China Welding Institution, 2001, 22(6): 18-21.
    [10] 张 华, 林三宝, 吴 林, 等. AZ31镁合金搅拌摩擦焊接头力学性能[J]. 焊接学报, 2003, 24(5): 65-69. Zhang Hua, Lin Sanbao, Wu Lin, et al. Mechanical properties of friction stir welds on AZ31 magnesium alloy[J]. Transactions of the China Welding Institution, 2003, 24(5): 65-69.
    [11] 郭韋華, 王快社, 王 文, 等. 焊后热处理对镁合金搅拌摩擦焊接接头的影响[J]. 稀有金属材料与工程, 2011, 40(6): 1075-1078. Guo Wei, Wang Kuaishe, Wang Wen, et al. Influence of post-weld heat treatments on friction stir-welded AZ31B magnesium alloy joints[J]. Rare Metal Materials and Engineering, 2011, 40(6): 1075-1078.
    • 相关文章
    • 施引文献(32)

  • 期刊类型引用(21)

    1. 张香云，雷朱坦，耿家源，刘刚. AZ31/LA141搅拌摩擦搭接焊工艺及性能研究. 兵器材料科学与工程. 2024(02): 24-29 . 百度学术
    2. 韩政，蒋少松，李升，吴洁璇. LZ91镁锂合金四层中空结构件连接工艺. 锻压技术. 2024(05): 135-141 . 百度学术
    3. 赵玉军. 加工速度对AZ31镁合金搅拌摩擦加工组织和力学性能的影响. 南阳理工学院学报. 2024(04): 120-124 . 百度学术
    4. 宋文杰，贺帅，沈奇江，吴宗育. LA141镁锂合金搅拌摩擦焊接过程温度场模拟. 陕西科技大学学报. 2023(01): 117-122 . 百度学术
    5. 雷朱坦，武冰冰，王津，耿家源，刘刚. AZ31/LA141搅拌摩擦搭接焊接头的组织与力学性能. 航空制造技术. 2023(08): 117-123 . 百度学术
    6. 夏聪聪，马立彩，鲁传洋，王锋，唐佳奇. LA103W镁锂合金TIG焊接接头组织与性能研究. 航天制造技术. 2023(05): 50-53 . 百度学术
    7. 刘沁钰，周利，戎校宇，杨海峰，赵洪运. 镁锂合金焊接技术研究现状. 材料导报. 2022(10): 150-159 . 百度学术
    8. 沙春生，张成聪，张毅，黄婉如. MLZ91镁锂合金激光焊接接头的显微组织与力学性能. 热加工工艺. 2022(13): 57-60 . 百度学术
    9. 刘刚，张玺，武冰冰，解芳，马振铎. 旋转速度对LZ91镁锂合金搅拌摩擦加工改性的影响. 热加工工艺. 2022(16): 18-21 . 百度学术
    10. 刘兰波，李源，柴艳红，刘娜，毛喆，陈敏豪. 镁锂合金制造工艺技术研究及应用现状. 航天制造技术. 2022(05): 74-78 . 百度学术
    11. 刘刚，方诚，朱磊，黄青娜，解芳. 正交试验法优化超轻LA141镁锂合金表面植酸处理工艺研究. 河北科技大学学报. 2022(06): 571-578 . 百度学术
    12. 姜炳春，付琴，胡少华，唐联耀，刘方方. LZ92镁锂合金激光焊接接头的显微组织与力学性能. 机械工程材料. 2021(01): 46-49 . 百度学术
    13. 肖雪，刘怀海，耿家源，刘刚. 挤压态Mg-9Li-xAl-0.6Y合金组织与力学性能研究. 有色金属工程. 2021(04): 1-7 . 百度学术
    14. 张菊梅，段鑫，王凯，张阳，蔡辉. 水热反应温度对LA103Z镁锂合金表面MAO/LDH复合膜层微观组织及耐蚀性的影响. 表面技术. 2021(05): 261-268+280 . 百度学术
    15. 刘刚，秦丽霞，张玺，彭银利，耿家源. LZ91镁锂合金搅拌摩擦加工的组织与力学性能. 热加工工艺. 2021(18): 56-60 . 百度学术
    16. 宋奎晶，董志波，李洋，李冬梅，朱帅，吕磊，罗俊睿. 镁锂合金搅拌摩擦焊及电子束焊研究. 电子机械工程. 2020(01): 46-50 . 百度学术
    17. 江雯，蒋璐瑶，黄伟九，郭非，董海澎. 退火处理对搅拌摩擦加工LZ91双相镁锂合金微观组织及力学性能的影响. 材料导报. 2020(Z1): 307-311 . 百度学术
    18. 苑晨晨，蒋健博，李慧，李福山，崔梦宇，徐荣正. 超轻双相LZ91镁锂合金搅拌摩擦搭接焊接技术研究. 有色金属工程. 2020(07): 26-31 . 百度学术
    19. 江雯，蒋璐瑶，黄伟九，郭非，董海澎. 退火处理对搅拌摩擦加工LZ91双相镁锂合金微观组织及力学性能的影响. 材料导报. 2020(S1): 307-311 . 百度学术
    20. 李慧，徐荣正，侯艳喜，国旭明. 镁锂合金的焊接技术及其在航天领域的应用. 热加工工艺. 2019(01): 1-4 . 百度学术
    21. 范蒙，张贵锋，柴东郎，王士元. 镁锂超轻合金搅拌摩擦焊及其机制的研究. 焊管. 2019(11): 25-30 . 百度学术

    其他类型引用(11)

    • 资源附件(0)
计量
  • 文章访问数:  343
  • HTML全文浏览量:  10
  • PDF下载量:  385
  • 被引次数: 32
出版历程
  • 收稿日期:  2015-04-15

目录

摘要
HTML全文
    参考文献(11)
    相关文章
    施引文献(32)
    资源附件(0)

    /

    返回文章
    返回

    网站版权 © 焊接杂志社焊接学报编辑部电话：0451-86323218地址：哈尔滨市松北区创新路2077号

    本系统由 北京仁和汇智信息技术有限公司 开发  百度统计