疲劳裂纹扩展过程中焊接残余应力重分布测试
A novel method for evaluation of welding residual stress redistribution during fatigue crack growth
-
摘要:
提出了一种新的焊接残余应力在疲劳裂纹扩展过程中重分布规律的测试方法，并给出了相应的计算公式.在裂纹扩展的路径上粘贴若干三向电阻应变片，然后利用动态应变仪实时采集裂纹扩展过程中的应变变化，根据所推导的公式换算成相应的残余应力变化，从而得到裂纹扩展过程中残余应力重分布的规律.利用这种方法，试验测试了高强钢TIG焊接接头在疲劳裂纹扩展过程中的焊接残余应力重分布规律，并与一种解析的方法进行了对比.结果表明，该方法能够更为准确地表征裂纹扩展过程中焊接残余应力重分布的情况.
Abstract:A novel methodology for evaluation of welding residual stress (WRS) redistribution during fatigue crack growth (FCG) was proposed in this paper and some necessary equations were derived. By using strain gauge rosettes (with three strain gauges of different directions manufactured on one substrate) attached to the surface of the sample along the potential crack propagation path, the amounts of strain change were collected by a dynamic strain testing system and the corresponding amounts of WRS redistribution were calculated following our equations, which were used to characterize the WRS redistribution thereafter. Experimental tests were carried out to determine the redistribution of WRS during FCG of a high strength steel welded joint employing our proposed methodology. It turned out that this straightforward methodology was capable of accurately capturing the WRS redistribution during FCG relative to an analytical method proposed previously in the literature.
-
-
[1] 张正伟,张昭,张洪武.焊接残余应力对2024铝合金薄板疲劳寿命的影响[J].焊接学报, 2014, 35(10):29-32 Zhang Zhengwei, Zhang Zhao, Zhang Hongwu. Influence of welding residual stresses on fatigue life of Al 2024 plate[J]. Transactions of the China Welding Institution, 2014, 35(10):29-32 [2] Murugan R, Venugobal P, Ramaswami T, et al. Studies on the effect of weld defect on the fatigue behavior of welded structures[J]. China Welding, 2018, 27(1):53-59. [3] 李书齐,方洪渊,刘雪松,等.焊接构件热振复合时效的数值和试验分析[J].焊接学报, 2016, 37(5):111-114 Li Shuqi, Fang Hongyuan, Liu Xuesong, et al. Numerical and experimental analysis of thermal-vibration stress relief for welded structure[J]. Transactions of the China Welding Institution, 2016, 37(5):111-114 [4] Wang Q, Yan Z, Liu X, et al. Understanding of fatigue crack growth behavior in welded joint of a new generation Ni-Cr-Mo-V high strength steel[J]. Engineering Fracture Mechanics, 2018, 194:224-239. [5] Terada H. Stress intensity factor analysis and fatigue behavior of a crack in the residual stress field of welding[J]. Fatigue of Aircraft Structures, 2011(1):5-15. [6] 徐济民,吴振宇,苏毅.焊接残余应力对裂纹闭合与疲劳裂纹扩展速率的影响[J].清华大学学报(自然科学版), 1988, 28(2):23-33 Xu Jimin, Wu Zhenyu, Su Yi. The effects of welding residual stresses on fatigue crack closure and propagation rates[J]. Journal of Tsinghua Universiity, 1988, 28(2):23-33 [7] Wang Q, Liu X, Wang P, et al. Numerical simulation of residual stress in 10Ni5CrMoV steel weldments[J]. Journal of Materials Processing Technology, 2017, 240:77-86. [8] 张晓,姚润钢,王任甫,等.屈服强度参数对10Ni5CrMoV钢焊接残余应力数值计算结果的影响[J].焊接学报, 2010, 31(4):97-100 Zhang Xiao, Yao Rungang, Wang Renfu, et al. Effects of yield strength parameters on welding residual stress simulation results of 10Ni5CrMoV steel[J]. Transactions of the China Welding Institution, 2010, 31(4):97-100 [9] 王苹,刘永,李大用,等.固态相变对10Ni5CrMoV钢焊接残余应力的影响[J].焊接学报, 2017, 38(5):125-128 Wang Ping, Liu Yong, Li Dayong, et al. Effect of solid-state phase transformation on welding residual stress of 10Ni5CrMoV steel[J]. Transactions of the China Welding Institution, 2017, 38(5):125-128 [10] Liljedahl C, Tan M, Zanellato O, et al. Evolution of residual stresses with fatigue loading and subsequent crack growth in a welded aluminium alloy middle tension specimen[J]. Engineering Fracture Mechanics, 2008, 75:3881-3894. -
期刊类型引用(4)
1. 朱清清，张津超，王恒，曹宇鹏，苏波泳，花国然. 开放环境下钛合金激光熔覆的表面色差模型研究. 表面技术. 2024(07): 156-163+199 . 
百度学术
2. 宣鹏举，张淑婷，唐卫岗，欧阳佩旋，张涛，唐紫苑. 铜磷钎料热加工过程表观变色机理研究. 有色金属工程. 2022(03): 24-31 . 百度学术
3. 刘晓芳，张冠星，常云峰，王蒙，钟素娟. 干燥过滤器焊后泄露原因. 焊接. 2021(10): 34-37+62-63 . 百度学术
4. 刘亦贤，陈永，李书珍，蔡国磊，赵晨，李国鹏，戴谷川. 铜磷钎料对钎焊性能影响的研究进展. 热加工工艺. 2020(23): 1-7 . 百度学术
其他类型引用(0)
计量
- 文章访问数: 362
- HTML全文浏览量: 1
- PDF下载量: 167
- 被引次数: 4
下载: