烧结压力对自钎剂钎料性能的影响

李秀朋; 龙伟民; 陈曦; 沈元勋; 钟素娟

烧结压力对自钎剂钎料性能的影响

1.
郑州机械研究所新型钎焊材料与技术国家重点实验室, 郑州 450001
2.
河南工业大学土木建筑学院, 郑州 450001

基金项目: 国际科技合作专项资助项目(2014DFR50820);华南理工大学开放基金资助项目(2013001) *参加此项研究工作的还有裴夤崟

计量
- 文章访问数: 236
- HTML全文浏览量: 4
- PDF下载量: 85
出版历程
- 收稿日期: 2014-11-03

Influence of sintering pressure on property of self-fluxing filler metal

1.
State Key Laboratory of Advanced Brazing Filler Metals and Technology, Zhengzhou Research Institute of Mechanical Engineering, Zhengzhou 450001, China
2.
School of Civilengineering and Architecture, Henan University of Technology, Zhengzhou 450001, China

摘要

摘要: 采用热压烧结法制备了Al-12Si自钎剂钎料环,对不同烧结压力下钎料的润湿性、显微硬度和显微组织进行了研究. 结果表明,自钎剂钎料润湿性环随着烧结压力升高呈现上升趋势,在烧结压力为222 MPa时铺展面积达到152 mm²;随着烧结压力的增大,自钎剂钎料密度、显微硬度逐渐增大,但上升趋势变缓;钎料显微组织主要是灰色基体上均匀分布着黑色大块状相和白色小颗粒;XRD结果显示自钎剂钎料只有α-Al固溶体,初晶硅和Nocolok钎剂三种物相,热压烧结法制备自钎剂钎料未发生氧化、水解等反应,加上硅的活化作用保证了钎料高活性.
- 自钎剂钎料 /
- 铝及其合金 /
- 铝硅钎料 /
- 润湿性
Abstract: The ring of Al-12Si self-fluxing filler metals has been prepared by hot pressed sintering. The wetting property, microhardness, microscopic structure of self-fluxing on different sintering pressure were studied. The results showed that the spreading areas of the self-fluxing filler metals were affected with sintering pressure. And the spreading areas of the self-fluxing filler metals was up to 152 mm² when the sintering pressure was at 222 MPa. With increasing of the sintering pressure, the density, microhardness of the self-fluxing filler metals increased, but the tendency of increasing became slowly. The microscopic structure of self-fluxing filler metals was composed of black large lump and white small particles which was evenly distributed on the gray matrix; XRD results showed that self-fluxing filler metals was only composed of α-Al solid solution, primary crystal silicium and Nocolok filler metals, which denoted that the filler metals prepared by hot pressed sintering did not occur oxidation reactions and hydrolysis reactions. The activation of silicium ensured the high activity of filler metals.
- self-fluxing filler metal /
- Al and Al alloy /
- Al-Si filler metal /
- wettability

HTML全文

参考文献(11)

[1]	龙伟民, 乔培新, 王海滨, 等. 粉末合成钎料的探讨[J]. 机械工程学报, 2001, 37(10): 107-108. Long Weimin, Qiao Peixin, Wang Haibin, et al. Discussion of power synthetic filler materials[J]. Chinese Journal of Mechanical Engineering, 2001, 37(10): 107-108.
[2]	朱宏, 薛松柏, 盛重. 6063铝合金阶梯焊中温钎料腐蚀性能[J]. 焊接学报, 2009, 30(10): 29-32. Zhu Hong, Xue Songbai, Sheng Zhong. Corrosion resistance of intermediate temperature filler metal for stepped welding to 6063 aluminum alloy[J]. Transactions of the China Welding Institution, 2009, 30(10): 29-32.
[3]	Tsao L C, Weng W P, Cheng M D, et al. Brazeability of a 3003 aluminum alloy with Al-Si-Cu-based filler metals[J]. Journal of Materials Engineering and Performance, 2002, 11(4): 360-364.
[4]	Chang S Y, Tsao L C, Li T Y, et al. Joining 6061 aluminum alloy with Al-Si-Cu filler metals[J]. Journal of Alloys and Compounds, 2009, 448(1): 174-180.
[5]	Humpston G, Sangha S P, Jacobson D M. New filler metals and process for fluxless brazing of aluminium engineering alloys[J]. Materials Science and Techonogy, 1995, 11(11): 1161-1168.
[6]	Chuang T H, Tsao L C, Tsai T C, et al. Development of a low-melting-point filler metal for brazing aluminum alloys[J]. Metallurgical and Materials Transactions A, 2000, 31(9): 2239-2245.
[7]	薛松柏, 董健, 吕晓春, 等. LY12铝合金中温钎焊技术[J]. 焊接学报, 2003, 24(3): 21-23. Xue Songbai, Dong Jian, lü Xiaochun, et al. Brazing technology of LY12 Al-alloy at middle temperature[J]. Transactions of the China Welding Institution, 2003, 24(3): 21-23.
[8]	王冠, 李远波, 郭忠宁, 等. 汽车散热器新型铝合金钎焊接头腐蚀行为的分析[J]. 焊接学报, 2011, 32(6): 25-28. Wang Guan, Li Yuanbo, Guo Zhongning, et al. Research on corrosion of automobile condenser brazed with novel aluminum alloy[J]. Transactions of the China Welding Institution, 2011, 32(6): 25-28.
[9]	黄培云. 粉末冶金原理[M]. 北京: 冶金工业出版社, 1997.
[10]	张启运, 庄鸿寿. 钎焊手册[M]. 北京: 机械工业出版社, 2008.
[11]	张启运, 刘淑琪. 氟铝酸钾高温铝钎剂的湿法合成及其在钎焊时的作用机理[J]. 焊接学报, 1982, 3(4): 153-157. Zhang Qiyun, Xiu Shuqi. The solution synthesis of potassium fluoluminate flux and its brazing mechanism[J]. Transactions of the China Welding Institution, 1982, 3(4): 153-158.