高端刀具异种钢A-TIG焊焊接性
Weldability of dissimilar steels for high-end cutting toolswith A-TIG welding
-
摘要: 针对高端刀具焊接时必须整体预热,接头质量不稳定的问题,采用A-TIG焊接方法对高端刀具中的430不锈钢刀背和3Cr13-1Cr17-3Cr13"三明治"复合不锈钢刀刃进行焊接.研究了活性剂对焊缝熔深﹑焊缝气孔﹑接头力学性能﹑微观组织及接头抗腐蚀性能的影响,并和常规TIG焊进行了比较.结果表明,利用A-TIG可以无需预热实现430不锈钢刀背和3Cr13-1Cr17-3Cr13"三明治"不锈钢刀刃的焊接,且单面焊双面成形,焊缝中未出现气孔、裂纹,接头抗拉强度可达606 MPa;接头热影响区非常窄,焊缝晶粒得到细化;活性剂的加入未降低焊接接头的抗腐蚀性能.因此,高端刀具异种钢A-TIG焊具有良好的焊接性,接头质量高.Abstract: In TIG welding of high-end cutting tools, the entire tools must be preheated. A-TIG welding was selected in this paper to weld 430 stainless steel knife back and sandwich(3Cr13-1Cr17-3Cr13) stainless steel blade, and study the effect of fluxes on the weld shape. The differences between A-TIG and conventional TIG on the weld penetration, pores in the weld, microstructure, mechanical properties and corrosion resistance of the joint were studied in this paper. The results show that satisfied joint with excellent weld appearance between 430 stainless steel knife back and sandwich(3Cr13-1Cr17-3Cr13) stainless steel blade could be achieved by A-TIG welding. No defects were detected in the joint and the grains in weld were refined. The HAZ was very narrow and the tensile strength of joint was 606 MPa. The activating flux did not reduce the corrosion resistance of welded joint.
-
Keywords:
- A-TIG welding /
- dissimilar steels /
- microstructure /
- mechanical property
-
-
期刊类型引用(6)
1. 曹志龙，朱浩，安同邦，王晨霁，马成勇，彭云. 1 000 MPa级高强钢熔敷金属强韧化机理分析. 焊接学报. 2023(07): 116-122+135-136 . 
本站查看
2. 张岩. 高强钢在轻量化结构设计中的应用及其焊接. 电焊机. 2021(12): 34-40+128 . 百度学术
3. 栗卓新，苏小虎，李红，KIM Hee Jin. 690 MPa级以上高强钢焊接熔敷金属微观组织及其联合贝氏体的研究进展. 中国材料进展. 2019(12): 1169-1176 . 百度学术
4. 隋轶，韩严法，傅博，胡奉雅，刘芳芳，蒋健博. 应用示波冲击法研究Q960钢焊接热模拟冲击韧性. 宽厚板. 2018(03): 1-4 . 百度学术
5. 康丹丹，万天明，王高见，郑永强. 水电用1000 MPa级超高强钢焊接的研究进展. 热加工工艺. 2018(15): 11-13+17 . 百度学术
6. 武丹，刘政军，苏允海，裘荣鹏. 夹杂物对高强钢焊缝金属组织和冷裂纹影响分析. 热加工工艺. 2018(23): 246-249 . 百度学术
其他类型引用(1)
计量
- 文章访问数: 198
- HTML全文浏览量: 1
- PDF下载量: 105
- 被引次数: 7
下载: