热处理对高强铝合金搅拌摩擦焊接头热力影响区组织和性能的影响

基金项目: 国家自然科学基金资助项目(10577010)

Effect of heat treatment on microstructure and properties of thermomechanical affected zone of high-strength aluminum alloy

State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China

摘要: 分析讨论了热处理对高强铝合金热力影响区的组织和力学性能的影响.结果表明,经热处理后,热力影响区的棒状沉淀相逐渐消失,球状沉淀相弥散分布在热力影响区的晶界和晶粒中.两种铝合金在热处理后力学性能上都有一定的提高,7075铝合金接头的抗拉强度可达415 MPa,是母材抗拉强度的89.5%,7050铝合金接头的抗拉强度可达422 MPa,是母材抗拉强度的89.8%,断裂几乎都发生在前进侧的热力影响区,并且硬度的最低处在前进侧热力影响区.
- 铝合金 /
- 微观组织 /
- 热处理
Abstract: The effect of heat treatment on microstructure and properties of high-strength aluminum alloy was investigated.The results showed that the rod-like precipitation disappears gradually and the spherical precipitation is dispersed in the grain boundary and grain of TMAZ after heat treatment.The mechanical properties of aluminum alloys after heat treatment is improved,the tensile strength of 7075 aluminum alloy can reach to 415 MPa,89.5% of the base metal,the tensile strength of 7050 aluminum alloy can reach to 422 MPa,89.8% of the base metal,both the fracture and the lowest hardness appear in TMAZ of advancing side of joints.
- aluminum alloy /
- microstructure /
- heat treatment

1.	郑勇，魏连峰，杨灿湘，邱绍宇，李华鑫，王军健，杨建国. ODS钢焊接技术研究进展与展望. 焊接学报. 2024(12): 117-128 . 本站查看
2.	盖欣，陈浩瀚，张晨璐，冯国才，芦丽莉. 搅拌摩擦焊接技术在Fe基合金中的研究进展综述. 科技视界. 2022(33): 90-92 . 百度学术
3.	李小欣，郑延召，徐仲勋，王晓贞. 焊接参数对5A06铝合金搅拌摩擦焊接头性能的影响. 上海金属. 2021(03): 19-25 . 百度学术
4.	周利，张仁晓，舒凤远，黄永宪，冯吉才. Q235钢搅拌摩擦焊接头微观组织与力学性能分析. 焊接学报. 2019(03): 80-84+164 . 本站查看
5.	李胜利，杨新岐，唐文珅，李会军. 新型9Cr-1Mo钢搅拌摩擦焊接头组织及性能. 焊接学报. 2019(04): 28-35+162 . 本站查看
6.	孙鹏，徐岳. 钢构桥梁钢的搅拌摩擦焊组织与性能研究. 热加工工艺. 2019(19): 30-34+38 . 百度学术
7.	薛松柏，王博，张亮，龙伟民. 中国近十年绿色焊接技术研究进展. 材料导报. 2019(17): 2813-2830 . 百度学术