超高强淬火钢板中频点焊接头组织与断口形貌

韩立军, 谷诤巍, 张正林

韩立军, 谷诤巍, 张正林. 超高强淬火钢板中频点焊接头组织与断口形貌[J]. 焊接学报, 2010, (4): 101-104.
引用本文: 韩立军, 谷诤巍, 张正林. 超高强淬火钢板中频点焊接头组织与断口形貌[J]. 焊接学报, 2010, (4): 101-104.
shu
HAN Lijun, GU Zhengwei, ZHANG Zhenglin. Microstructure and fractography of intermediate frequency spot welding of precision ultra-high strength quenching steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2010, (4): 101-104.
Citation: HAN Lijun, GU Zhengwei, ZHANG Zhenglin. Microstructure and fractography of intermediate frequency spot welding of precision ultra-high strength quenching steel[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2010, (4): 101-104.
shu

超高强淬火钢板中频点焊接头组织与断口形貌

  • 1.

    一汽大众汽车有限公司产品管理部, 长春 130011

  • 2.

    吉林大学材料科学与工程学院, 长春 130022

Microstructure and fractography of intermediate frequency spot welding of precision ultra-high strength quenching steel

  • 1.

    The FAW-Wolkswagen Automobile Company Ltd., Changchun 130011, China

  • 2.

    College of Materials Science and Engineering, Jilin University, Changchun 130022, China

摘要

    摘要
  • 摘要: 以超高强度淬火钢EN10292TL4225为研究对象,采用先进的中频点焊连接技术,利用优化的焊接参数实现了超高强钢同种材料之间的优质连接,进行了高强钢的点焊接头拉伸试验和焊点表面硬度分布试验以及对拉伸断口的扫描电镜分析.结果表明,试验得到的点焊接头具有良好的力学性能和接头组织形貌,焊接接头组织具有和母材一致的显微组织,断口形貌具有塑性韧窝的特征,能够满足汽车产品碰撞与道路试验设计的要求.
    Abstract: Precision ultra-high strength quenching steel EN 10 292 TL4225 was selected for the study.The intermediate frequency (IF) spot welding process,one kind of advanced jointing technologies,was used,and the perfect welded joints were obtained by using the optimum welding parameters.The mechanical properties of the joints,such as the tension strength,the hardness distribution,were tested,and the microstructure of the fracture was analyzed by scanning electron microscope.The test results show that the joints welded by using IF spot welding process has good mechanical properties,the microstructure of the joints is similar with that of the base metal,the fracture of the joints has the characteristics of plastic,and the mechanical properties completely meet the actual need of car product crash test and road testing.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献(25)

  • 期刊类型引用(13)

    1. 董会，甘少明，杜永祺，白佳鑫，程煜辰，李明，朱朝璇. 激光扫描速率对NiCr/Cr_3C_2涂层微结构与耐磨性的影响. 金属热处理. 2023(11): 282-287 . 百度学术
    2. 皮智敏，周鸿凯，黄志武，陈枭. WC-Cr_3C_2基金属陶瓷涂层的研究现状. 热加工工艺. 2021(02): 6-9 . 百度学术
    3. 胡登文，刘艳，陈辉，王梦超. Q960E钢激光熔覆Ni基WC涂层组织及性能. 中国激光. 2021(06): 239-245 . 百度学术
    4. 陆琪琪，叶林，陆海峰，张学峰，阮新宇，覃恩伟，吴树辉. 适用于垃圾焚烧炉的激光熔覆技术研究. 热处理. 2021(02): 31-35+39 . 百度学术
    5. 张敏，王刚，张立胜，许桓瑞，张云龙，许帅. 40Cr钢表面激光熔覆Fe, Ni基涂层组织性能研究. 稀有金属. 2021(08): 928-935 . 百度学术
    6. 王冬春，杜锦涛，刘辉，栾程群. 碳化钨耐磨材料激光熔覆关键问题. 电焊机. 2021(08): 146-152+182 . 百度学术
    7. 杨宁，李立凯. 激光功率和粉末含量对(V_2O_5+B_2O_3+C)镍基涂层硬度的影响. 热加工工艺. 2021(24): 103-105 . 百度学术
    8. 钱绍祥. 激光熔覆铁基合金涂层的组织及耐蚀性能. 铸造技术. 2019(06): 613-616 . 百度学术
    9. 杨宁，李立凯. 激光熔覆(V_2O_5+WO_3+C)/Ni60涂层的磨损性能研究. 稀有金属与硬质合金. 2019(04): 54-57+64 . 百度学术
    10. 杨宁，李立凯. 激光功率和粉末含量对(B_2O_3+WO_3+C)镍基熔覆层硬度的影响. 应用激光. 2019(04): 574-579 . 百度学术
    11. 李美艳，韩彬，林学强. 基于“学研创”交叉融合的激光加工实验室建设与安全管理实践. 实验技术与管理. 2018(12): 242-245 . 百度学术
    12. 马群双，李亚江，王娟，段虎明，徐广源. 宽束激光熔覆Ni60/WC复合层显微组织及抗剪强度. 焊接学报. 2016(12): 49-52+131 . 本站查看
    13. 李正秋，石玗，曹驰，苏艳文. 半导体激光熔覆Ni基合金堆焊层组织及性能的研究. 应用激光. 2016(05): 547-552 . 百度学术

    其他类型引用(12)

    • 资源附件(0)
计量
  • 文章访问数:  304
  • HTML全文浏览量:  8
  • PDF下载量:  79
  • 被引次数: 25
出版历程
  • 收稿日期:  2009-08-19

目录

摘要
HTML全文
    参考文献(0)
    相关文章
    施引文献(25)
    资源附件(0)

    /

    返回文章
    返回

    网站版权 © 焊接杂志社焊接学报编辑部电话：0451-86323218地址：哈尔滨市松北区创新路2077号

    本系统由 北京仁和汇智信息技术有限公司 开发  百度统计