Abstract: Domestic ceramics have been chemically plated nickel and the brazing of ceramics plated nickel with 1Cr18Ni9Ti stainless steel was realized.Interfacial structures and properties of ceramic/Ni/Sn-3.5Ag/stainless steel joint in atmosphere were analyzed by some test methods such as scanning electron microscopy (SEM), energy distribution spectrometer (EDS), X-ray diffraction (XRD), shear stress test and so on.The results show that the joint of chemical plated nickel ceramics with 1Cr18Ni9Ti stainless steel is a multilayer compound structure.Plated nickel layer generated interfacial reaction with tin based solder and the productions of interface reaction are Ni₃Sn₄ intermetallic compound and tin base solution. Shear strengthen of the joint is up to 15.7MPa when soldering temperature and time are 300℃ and 5 min respectively.This method is low cost and convenient for batch production.Thus, it broadens the use range of domestic ceramics and has certain applied value.