铝/镀锌钢板CMT熔钎焊界面区组织与接头性能
Interface microstructure and mechanical property of CMT welding-brazed joint between aluminum and galvanized steel sheet
-
摘要: 采用冷金属过渡方法(CMT)对铝和镀锌钢板异种材料进行了熔钎焊连接。使用扫描电镜(SEM)、能谱分析(EDAX)和拉伸试验对焊接接头界面区显微组织及接头性能进行研究。试验结果表明,铝和镀锌钢能得到成形良好的搭接接头。在CMT熔钎焊的方法下,形成了中间厚两边薄的界面区,并且在熔化区一侧边缘形成了富锌区,界面区组织成分也由致密的FeAl3金属间化合物层变为α固溶体和FeAl3化合物混合层,而富锌区是由富铝的α固溶体和残留的铝组成。在进行拉伸试验时,断裂发生在铝母材的热影响区,接头强度为72.09 MPa。Abstract: Welding-brazing experiment of aluminum and galvanized steel was conducted with cold metal transfer method.The interface microstructure and mechanical property of the joint were analyzed by SEM, EDAX and transverse tensile test.The results indicate that good lap joint between aluminum and galvanized steel sheet can be made in appropriate parameters.The interface turns to be thin from middle to the edge with the components changing from FeAl 3 intermetallics to a compound of αsolid solution and FeAl3 intermetallics.Meanwhile, a rich-zinc zone composed of α solid solution and aluminum at the edge of weld metal exists.In the tensile test, fracture appears in the heat affected zone of aluminum base metal, and its tensile-strength is 72.09MPa.
-
Keywords:
- welding-brazing /
- cold metal transfer /
- intermetallics /
- interface /
- rich-zinc zone
-
-
期刊类型引用(6)
1. 苏才津，秦南南，冯哲，张丽. 激光熔覆铁基合金涂层熔覆质量形貌预测. 四川冶金. 2025(01): 16-21 . 
百度学术
2. 方琳. 镍基碳化钨合金粉末组织及性能. 世界有色金属. 2021(19): 3-5 . 百度学术
3. 尹燕，康平，路超，张圆，张瑞华. 激光焊接异种钢组织及显微硬度分析. 焊接学报. 2020(07): 71-77+100-101 . 本站查看
4. 张群莉，姚中志，周塘，姚建华，Volodymyr S.Kovalenko. 前驱体对激光熔覆复合溶胶凝胶制备陶瓷涂层的影响. 表面技术. 2019(02): 1-9 . 百度学术
5. 尹燕，潘存良，赵超，张瑞华，屈岳波. 激光熔覆高铬铁基合金的组织形成机制及对显微硬度的影响. 焊接学报. 2019(07): 114-120+166 . 本站查看
6. 尹燕，路超，刘鹏宇，肖梦智，蔡伟军，张瑞华，屈岳波. 激光熔敷制备高速钢涂层. 电焊机. 2017(10): 99-103 . 百度学术
其他类型引用(3)
计量
- 文章访问数: 214
- HTML全文浏览量: 5
- PDF下载量: 61
- 被引次数: 9
下载: