QFP组件的优化模拟及焊点热疲劳寿命的预测
Optimum simulation and prediction on thermal fatigue life of soldered joints of QFP devices
-
摘要: 采用有限元方法研究了方形扁平式封装QFP(quadflatpackage)组件的优化模拟及引线宽度与间距对焊点疲劳寿命的影响规律。结果表明,在QFP64组件的所有焊点中,最外侧焊点的正前面存在最大应变值,易产生裂纹,发生疲劳破坏,为组件的最脆弱部位。QFP引线间距固定时,随着引线宽度的增加,焊点等效应变值逐渐增加,焊点可靠性降低,热疲劳寿命降低;QFP引线宽度固定时,随着引线间距的增加,存在一个焊点热疲劳寿命最大值;所选取的计算模型中,当引线宽度为0.15mm,引线间距为0.45mm时,焊点可靠性最高,组件具有最长的疲劳寿命。Abstract: Optimum simulation for QFP devices and effects of lead widths and lead pitches of QFP on the thermal fatigue life of soldered joints of QFP devices were studied by means of FEM method. Results indicate that the maximum strain value exists at the front of the outside soldered joint in all the soldered joints of QFP64, where is the weakest position at which cracks initiation take place easily and lead to failure owing to thermal fatigue finally. When the lead pitches are constant, the equivalent strain existing in soldered joints increases with the increasing of lead widths, the reliability of the soldered joints declines and the thermal fatigue life decreases.When the lead widths are unvaried, the equivalent strain existing in soldered joints doesn' t decrease at all times in which there exists a maximum value of the thermal fatigue life with the increase of lead pitches. While lead width is 0.15mm and lead pitch is 0.45mm of QFP64, the reliability of the soldered joint is highest and the device can be served for longest time.
-
Keywords:
- finite element method /
- QFP /
- equivalent strain /
- thermal fatigue life /
- soldered joint
-
-
期刊类型引用(10)
1. 仇一卿，姚徐伟，卜星，赵舵，张自立，陆伟，倪林斌. 2219铝合金搅拌摩擦焊焊缝X射线影像特征及其形成原因. 电焊机. 2023(06): 117-121+134 . 
百度学术
2. 丁吉坤，宋建岭，韩国良，田龙，高泽峰. 2219厚板铝合金VPTIG焊接接头组织及性能. 焊接. 2020(04): 47-51+64 . 百度学术
3. 丁吉坤，宋建岭，蒙丹阳，高泽峰，王亚森. 2219厚板铝合金钨极和熔化极惰性气体保护焊焊接接头组织与性能对比. 宇航材料工艺. 2020(05): 93-97 . 百度学术
4. 蒙丹阳，张登魁，韩国良，张慧峰，孙全. 中厚板2219铝合金摆动TIG焊接头组织及性能研究. 焊接技术. 2020(12): 34-37+120 . 百度学术
5. 宋建岭，李庆庆，刘含伟，肖宏，林三宝. Si元素含量对5A06/2219异种铝合金焊接裂纹的影响. 焊接. 2019(02): 35-39+67 . 百度学术
6. 刘含伟，王斌，韩国良，王照禹，刘飞. 两种热处理状态2219铝合金对接接头补焊特性. 焊接. 2019(04): 49-53+67-68 . 百度学术
7. 阮德重，张登魁，王国庆，单际国，赵玥，吴爱萍. 基于RBF神经网络预测2219铝合金多层TIG焊接头拉伸性能研究. 焊接技术. 2019(06): 22-27 . 百度学术
8. 黄诚，王非凡，鄢东洋，刘德博，胡正根. 2219-T87/T852铝合金异质接头力学性能弱化及断裂机制. 宇航材料工艺. 2018(02): 56-60 . 百度学术
9. 孙世烜，贾晓喆，高彦军，李超，王凯，李晓光. 冷却条件对2219铝合金搅拌摩擦焊接头组织及性能的影响. 热加工工艺. 2018(17): 25-29+35 . 百度学术
10. 颜旭，马核，熊林玉，田志杰，张彦华. 2219铝合金TIG焊接头断裂性能研究. 航天制造技术. 2017(04): 16-20 . 百度学术
其他类型引用(5)
计量
- 文章访问数: 191
- HTML全文浏览量: 2
- PDF下载量: 82
- 被引次数: 15
下载: