TC1合金表面电火花沉积WC-8Co涂层界面行为

汪瑞军, 钱乙余, 黄小鸥, 刘军

汪瑞军, 钱乙余, 黄小鸥, 刘军. TC1合金表面电火花沉积WC-8Co涂层界面行为[J]. 焊接学报, 2003, (5): 88-90,96.
引用本文: 汪瑞军, 钱乙余, 黄小鸥, 刘军. TC1合金表面电火花沉积WC-8Co涂层界面行为[J]. 焊接学报, 2003, (5): 88-90,96.
shu
WANC Rui-jun, QIAN Yi-yu, HUANG Xiao-ou, LIU Jun. Interface behavior of WC-8Co coating on Ti alloy produced by electrospark deposition[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (5): 88-90,96.
Citation: WANC Rui-jun, QIAN Yi-yu, HUANG Xiao-ou, LIU Jun. Interface behavior of WC-8Co coating on Ti alloy produced by electrospark deposition[J]. TRANSACTIONS OF THE CHINA WELDING INSTITUTION, 2003, (5): 88-90,96.
shu

TC1合金表面电火花沉积WC-8Co涂层界面行为

  • 1.

    哈尔滨工业大学 现代焊接生产技术国家重点实验室, 哈尔滨 150001;中国农业机械化科学研究院 表面工程技术研究所, 北京 100083

  • 2.

    哈尔滨工业大学 现代焊接生产技术国家重点实验室, 哈尔滨 150001

  • 3.

    中国农业机械化科学研究院 表面工程技术研究所, 北京 100083

Interface behavior of WC-8Co coating on Ti alloy produced by electrospark deposition

  • 1.

    National Key laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 150001, China;Surface Engineering Technology Institute, Chinese Academy of Agricultural Mechanization Sciences, Bejing 100083, China

  • 2.

    National Key laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 150001, China

  • 3.

    Surface Engineering Technology Institute, Chinese Academy of Agricultural Mechanization Sciences, Bejing 100083, China

摘要

    摘要
  • 摘要: 钛合金在航空、航天工业得到了广泛应用。但其耐磨性差,对磨面容易产生粘结及对微动磨损敏感等缺点,限制其应用领域的进一步扩大。实践证明,采用电火花强化技术在TC1合金表面制造WC-8Co强化层,可以有效提高TC1基体表面耐磨性能。作者研究了WC-8Co强化层的表面状态、界面行为以及相结构组成,认为TC1合金表面强化高熔点的WC-8Co材料,厚度可大于50 μm;强化层与基体之间存在过渡区;强化层表面由TiC、W2C和少量W组成;强化层截面的显微硬度是基体的3倍以上。
    Abstract: Ti alloy has been widely used on aviation and space navigation industries,but its poor wearing resistance,along with the easily produced fricative adhesion on surfaces and the damage sensiveness to micro-drive wearing,has limited its further applications.The WC-8Co coating produced by electro spark deposition on Ti alloy can effectively improve substrate's wearing resistance.In this paper the behaviour of the interface between substrate and coating was discussed,as well as the micro-structure form of the intersection and the microstructure features between layers,was also observed and analyzed.The coating has superfine micro-structure se that the wearing resistance of the surface was effectively improved.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献(25)

  • 期刊类型引用(13)

    1. 董会，甘少明，杜永祺，白佳鑫，程煜辰，李明，朱朝璇. 激光扫描速率对NiCr/Cr_3C_2涂层微结构与耐磨性的影响. 金属热处理. 2023(11): 282-287 . 百度学术
    2. 皮智敏，周鸿凯，黄志武，陈枭. WC-Cr_3C_2基金属陶瓷涂层的研究现状. 热加工工艺. 2021(02): 6-9 . 百度学术
    3. 胡登文，刘艳，陈辉，王梦超. Q960E钢激光熔覆Ni基WC涂层组织及性能. 中国激光. 2021(06): 239-245 . 百度学术
    4. 陆琪琪，叶林，陆海峰，张学峰，阮新宇，覃恩伟，吴树辉. 适用于垃圾焚烧炉的激光熔覆技术研究. 热处理. 2021(02): 31-35+39 . 百度学术
    5. 张敏，王刚，张立胜，许桓瑞，张云龙，许帅. 40Cr钢表面激光熔覆Fe, Ni基涂层组织性能研究. 稀有金属. 2021(08): 928-935 . 百度学术
    6. 王冬春，杜锦涛，刘辉，栾程群. 碳化钨耐磨材料激光熔覆关键问题. 电焊机. 2021(08): 146-152+182 . 百度学术
    7. 杨宁，李立凯. 激光功率和粉末含量对(V_2O_5+B_2O_3+C)镍基涂层硬度的影响. 热加工工艺. 2021(24): 103-105 . 百度学术
    8. 钱绍祥. 激光熔覆铁基合金涂层的组织及耐蚀性能. 铸造技术. 2019(06): 613-616 . 百度学术
    9. 杨宁，李立凯. 激光熔覆(V_2O_5+WO_3+C)/Ni60涂层的磨损性能研究. 稀有金属与硬质合金. 2019(04): 54-57+64 . 百度学术
    10. 杨宁，李立凯. 激光功率和粉末含量对(B_2O_3+WO_3+C)镍基熔覆层硬度的影响. 应用激光. 2019(04): 574-579 . 百度学术
    11. 李美艳，韩彬，林学强. 基于“学研创”交叉融合的激光加工实验室建设与安全管理实践. 实验技术与管理. 2018(12): 242-245 . 百度学术
    12. 马群双，李亚江，王娟，段虎明，徐广源. 宽束激光熔覆Ni60/WC复合层显微组织及抗剪强度. 焊接学报. 2016(12): 49-52+131 . 本站查看
    13. 李正秋，石玗，曹驰，苏艳文. 半导体激光熔覆Ni基合金堆焊层组织及性能的研究. 应用激光. 2016(05): 547-552 . 百度学术

    其他类型引用(12)

    • 资源附件(0)
计量
  • 文章访问数:  283
  • HTML全文浏览量:  6
  • PDF下载量:  56
  • 被引次数: 25
出版历程
  • 收稿日期:  2003-04-11

目录

摘要
HTML全文
    参考文献(0)
    相关文章
    施引文献
    资源附件(0)

    /

    返回文章
    返回

    网站版权 © 焊接杂志社焊接学报编辑部电话：0451-86323218地址：哈尔滨市松北区创新路2077号

    本系统由 北京仁和汇智信息技术有限公司 开发  百度统计