Microstructure and properties of titanium alloy/copper-nickel/stainless steel welded joints
-
摘要: 采用铜-镍复合填充金属进行了钛合金和不锈钢的冷金属过渡焊接，借助扫描电子显微镜、X射线衍射仪研究铜-镍复合填充金属对钛合金/不锈钢焊接接头微观组织和力学性能的影响. 结果表明，添加铜-镍复合填充金属后得到了无焊接缺陷的钛合金/不锈钢焊接接头. 接头中形成了硬度相对Ti-Fe，Ti-Cu金属间化合物较低的Ti-Ni金属间化合物，改善了钛合金/不锈钢焊接接头的拉伸性能. 当焊接电流为182 A时，钛合金/不锈钢接头的拉剪强度最大为348 MPa. 钛合金/不锈钢接头由不锈钢-焊缝金属界面、不锈钢-纯镍-钛合金界面、钛合金-焊缝金属界面和焊缝金属组成，接头中形成了Ti-Cu，Ti-Ni，Al-Cu-Ti和Al-Ni-Ti-Fe-Cu金属间化合物.随着焊接电流的增大，钛合金侧界面反应层的显微硬度逐渐增大，且反应层的宽度也逐渐变宽.
-
关键词:
- 冷金属过渡焊 /
- 钛合金/不锈钢焊接接头 /
- 铜-镍复合填充金属 /
- 拉剪强度
Abstract: Cold metal transfer welding of titanium alloy and stainless steel was carried out using copper-nickel composite filler metal. The effects of copper-nickel composite filler metal on the microstructure and mechanical properties of the joint were investigated by scanning electron microscope and X-ray diffractometer. The results show that defect-free welded joint was obtained, and Ti-Ni intermetallic compound was formed in the joint. As the hardness of the Ti-Ni intermetallic compound is lower than that of the Ti-Fe and Ti-Cu intermetallic compounds, the tensile property of the joint was improved. When the welding current was set at 182 A, the maximum tensile and shear strength of the joint was achieved at 348 MPa. The titanium alloy/stainless steel joint was composed of stainless steel-weld metal interface, stainless steel-pure nickel-titanium alloy interface, titanium alloy-weld metal interface and weld metal, and Ti-Cu, Ti-Ni, Al-Cu-Ti and Al-Ni-Ti-Fe-Cu intermetallic compounds were formed in the joint. With the increase of welding current, there was a gradual growth in the microhardness and the width of the interface reaction layer on the titanium alloy side. -
0. 序言
为满足轻量化及高可靠性的设计需求，具有高比强度的7xxx系(Al-Zn-Mg-Cu)高强铝合金被广泛应用于飞机蒙皮、桁条等零部件的制造[1-2]. 上述构件通常采用电阻点焊及铆接等传统工艺方法. 然而，电阻点焊在焊接铝合金时易产生裂纹和气孔等缺陷. 铆接会增加结构自重，也易产生间隙腐蚀. 回填式搅拌摩擦点焊(refill friction stir spot welding, RFSSW)是一种新型的固相点焊技术，该方法可通过搅拌头的旋转以及各部件的上下往复运动使焊点金属塑化，并同时进行金属的挤出和回填，最终实现冶金结合[3- 4]. 该方法可有效避免电阻点焊所引起的焊接缺陷. 同时，由于不需要填充材料，利于实现结构的轻量化. 此外，与传统直插式搅拌摩擦点焊相比，RFSSW可对匙孔进行回填，增加焊点面积，提高接头承载能力[5-6]. 基于此，RFSSW有望成为飞机制造新一代主导连接技术之一.
然而，由于Al-Zn-Mg-Cu体系共晶点较低，在RFSSW过程中会发生组分液化，并形成共晶组织，甚至产生液化裂纹，这将严重降低接头的力学性能[7]. 然而，常规RFSSW方法采用恒定的搅拌头转速，在搅拌套扎入阶段为了使材料快速塑化搅拌头转速相对较高，导致后续回填阶段热输入过高，难以有效抑制组分液化的发生.
针对上述问题，研究中发明了可变转速回填式搅拌摩擦点焊(variable rotation speed-refill friction stir spot welding, V-RFSSW)新方法. 该方法通过在在扎入阶段采用较高转速使材料快速塑化以保障焊点成形，后续回填阶段通过降低转速控制焊接热输入，以达到抑制组分液化，增加焊点材料强度，提升接头承载能力的目的. 文中针对7B04-T74铝合金开展V-RFSSW有限元数值仿真及焊接工艺试验，通过对焊接温度场及接头组织性能的研究，揭示V-RFSSW新方法对焊接热输入及接头组织性能的调控机制.
1. 有限元模型的建立
1.1 几何模型及网格划分
将工件设为两块75 mm × 75 mm × 1.9 mm板材搭接组成，搭接面积为75 mm × 30 mm (图1). 为了避免接触不稳定等问题，搭接界面被忽略. 采用尺寸疏密过渡的四面体网格对模型进行划分. 在搅拌头下方的焊接区域工件网格边长为0.5 mm，焊接区以外网格边长由1 mm向3 mm过渡. 搅拌针、搅拌套、压紧环以及垫板的网格边长设置为0.8 mm.
1.2 材料本构及摩擦产热模型
7B04铝合金本构模型可以用Arrhenius方程进行描述，真实应力σ、温度T以及应变速率ε之间的关系可表述为
$$ \varepsilon = A{(\sin \alpha \sigma )^n}\exp \left(\frac{{ - Q}}{{RT}}\right) $$ (1) 式中：A为结构因子，为1.15×1017；α为应力水平参数，为0.00882；n为应力指数，为6.3346；Q为热变形激活能，为228 620 J/mol；R为气体常数，为8.314 J/(mol∙K)[8]. 此外，不同温度热导率、换热系数等参数取值参照文献[8]. 采用剪切摩擦模型描述焊具与被焊板材之间的摩擦行为，摩擦力f可表示为
$$ f = m\tau $$ (2) 式中：m为剪切摩擦因子；τ为材料剪切屈服应力.根据文献[8]，当温度低于475 ℃时，m = 0.32保持恒定；当温度高于475 ℃时，7B04铝合金沉淀相开始局部熔化，m呈线性下降；当材料温度升至532 ℃时，材料整体开始熔化，此时m降至0.
采用此模型对搅拌头扎入阶段转速ω1 = 1500 r/min、搅拌头回填阶段转速ω2 = 1000 r/min的V-RFSSW进行三维热-流耦合数值仿真，并与试验测温结果进行对比. 图2为距焊点中心6 mm且距离上表面1 mm处焊接热循环模拟与实际测量的热循环曲线对比. 结果表明，二者吻合良好，表明所建立的模型具有较好的预测精度.
![]()
图 2 焊接热循环仿真与试验结果对比Figure 2. Comparison of welding thermal cycle simulation and measurement results2. 试验方法
试验采用2 mm厚7B04-T74铝合金作为母材，其化学成分及力学性能如表1所示. 试验采用航天工程装备(苏州)有限公司生产的FSSW-04C型回填式搅拌摩擦点焊设备. 搅拌头由搅拌针、搅拌套、压紧环三者间隙装配组成, 其中搅拌针、搅拌套、压紧环外径分别为5.2，9.0和18.0 mm. 采用RFSSW与V-RFSSW对比的方式进行试验研究. 首先，固定两种焊接方法的搅拌套扎入深度(2.5 mm)及焊接时间(5 s)相同. 其中，RFSSW搅拌头转速ω1 = ω2 = 1500 r/min. 相应的V-RFSSW搅拌头扎入阶段转速ω1 = 1500 r/min，而搅拌头回填阶段转速降低至ω2 = 1000 r/min. 为了更充分的对比V-RFSSW的效果，采用与V-RFSSW的平均转速相同的RFSSW试验进行对比，即ω = 1/2(ω1 + ω2). 此时选取的RFSSW工艺参数为ω1 = ω2 = 1250 r/min. 具体工艺参数如表2所示.
表 1 7B04-T74铝合金的化学成分和力学性能Table 1. Chemical compositions and mechanical properties of 7B04-T74 aluminum alloy化学成分(质量分数，%) 力学性能 Zn Mg Cu Mn Fe Cr Si Ni Ti Al 抗拉强度Rm/MPa 屈服强度ReL/MPa 断后伸长率A(%) 5.86 2.51 1.62 0.34 0.18 0.15 0.07 0.05 0.03 余量 550 492 10.0 表 2 工艺参数Table 2. Welding parameters序号 方法 扎入阶段转速
ω1 /(r·min−1)回填阶段转速
ω2 /(r·min−1)下扎深度
p /mm焊接时间
tw /s峰值温度
Tmax /℃高温停留时间
th /s1 RFSSW 1250 1250 2.5 5 475 0 2 RFSSW 1500 1500 2.5 5 522 1.6 3 V-RFSSW 1500 1000 2.5 5 493 0.4 3. 结果与讨论
3.1 温度场及热循环
图3为ω1 = 1500 r/min，ω2 = 1000 r/min时V-RFSSW接头不同时刻的温度场分布特征. 温度场围绕搅拌头轴线呈圆形对称分布. 在下扎阶段初期，被搅拌头加热的塑性金属向上流入搅拌套的空腔内，导致高温区域集中在此处，此时搅拌套内塑形金属温度趋于一致. 随着焊接的进行，空腔内材料温度逐渐升高，且由于底部散热条件较差，高温区域集中在空腔底部，在纵向上呈现明显的温度梯度. 随着焊接进入回填阶段，由于转速降低，空腔内温度有所下降.
![]()
图 3 不同时刻V-RFSSW接头上表面及横截面的温度分布Figure 3. Temperature distributions of the top surface and cross-section of the joints at different time for V-RFSSW. (a) t = 1 s (the top surface); (b) t = 2.5 s (the top surface); (c) t = 4 s (the top surface); (d) t=1 s (cross-section); (e) t = 2.5 s (cross-section); (f) t = 4 s (cross-section)为了揭示V-RFSSW方法焊接热循环特征及降低焊接热输入的效果，采用焊接结束时焊点中轴线上距离上表面1 mm的特征点，其热循环来代表RFSSW及V-RFSSW搅拌区热循环，结果如图4所示. 对于RFSSW，当ω1 = ω2 = 1500 r/min时，搅拌区焊接热循环曲线呈现为先升高后下降的趋势，峰值温度出现在下扎阶段t = 3 s时，达到522 ℃. 对于7B04铝合金，当温度超过475 ℃时材料开始发生组分液化[9]，因此，研究中把温度超过此温度的时间定义为高温停留时间(th)，此时th = 1.6 s. 对于V-RFSSW，在扎入阶段搅拌区升温速率几乎相同. 由于回填阶段转速ω2由1500 r/min降为1000 r/min，导致热循环曲线发生陡降，峰值温度在焊接扎入阶段结束时刻，即t = 2.5 s时出现，峰值温度493 ℃，相应的高温停留时间th = 1.6 s. 可见，V-RFSSW通过降低回填阶段的搅拌头转速可明显抑制焊接热输入，降低搅拌区峰值温度及高温停留时间. 虽然对于以上两种方法在扎入阶段完全相同，但是由于回填阶段转速不同，必然对搅拌区材料流动造成了影响. 而研究中针对两种方法选取的搅拌区热循环特征点是焊点成形以后的相同位置点，由于之前经历的材料流动行为的差异导致了扎入阶段热循环曲线有所差异.
将V-RFSSW与平均转速相同的RFSSW相对比，此时RFSSW工艺参数为ω1 = ω2 = 1250 r/min. 结果表明，此参数下焊接扎入阶段升温速率明显下降，搅拌区峰值温度Tmax = 475 ℃，高温停留时间th = 0. 可见，V-RFSSW对比于平均转速相同的RFSSW，并未降低焊接热输入.
3.2 焊点成形及接头微观组织特征
图5为不同焊接方法下焊点横截面宏观形貌. 对于RFSSW，当ω1 = ω2 = 1500 r/min时，可以获得良好的焊点成形(图5a). 将搅拌套直接作用区定义为搅拌区，此区域为焊点的主要承载区域. 紧邻搅拌区材料受到搅拌区内剧烈流动塑性材料的剪切作用，也发生了一定程度的塑性变形，可定义为热力影响区. 与热力影响区相邻，只受到焊接热作用的区域定义为热影响区. 对于V-RFSSW，降低回填阶段转速ω2至1000 r/min，仍可获得较好的焊点成形(图5b). 然而，与V-RFSSW平均转速相同RFSSW，即ω1 = ω2 = 1250 rpm时，在焊点上表面出现明显的环沟槽缺陷(图5c)，这将显著降低焊点上板的承载厚度，导致承载能力的下降. 这是由于当扎入阶段转速较低时，焊接产热不足以使被焊材料发生充分的塑化，无法全部进入搅拌套的空腔内，在回填阶段塑性材料不足以填满整个焊点，导致缺陷的生成. V-RFSSW方法既可以通过较高的扎入阶段转速保证焊点成形，又可以通过降低回填阶段转速抑制焊接热输入，降低峰值温度及高温停留时间.
![]()
图 5 RFSSW和V-RFSSW焊点横截面Figure 5. Cross sections of RFSSW and V-RFSSW joints. (a) ω1 = ω2 = 1 500 r/min; (b) ω1 = 1 500 r/min, ω2 = 1 000 r/min; (c) ω1 = ω2 = 1 250 r/min图6为RFSSW和V-RFSSW搅拌区微观组织形貌. 如图6a和图6b所示，两种焊接方法下搅拌区内均呈现细小的等轴晶，这是由于铝合金在高温及大塑性变形下发生了动态再结晶[10]. 在RFSSW搅拌区内发现了大量的黑色条带状组织，如图6a箭头所示. 通过扫描电子显微镜(scanning electron microscope，SEM)对该组织进行放大观察(图6c)，可以判断其为聚集在晶界附近的共晶组织. 经能谱仪(energy dispersive spectrometer，EDS)分析，发现相对母材晶界共晶组织内Zn，Cu等合金元素发生了富集，如图6d所示. 这说明RFSSW过程中7B04铝合金沉淀相在晶界处发生了组分液化并形成局部液相，在随后的冷却过程中液相来不及向基体内扩散，并在晶界处发生了liquid→α-Al + S(Al2CuMg) + η(MgZn2)等三元共晶反应[11]. 而V-RFSSW搅拌区内并未发现明显的黑色条带组织，说明采用该方法成功抑制了组分液化的发生. 值得注意的是，虽然V-RFSSW搅拌区峰值温度超过了组分液化的起始温度(475 ℃)，但由于高温停留时间较短，不足以生成足够的液相来形成共晶组织.
![]()
图 6 RFSSW和V-RFSSW接头搅拌区微观组织Figure 6. Microstructures in stir zones of RFSSW and V-RFSSW joints. (a) ω1 = ω2 = 1500 r/min; (b) ω1 = 1500 r/min, ω2 = 1000 r/min; (c) SEM magnification of black strip microstructure in Fig. 6a; (d) EDS results of eutectic phase3.3 接头的力学性能
对不同焊接方法接头横截面显微硬度分布进行了测试，结果如图7所示. 不同焊接方法下，接头的显微硬度分布曲线均呈“W”形. 对于RFSSW，当ω1=ω2=1500 r/min时，搅拌区范围较大，但平均硬度较低. V-RFSSW通过降低回填阶段搅拌头转速可抑制焊接热输入，此时搅拌区范围有所收窄，平均显微硬度有所增加. 对于平均转速相同的RFSSW，由数值仿真结果可知，此时焊接热输入最低，相应的搅拌区范围最窄，平均硬度值最高.
![]()
图 7 RFSSW和V-RFSSW接头的横截面显微硬度分布Figure 7. Hardness distributions in the cross-sections of RFSSW and V-RFSSW joints不同接头拉剪失效载荷及断裂接头横截面如图8所示. 不同方法所获得的接头均以“纽扣”形式发生断裂，裂纹的萌生和扩展均发生在搅拌区，这说明搅拌区为接头承载的主要区域. 当ω1 = ω2 = 1500 r/min时，RFSSW接头平均拉剪失效载荷为8162 N. 而V-RFSSW接头(ω1 = 1500 r/min，ω2 = 1000 r/min)拉剪失效载荷显著提高，达到8835 N. 这主要由于V-RFSSW通过降低了焊接热输入，提高了搅拌区材料强度的同时，抑制了该区域的组分液化，避免了脆硬的共晶组织生成，对裂纹的萌生及扩展起到了较好的抑制作用. 虽然在ω1 = ω2 = 1250 r/min下RFSSW接头搅拌区的显微硬度较高，同时也无共晶组织生成，但焊点表面出现了环沟槽缺陷，导致接头的力学性能较低.
4. 结论
(1) 针对2 mm厚的7B04-T74铝合金，采用可变转速回填式搅拌摩擦点焊进行数值模拟分析及试验研究发现，V-RFSSW温度场围绕搅拌头轴线呈圆形对称分布. 焊点高温区域集中在搅拌套空腔内部. 与扎入阶段转速相同的常规RFSSW相比，V-RFSSW新方法通过降低回填阶段搅拌头转速可显著降低焊接峰值温度及高温停留时间.
(2) V-RFSSW新方法既可在扎入阶段使材料充分塑化以保证焊点成形，又可以通过降低焊接热输入抑制组分液化的发生，避免共晶相的生成.
(3) V-RFSSW与常规RFSSW接头显微硬度均呈“W”形分布，且扎入阶段转速相同的情况下V-RFSSW接头搅拌区的平均硬度值较高. 在拉剪载荷下均以“纽扣”形式发生断裂，其中V-RFSSW接头拉剪失效载荷为8835 N，高于RFSSW接头的8162 N.
-
![]()
图 3 TC4/Cu-Ni/304接头不锈钢侧界面的微观组织
Figure 3. Microstructure of interface at the stainless steel side of TC4/Cu-Ni/304 joint
![]()
图 4 TC4/Cu-Ni/304接头不锈钢-纯镍-钛合金界面I, II, III, IV区域的微观组织
Figure 4. Microstructure of I, II, III, IV region of interface from stainless steel to pure nickel to titanium alloy of TC4/Cu-Ni/304 joint. (a) interface from stainless steel to pure nickel to titanium alloy; (b) I region; (c) II region; (d) III region; (e) IV region
![]()
图 5 TC4/Cu-Ni/304接头钛合金侧界面和焊缝金属的微观组织
Figure 5. Microstructure of regions on interface at the titanium alloy side and weld metal of TC4/Cu-Ni/304 joint. (a) interface at the titanium alloy side of TC4/Cu-Ni/304 joint; (b) I region; (c) II region; (d) III region; (e) WM
![]()
图 6 不同焊接电流下TC4/Cu-Ni/304接头的显微硬度分布
Figure 6. Microhardness distribution of TC4/Cu-Ni/304 joint with different welding current. (a) region from TC4 to pure nickel interlayer to 304 to WM; (b) region from TC4 to WM
![]()
图 7 不同焊接电流下TC4/Cu-Ni/304接头的拉剪强度
Figure 7. Tensile-shear strength of TC4/Cu-Ni/304 joint with different welding current
![]()
图 8 TC4/304接头的断口分析
Figure 8. Fracture analysis of TC4/304 joint. (a) fracture surface of TC4/Cu-Ni/304 joint; (b) fracture side of TC4/Cu-Ni/304 joint; (c) fracture surface of TC4/Cu/304 joint; (d) fracture side of TC4/Cu/304 joint
![]()
图 9 TC4/Cu-Ni/304接头的断口表面XRD图谱
Figure 9. XRD pattern of fracture surface of TC4/Cu-Ni/304 joint
表 1 材料的化学成分 (质量分数,%)
Table 1 Chemical compositions of materials
材料 Cr Ni Mn Si Fe Al V Ti Cu C N H O Pb Zn 304 18.0 ~ 20.0 8.0 ~ 12.0 2.0 1.0 余量 — — — — ≤0.03 — — — — — TC4 — — — — 0.3 5.5 ~ 6.8 3.5 ~ 4.5 余量 — ≤0.5 ≤0.5 ≤0.5 ≤0.5 — — ERCuNiAl — 6.0 1.0 — — 8.0 — — 余量 — — — — ≤0.1 ≤0.1 
下载: 导出CSV
表 2 CMT焊的工艺参数
Table 2 Process parameters of CMT welding
试样
编号送丝速度
νs /(m·min−1)焊接速度
ν/(mm·s−1)焊接电流
I/A1 4.5 8.53 141 2 5.0 8.53 160 3 5.5 8.53 171 4 6.0 8.53 182
下载: 导出CSV
表 3 图3和图4中各点的EDS测试结果(原子分数，%)
Table 3 EDS test results of each point in Fig. 3 − Fig. 4
测试点 Al Ni Ti Fe Cu Cr 可能的相 1 17.95 6.82 0.88 7.39 62.72 1.31 铜固溶体和Al3Ti相 2 13.74 6.61 2.64 51.52 8.04 13.81 Fe-Cr-Al IMCs 3 2.27 62.15 17.71 11.85 1.66 2.98 Fe固溶体和TiNi3 IMCs 4 1.29 68.48 24.05 1.28 2.23 0.57 Ni固溶体和TiNi3 IMCs 5 1.13 71.79 24.22 0.39 0.39 0.27 TiNi3和TiNi IMCs 6 0.58 70.87 23.89 0.43 1.17 0.31 TiNi3和TiNi IMCs 7 7.25 44.92 41.48 0.68 1.87 0.61 TiNi和TiNi2 IMCs 8 15.13 10.88 57.17 2.30 4.97 1.65 Ti-Al-Ni IMCs 9 6.83 25.18 57.47 3.96 2.74 0.67 Ti固溶体和TiNi2 IMCs
下载: 导出CSV
表 4 图5中各点的EDS测试结果(原子分数，%)
Table 4 EDS test results of each point in Fig. 5
测试点 Al Ni Ti Fe Cu Cr 可能的相 10 13.71 2.59 44.59 4.28 29.11 1.30 Ti2Cu和AlTi3 IMCs 11 22.02 3.84 27.05 1.93 42.83 0.55 AlCuTi和AlCu2Ti IMCs 12 6.87 2.13 43.58 1.81 38.48 0.95 TiCu和Ti2Cu IMCs 13 21.35 4.26 23.61 2.35 44.87 0.69 AlCuTi和AlCu2Ti IMCs 14 27.52 21.29 20.08 17.07 10.45 1.73 Al-Ni-Ti-Fe-Cu IMCs 15 17.40 3.74 1.61 3.75 68.98 1.40 铜固溶体和Al3Ti相 16 25.75 25.39 21.11 12.86 11.96 1.83 Al-Ni-Ti-Fe-Cu IMCs 17 14.83 5.61 1.74 3.54 72.98 1.01 铜固溶体和Al3Ti相
下载: 导出CSV
-
[1] 常敬欢. 钛/钢冷金属过渡焊接头的连接机理及腐蚀行为研究[D]. 兰州: 兰州理工大学, 2021. Chang Jinghuan. Study on joining mechanism and corrosion behavior of titanium/steel cold metal transfer welded joints[D]. Lanzhou: Lanzhou University of Technology, 2021.
[2] Richaud Minier H, Marchebois H, Gerard P. Titanium and super stainless steel welded tubing solutions for sea water cooled heat exchangers[J]. Materials Technology, 2009, 24(3): 191 − 200. doi: 10.1179/106678509X12475883949422
[3] 张岩, 谷晓燕, 朱丽娟, 等. SUS301L 薄板不锈钢脉冲激光焊接头的组织特点与硬度分布[J]. 材料热处理学报, 2016, 37(S1): 55 − 60. Zhang Yan, Gu Xiaoyan, Zhu Lijuan, et al. Microstructure characteristics and hardness distribution of pulsed laser welded SUS301L stainless steel sheet joint[J]. Transactions of Materials and Heat Treatment, 2016, 37(S1): 55 − 60.
[4] Shankar A R, Sole R, Thyagarajan K, et al. Failure analysis of titanium heater tubes and stainless steel heat exchanger weld joints in nitric acid loop[J]. Engineering Failure Analysis, 2019, 99: 248 − 262. doi: 10.1016/j.engfailanal.2019.02.016
[5] 温炳权, 王宾, 路学成. 金属材料手册[M]. 北京: 电子工业出版社, 2013. Wen Bingquan, Wang Bin, Lu Xuecheng. Handbook of metal materials[M]. Beijing: Electronic Industry Press, 2013.
[6] Villars P, Okamoto H. Handbook of ternary alloy phase diagrams[M]. ASM International, Materials Park, OH, USA, 1995.
[7] 祝要民, 李青, 邱然锋, 等. 钛/钢异种金属焊接的研究现状[J]. 电焊机, 2016, 46(11): 78 − 82. Zhu Yaomin, Li Qing, Qiu Ranfeng, et al. Researching status of dissimilar metal welding of titanium and steel[J]. Electric Welding Machine, 2016, 46(11): 78 − 82.
[8] Nizamettin Kahramana, Behcet Gulenc. Joining of titanium/stainless steel by explosive welding and effect on interface[J]. Journal of Materials Processing Technology, 2005, 169(2): 127 − 133. doi: 10.1016/j.jmatprotec.2005.06.045
[9] Velmurugan C, Senthilkumar V, Sarala S, et al. Low temperature diffusion bonding of Ti-6Al-4V and duplex stainless steel[J]. Journal of Materials Processing Technology, 2016, 234: 272 − 279. doi: 10.1016/j.jmatprotec.2016.03.013
[10] Li X, Li J, Liao Z, et al. Microstructure evolution and mechanical properties of rotary friction welded TC4/SUS321 joints at various rotation speeds[J]. Materials & Design, 2016, 99: 26 − 36.
[11] Kundu S, Ghosh M, Laik A, et al. Diffusion bonding of commercially pure titanium to 304 stainless steel using copper interlayer[J]. Materials Science & Engineering: A, 2005, 407(1-2): 154 − 160. doi: 10.1016/j.msea.2005.07.010
[12] Deng Y Q, Sheng G M, Yin L J, et al. Impulse pressuring diffusion bonding of titanium to stainless steel using a copper interlayer[J]. Rare Metal Materials and Engineering, 2015, 44(5): 1041 − 1045. doi: 10.1016/S1875-5372(15)30063-1
[13] Kundu S, Sam S, Chatterjee S. Interfacial reactions and strength properties in dissimilar titanium alloy/Ni alloy/microduplex stainless steel diffusion bonded joints[J]. Materials Science & Engineering: A, 2013, 560: 288 − 295. doi: 10.1016/j.msea.2012.09.069
[14] Song T F, Jiang X S, Shao Z Y, et al. Microstructure and mechanical properties of vacuum diffusion bonded joints between Ti-6Al-4V titanium alloy and AISI316L stainless steel using Cu/Nb multi-interlayer[J]. Vacuum, 2017, 145: 68 − 76. doi: 10.1016/j.vacuum.2017.08.017
[15] 毕志雄, 李雪交, 吴勇, 等. 钛箔/钢爆炸焊接的界面结合性能[J]. 焊接学报, 2022, 43(4): 81 − 85. Bi Zhixiong, Li Xuejiao, Wu Yong, et al. Interfacial bonding properties of titanium foil/steel explosive welding[J]. Transactions of the China Welding Institution, 2022, 43(4): 81 − 85.
[16] Vigraman T, Ravindran D, Narayanasamy R. Effect of phase transformation and intermetallic compounds on the microstructure and tensile strength properties of diffusion-bonded joints between Ti-6Al-4V and AISI 304L[J]. Materials & Design, 2012, 36: 714 − 727.
[17] Li S, Chen Y, Zhou X, et al. High-strength titanium alloy/steel butt joint produced via friction stir welding[J]. Materials Letters, 2019, 234: 155 − 158. doi: 10.1016/j.matlet.2018.09.094
[18] Wang T, Zhang B, Wang H, et al. Microstructures and mechanical properties of electron beam-welded titanium-steel joints with vanadium, nickel, copper and silver filler metals[J]. Journal of Materials Engineering and Performance, 2014, 23(4): 1498 − 1504. doi: 10.1007/s11665-014-0897-8
[19] Hao X, Dong H, Xia Y, et al. Microstructure and mechanical properties of laser welded TC4 titanium alloy/304 stainless steel joint with (CoCrFeNi)100-xCux high-entropy alloy interlayer[J]. Journal of Alloys and Compounds, 2019, 803: 649 − 657. doi: 10.1016/j.jallcom.2019.06.225
[20] Zhang Y, Chen Y, Zhou J, et al. Experimental and numerical study on microstructure and mechanical properties for laser welding-brazing of TC4 titanium alloy and 304 stainless steel with Cu-base filler metal[J]. Journal of Materials Research and Technology, 2020, 9(1): 465 − 477. doi: 10.1016/j.jmrt.2019.10.075
[21] 牛小男, 崔丽, 王鹏, 等. 镍铝青铜过渡层对钛合金/不锈钢异种材料激光焊接头组织与力学性能的影响[J]. 焊接学报, 2022, 43(1): 42 − 47. Niu Xiaonan, Cui Li, Wang Peng, et al. Effect of nickel aluminum bronze transition layer on microstructure and mechanical properties of laser welded titanium alloy/stainless steel joint[J]. Transactions of the China Welding Institution, 2022, 43(1): 42 − 47.
[22] Li W, Chang J H, Wen B F, et al. Joining of dissimilar metals between magnesium AZ31B and aluminum A6061-T6 using galvanized steel as a transition joining layer[J]. Journal of Iron and Steel Research International, 2022, 29(4): 677 − 686. doi: 10.1007/s42243-021-00589-z
[23] Cao R, Chang J H, Huang Q, et al. Behaviors and effects of Zn coating on welding-brazing process of Al-steel and Mg-steel dissimilar metals[J]. Journal of Manufacturing Processes, 2018, 31: 674 − 688. doi: 10.1016/j.jmapro.2018.01.001
[24] 黄倩, 曹睿, 朱海霞, 等. 铝/裸钢板冷金属过渡点塞焊接头组织及力学性能[J]. 焊接学报, 2014, 35(11): 59 − 62. Huang Qian, Cao Rui, Zhu Haixia, et al. Process and performance of cold metal transfer spot plug welding between aluminum alloy and bare steel[J]. Transactions of the China Welding Institution, 2014, 35(11): 59 − 62.
[25] Zhang B G, Wang T, Chen G Q, et al. Contact reactive joining of TA15 and 304 stainless steel via a copper interlayer heated by electron beam with a beam deflection[J]. Journal of Materials Engineering and Performance, 2012, 21(10): 2067 − 2073. doi: 10.1007/s11665-012-0132-4
[26] 李标峰. 钛与钢及钛复合钢板的焊接性研究(Ⅱ)[J]. 材料开发与应用, 2004, 19(2): 45 − 46. doi: 10.19515/j.cnki.1003-1545.2004.02.013 Li Biaofeng. Study on the weldability of titanium and steel and titanium clad steel plate(Ⅱ)[J]. Development and Application of Materials, 2004, 19(2): 45 − 46. doi: 10.19515/j.cnki.1003-1545.2004.02.013
[27] 常敬欢, 曹睿, 闫英杰. 钛合金/不锈钢冷金属过渡焊接头组织及性能[J]. 焊接学报, 2021, 42(6): 44 − 51. Chang Jinghuan, Cao Rui, Yan Yingjie. Microstructure and properties of titanium alloy/stainless steel joint by cold metal transfer joining technology[J]. Transactions of the China Welding Institution, 2021, 42(6): 44 − 51.
-
期刊类型引用(2)
1. 赵衍华，张粟泓，王非凡，郝云飞，宋建岭，孙世烜，王国庆. 搅拌摩擦焊接与加工技术进展. 航天制造技术. 2025(01): 1-25 . 
百度学术
2. 刘柏韬，顾彬，余海东. 关于铝合金薄板高速搅拌摩擦焊接搅拌头的新型设计. 机械设计与研究. 2023(05): 152-157 . 百度学术
其他类型引用(3)
计量
- 文章访问数: 285
- HTML全文浏览量: 37
- PDF下载量: 45
- 被引次数: 5