Microstructure and mechanical properties of laser cladding TC4/Inconel 625/316L stainless steel gradient material
-
摘要: 为了提高不锈钢工件的综合性能，采用激光熔覆工艺在不锈钢上制备TC4熔覆层、Inconel 625熔覆层作为过渡层，通过光学显微镜、扫描电子显微镜、X射线衍射仪、能谱仪、硬度计、摩擦磨损和电化学测试等研究了TC4熔覆层微观组织、显微硬度、电化学性能和摩擦磨损性能. 结果表明，熔覆层成形质量良好且具有均匀致密的微观组织. 熔覆过程中，由于元素扩散与高温作用发生的共晶反应，熔覆层中生成CrNi2和Ti2Ni增强相，大大提升了熔覆层的硬度与耐磨性；TC4熔覆层磨损机制主要为磨粒磨损与氧化磨损，耐磨性优于基体；TC4熔覆层的腐蚀电流密度小于基体，耐蚀性显著高于基体.Abstract: In order to improve the comprehensive performance of stainless steel workpiece, a TC4 cladding layer was prepared on stainless steel by laser cladding process, with Inconel 625 cladding layer as the transition layer. The microstructure, microhardness, electrochemical properties and tribological properties of TC4 cladding layer were studied. The results show that the cladding layer has high forming quality and uniform and dense microstructure. During the cladding process, the eutectic reaction caused by element diffusion and high temperature leads to the formation of CrNi2 and Ti2Ni reinforced phases in the cladding layer, which has signifcantley improved the hardness and wear resistance of the cladding layer. The wear mechanism of TC4 cladding layer is mainly abrasive wear and oxidation wear, and the wear resistance is better than that of the matrix. The corrosion current density is lower, and the corrosion resistance of TC4 cladding layer is significantly higher than that of the matrix.
-
Keywords:
- laser cladding /
- reinforced phase /
- eutectic reaction /
- wear /
- corrosion resistance
-
0. 序言
为满足轻量化及高可靠性的设计需求，具有高比强度的7xxx系(Al-Zn-Mg-Cu)高强铝合金被广泛应用于飞机蒙皮、桁条等零部件的制造[1-2]. 上述构件通常采用电阻点焊及铆接等传统工艺方法. 然而，电阻点焊在焊接铝合金时易产生裂纹和气孔等缺陷. 铆接会增加结构自重，也易产生间隙腐蚀. 回填式搅拌摩擦点焊(refill friction stir spot welding, RFSSW)是一种新型的固相点焊技术，该方法可通过搅拌头的旋转以及各部件的上下往复运动使焊点金属塑化，并同时进行金属的挤出和回填，最终实现冶金结合[3- 4]. 该方法可有效避免电阻点焊所引起的焊接缺陷. 同时，由于不需要填充材料，利于实现结构的轻量化. 此外，与传统直插式搅拌摩擦点焊相比，RFSSW可对匙孔进行回填，增加焊点面积，提高接头承载能力[5-6]. 基于此，RFSSW有望成为飞机制造新一代主导连接技术之一.
然而，由于Al-Zn-Mg-Cu体系共晶点较低，在RFSSW过程中会发生组分液化，并形成共晶组织，甚至产生液化裂纹，这将严重降低接头的力学性能[7]. 然而，常规RFSSW方法采用恒定的搅拌头转速，在搅拌套扎入阶段为了使材料快速塑化搅拌头转速相对较高，导致后续回填阶段热输入过高，难以有效抑制组分液化的发生.
针对上述问题，研究中发明了可变转速回填式搅拌摩擦点焊(variable rotation speed-refill friction stir spot welding, V-RFSSW)新方法. 该方法通过在在扎入阶段采用较高转速使材料快速塑化以保障焊点成形，后续回填阶段通过降低转速控制焊接热输入，以达到抑制组分液化，增加焊点材料强度，提升接头承载能力的目的. 文中针对7B04-T74铝合金开展V-RFSSW有限元数值仿真及焊接工艺试验，通过对焊接温度场及接头组织性能的研究，揭示V-RFSSW新方法对焊接热输入及接头组织性能的调控机制.
1. 有限元模型的建立
1.1 几何模型及网格划分
将工件设为两块75 mm × 75 mm × 1.9 mm板材搭接组成，搭接面积为75 mm × 30 mm (图1). 为了避免接触不稳定等问题，搭接界面被忽略. 采用尺寸疏密过渡的四面体网格对模型进行划分. 在搅拌头下方的焊接区域工件网格边长为0.5 mm，焊接区以外网格边长由1 mm向3 mm过渡. 搅拌针、搅拌套、压紧环以及垫板的网格边长设置为0.8 mm.
1.2 材料本构及摩擦产热模型
7B04铝合金本构模型可以用Arrhenius方程进行描述，真实应力σ、温度T以及应变速率ε之间的关系可表述为
$$ \varepsilon = A{(\sin \alpha \sigma )^n}\exp \left(\frac{{ - Q}}{{RT}}\right) $$ (1) 式中：A为结构因子，为1.15×1017；α为应力水平参数，为0.00882；n为应力指数，为6.3346；Q为热变形激活能，为228 620 J/mol；R为气体常数，为8.314 J/(mol∙K)[8]. 此外，不同温度热导率、换热系数等参数取值参照文献[8]. 采用剪切摩擦模型描述焊具与被焊板材之间的摩擦行为，摩擦力f可表示为
$$ f = m\tau $$ (2) 式中：m为剪切摩擦因子；τ为材料剪切屈服应力.根据文献[8]，当温度低于475 ℃时，m = 0.32保持恒定；当温度高于475 ℃时，7B04铝合金沉淀相开始局部熔化，m呈线性下降；当材料温度升至532 ℃时，材料整体开始熔化，此时m降至0.
采用此模型对搅拌头扎入阶段转速ω1 = 1500 r/min、搅拌头回填阶段转速ω2 = 1000 r/min的V-RFSSW进行三维热-流耦合数值仿真，并与试验测温结果进行对比. 图2为距焊点中心6 mm且距离上表面1 mm处焊接热循环模拟与实际测量的热循环曲线对比. 结果表明，二者吻合良好，表明所建立的模型具有较好的预测精度.
![]()
图 2 焊接热循环仿真与试验结果对比Figure 2. Comparison of welding thermal cycle simulation and measurement results2. 试验方法
试验采用2 mm厚7B04-T74铝合金作为母材，其化学成分及力学性能如表1所示. 试验采用航天工程装备(苏州)有限公司生产的FSSW-04C型回填式搅拌摩擦点焊设备. 搅拌头由搅拌针、搅拌套、压紧环三者间隙装配组成, 其中搅拌针、搅拌套、压紧环外径分别为5.2，9.0和18.0 mm. 采用RFSSW与V-RFSSW对比的方式进行试验研究. 首先，固定两种焊接方法的搅拌套扎入深度(2.5 mm)及焊接时间(5 s)相同. 其中，RFSSW搅拌头转速ω1 = ω2 = 1500 r/min. 相应的V-RFSSW搅拌头扎入阶段转速ω1 = 1500 r/min，而搅拌头回填阶段转速降低至ω2 = 1000 r/min. 为了更充分的对比V-RFSSW的效果，采用与V-RFSSW的平均转速相同的RFSSW试验进行对比，即ω = 1/2(ω1 + ω2). 此时选取的RFSSW工艺参数为ω1 = ω2 = 1250 r/min. 具体工艺参数如表2所示.
表 1 7B04-T74铝合金的化学成分和力学性能Table 1. Chemical compositions and mechanical properties of 7B04-T74 aluminum alloy化学成分(质量分数，%) 力学性能 Zn Mg Cu Mn Fe Cr Si Ni Ti Al 抗拉强度Rm/MPa 屈服强度ReL/MPa 断后伸长率A(%) 5.86 2.51 1.62 0.34 0.18 0.15 0.07 0.05 0.03 余量 550 492 10.0 表 2 工艺参数Table 2. Welding parameters序号 方法 扎入阶段转速
ω1 /(r·min−1)回填阶段转速
ω2 /(r·min−1)下扎深度
p /mm焊接时间
tw /s峰值温度
Tmax /℃高温停留时间
th /s1 RFSSW 1250 1250 2.5 5 475 0 2 RFSSW 1500 1500 2.5 5 522 1.6 3 V-RFSSW 1500 1000 2.5 5 493 0.4 3. 结果与讨论
3.1 温度场及热循环
图3为ω1 = 1500 r/min，ω2 = 1000 r/min时V-RFSSW接头不同时刻的温度场分布特征. 温度场围绕搅拌头轴线呈圆形对称分布. 在下扎阶段初期，被搅拌头加热的塑性金属向上流入搅拌套的空腔内，导致高温区域集中在此处，此时搅拌套内塑形金属温度趋于一致. 随着焊接的进行，空腔内材料温度逐渐升高，且由于底部散热条件较差，高温区域集中在空腔底部，在纵向上呈现明显的温度梯度. 随着焊接进入回填阶段，由于转速降低，空腔内温度有所下降.
![]()
图 3 不同时刻V-RFSSW接头上表面及横截面的温度分布Figure 3. Temperature distributions of the top surface and cross-section of the joints at different time for V-RFSSW. (a) t = 1 s (the top surface); (b) t = 2.5 s (the top surface); (c) t = 4 s (the top surface); (d) t=1 s (cross-section); (e) t = 2.5 s (cross-section); (f) t = 4 s (cross-section)为了揭示V-RFSSW方法焊接热循环特征及降低焊接热输入的效果，采用焊接结束时焊点中轴线上距离上表面1 mm的特征点，其热循环来代表RFSSW及V-RFSSW搅拌区热循环，结果如图4所示. 对于RFSSW，当ω1 = ω2 = 1500 r/min时，搅拌区焊接热循环曲线呈现为先升高后下降的趋势，峰值温度出现在下扎阶段t = 3 s时，达到522 ℃. 对于7B04铝合金，当温度超过475 ℃时材料开始发生组分液化[9]，因此，研究中把温度超过此温度的时间定义为高温停留时间(th)，此时th = 1.6 s. 对于V-RFSSW，在扎入阶段搅拌区升温速率几乎相同. 由于回填阶段转速ω2由1500 r/min降为1000 r/min，导致热循环曲线发生陡降，峰值温度在焊接扎入阶段结束时刻，即t = 2.5 s时出现，峰值温度493 ℃，相应的高温停留时间th = 1.6 s. 可见，V-RFSSW通过降低回填阶段的搅拌头转速可明显抑制焊接热输入，降低搅拌区峰值温度及高温停留时间. 虽然对于以上两种方法在扎入阶段完全相同，但是由于回填阶段转速不同，必然对搅拌区材料流动造成了影响. 而研究中针对两种方法选取的搅拌区热循环特征点是焊点成形以后的相同位置点，由于之前经历的材料流动行为的差异导致了扎入阶段热循环曲线有所差异.
将V-RFSSW与平均转速相同的RFSSW相对比，此时RFSSW工艺参数为ω1 = ω2 = 1250 r/min. 结果表明，此参数下焊接扎入阶段升温速率明显下降，搅拌区峰值温度Tmax = 475 ℃，高温停留时间th = 0. 可见，V-RFSSW对比于平均转速相同的RFSSW，并未降低焊接热输入.
3.2 焊点成形及接头微观组织特征
图5为不同焊接方法下焊点横截面宏观形貌. 对于RFSSW，当ω1 = ω2 = 1500 r/min时，可以获得良好的焊点成形(图5a). 将搅拌套直接作用区定义为搅拌区，此区域为焊点的主要承载区域. 紧邻搅拌区材料受到搅拌区内剧烈流动塑性材料的剪切作用，也发生了一定程度的塑性变形，可定义为热力影响区. 与热力影响区相邻，只受到焊接热作用的区域定义为热影响区. 对于V-RFSSW，降低回填阶段转速ω2至1000 r/min，仍可获得较好的焊点成形(图5b). 然而，与V-RFSSW平均转速相同RFSSW，即ω1 = ω2 = 1250 rpm时，在焊点上表面出现明显的环沟槽缺陷(图5c)，这将显著降低焊点上板的承载厚度，导致承载能力的下降. 这是由于当扎入阶段转速较低时，焊接产热不足以使被焊材料发生充分的塑化，无法全部进入搅拌套的空腔内，在回填阶段塑性材料不足以填满整个焊点，导致缺陷的生成. V-RFSSW方法既可以通过较高的扎入阶段转速保证焊点成形，又可以通过降低回填阶段转速抑制焊接热输入，降低峰值温度及高温停留时间.
![]()
图 5 RFSSW和V-RFSSW焊点横截面Figure 5. Cross sections of RFSSW and V-RFSSW joints. (a) ω1 = ω2 = 1 500 r/min; (b) ω1 = 1 500 r/min, ω2 = 1 000 r/min; (c) ω1 = ω2 = 1 250 r/min图6为RFSSW和V-RFSSW搅拌区微观组织形貌. 如图6a和图6b所示，两种焊接方法下搅拌区内均呈现细小的等轴晶，这是由于铝合金在高温及大塑性变形下发生了动态再结晶[10]. 在RFSSW搅拌区内发现了大量的黑色条带状组织，如图6a箭头所示. 通过扫描电子显微镜(scanning electron microscope，SEM)对该组织进行放大观察(图6c)，可以判断其为聚集在晶界附近的共晶组织. 经能谱仪(energy dispersive spectrometer，EDS)分析，发现相对母材晶界共晶组织内Zn，Cu等合金元素发生了富集，如图6d所示. 这说明RFSSW过程中7B04铝合金沉淀相在晶界处发生了组分液化并形成局部液相，在随后的冷却过程中液相来不及向基体内扩散，并在晶界处发生了liquid→α-Al + S(Al2CuMg) + η(MgZn2)等三元共晶反应[11]. 而V-RFSSW搅拌区内并未发现明显的黑色条带组织，说明采用该方法成功抑制了组分液化的发生. 值得注意的是，虽然V-RFSSW搅拌区峰值温度超过了组分液化的起始温度(475 ℃)，但由于高温停留时间较短，不足以生成足够的液相来形成共晶组织.
![]()
图 6 RFSSW和V-RFSSW接头搅拌区微观组织Figure 6. Microstructures in stir zones of RFSSW and V-RFSSW joints. (a) ω1 = ω2 = 1500 r/min; (b) ω1 = 1500 r/min, ω2 = 1000 r/min; (c) SEM magnification of black strip microstructure in Fig. 6a; (d) EDS results of eutectic phase3.3 接头的力学性能
对不同焊接方法接头横截面显微硬度分布进行了测试，结果如图7所示. 不同焊接方法下，接头的显微硬度分布曲线均呈“W”形. 对于RFSSW，当ω1=ω2=1500 r/min时，搅拌区范围较大，但平均硬度较低. V-RFSSW通过降低回填阶段搅拌头转速可抑制焊接热输入，此时搅拌区范围有所收窄，平均显微硬度有所增加. 对于平均转速相同的RFSSW，由数值仿真结果可知，此时焊接热输入最低，相应的搅拌区范围最窄，平均硬度值最高.
![]()
图 7 RFSSW和V-RFSSW接头的横截面显微硬度分布Figure 7. Hardness distributions in the cross-sections of RFSSW and V-RFSSW joints不同接头拉剪失效载荷及断裂接头横截面如图8所示. 不同方法所获得的接头均以“纽扣”形式发生断裂，裂纹的萌生和扩展均发生在搅拌区，这说明搅拌区为接头承载的主要区域. 当ω1 = ω2 = 1500 r/min时，RFSSW接头平均拉剪失效载荷为8162 N. 而V-RFSSW接头(ω1 = 1500 r/min，ω2 = 1000 r/min)拉剪失效载荷显著提高，达到8835 N. 这主要由于V-RFSSW通过降低了焊接热输入，提高了搅拌区材料强度的同时，抑制了该区域的组分液化，避免了脆硬的共晶组织生成，对裂纹的萌生及扩展起到了较好的抑制作用. 虽然在ω1 = ω2 = 1250 r/min下RFSSW接头搅拌区的显微硬度较高，同时也无共晶组织生成，但焊点表面出现了环沟槽缺陷，导致接头的力学性能较低.
4. 结论
(1) 针对2 mm厚的7B04-T74铝合金，采用可变转速回填式搅拌摩擦点焊进行数值模拟分析及试验研究发现，V-RFSSW温度场围绕搅拌头轴线呈圆形对称分布. 焊点高温区域集中在搅拌套空腔内部. 与扎入阶段转速相同的常规RFSSW相比，V-RFSSW新方法通过降低回填阶段搅拌头转速可显著降低焊接峰值温度及高温停留时间.
(2) V-RFSSW新方法既可在扎入阶段使材料充分塑化以保证焊点成形，又可以通过降低焊接热输入抑制组分液化的发生，避免共晶相的生成.
(3) V-RFSSW与常规RFSSW接头显微硬度均呈“W”形分布，且扎入阶段转速相同的情况下V-RFSSW接头搅拌区的平均硬度值较高. 在拉剪载荷下均以“纽扣”形式发生断裂，其中V-RFSSW接头拉剪失效载荷为8835 N，高于RFSSW接头的8162 N.
-
![]()
图 1 TC4与Inconel 625熔覆层微观组织
Figure 1. Microstructure of TC4 and Inconel 625 cladding layers. (a) TC4; (b) Inconel 625
![]()
图 2 界面的SEM图像及其元素扩散情况
Figure 2. SEM images of interfaces and its element diffusion. (a) interface of TC4−Inconel 625; (b) line scanning results of TC4−Inconel 625; (c) interface of Inconel 625−316L; (d) line scanning results of Inconel 625−316L
![]()
图 3 TC4/Inconel 625/316L梯度材料XRD图谱
Figure 3. XRD images of TC4/Inconel 625/316L gradient material
![]()
图 4 TC4−Inconel 625界面局部SEM图像
Figure 4. Partially SEM images of TC4−Inconel 625 fusion interfaces. (a) TC4; (b) Inconel 625
![]()
图 6 316L不锈钢与TC4熔覆层的摩擦系数曲线
Figure 6. Coefficient of friction curve of the 316L stainless steel and TC4 cladding layer
![]()
图 7 316L不锈钢与TC4熔覆层磨损形貌
Figure 7. Wear morphology of 316L stainless steel and TC4 cladding layer. (a) 316L stainless steel; (b) TC4 cladding layer
![]()
图 8 316L不锈钢与TC4熔覆层开路电位曲线
Figure 8. Open circuit potential curves of 316L stainless steel and TC4 cladding layer. (a) 316L stainless steel; (b) TC4 cladding layer
![]()
图 9 等效电路图和EIS拟合图
Figure 9. Equivalent circuit diagram and EIS fitting diagram. (a) equivalent circuit diagram of TC4 cladding layer; (b) equivalent circuit diagram of 316L stainless steel; (c) EIS fitting diagram of TC4 cladding layer; (d) EIS fitting diagram of 316L stainless steel
![]()
图 10 TC4熔覆层与316L不锈钢的极化曲线
Figure 10. Polarization curves of TC4 cladding layer and substrate. (a) TC4 cladding layer; (b) 316L stainless steel
表 1 基体和熔覆粉末的化学成分(质量分数，%)
Table 1 Chemical compositions of substrate and cladding materials
材料 C Al Cr Ni Nb Mo V Fe Ti 316L 0.03 — 16 ~ 18 10 ~ 14 — 2 ~ 3 — 余量 — Inconel 625 0.03 — 20.21 余量 3.27 9.22 — 2.64 — TC4 <0.10 5.50 ~ 6.70 0.04 0.01 — — 3.45 ~ 4.50 ＜0.25 余量 
下载: 导出CSV
表 2 激光熔覆参数
Table 2 Laser cladding parameters
熔覆金属 光斑直径
D/mm扫描速度
v/(mm·s−1)送粉角度
θ/(°)送粉速度
vs/(g·min-1)Inconel 625 5 5.5 75 70 TC4 2 18 75 90
下载: 导出CSV
表 3 点1的EDS分析结果(原子分数，%)
Table 3 EDS analysis results of point 1
Al Ti V Ni Nb Mo 11.7 55.72 1.04 26.42 0.37 4.75
下载: 导出CSV
表 4 点2的EDS分析结果(原子分数，%)
Table 4 EDS analysis results of point 2
Cr Mn Si Ni Nb Mo 6.03 19.79 29.51 15.20 20.90 8.57
下载: 导出CSV
表 5 316L不锈钢与TC4熔覆层磨损表面EDS元素分析(质量分数，%)
Table 5 EDS elements analysis of wear surface of 316L stainless steel and TC4 cladding layer
表面 Ti Al Cr Ni Fe O TC4 熔覆层 36.00 3.61 1.46 3.87 — 55.06 316L不锈钢 — — 8.40 1.60 70.43 19.57
下载: 导出CSV
表 6 316L不锈钢EIS 拟合参数
Table 6 EIS fitting parameter table of 316L stainless steel
腐蚀液体系
中的s阻值
R4/（Ω·cm2）腐蚀层的电荷
转移电阻
R5/（Ω·cm2）常相位器件的电容
Q/（10−3F·cm2）CPE2-T CPE2-P 7.317 5 616 1.024 3 781.39
下载: 导出CSV
表 7 TC4熔覆层 EIS 拟合参数
Table 7 EIS fitting parameter table of TC4 cladding layer
腐蚀液体系中的阻值
R1/（Ω·cm2）腐蚀产物电容
C1/(F·cm2)腐蚀层的电荷转移电阻
R2/(Ω·cm2)腐蚀体系电荷移动阻值
R3/(Ω·cm2)常相位器件的电容Q/（10−5F·cm2） CPE2-T CPE2-P 9.18 1 5.23 63×10−6 36.6 7 965 42 9.85 02 58 690
下载: 导出CSV
表 8 TC4熔覆层与316L不锈钢的极化参数
Table 8 Polarization parameters of TC4 cladding layer and 316L stainless steel
试样 自腐蚀电位Ecorr /V 自腐蚀电流Icorr /(10−5A·cm−2) TC4 熔覆层 −1.035 5 2.511 9 316L不锈钢 −1.113 7 14.454
下载: 导出CSV
-
[1] 李妍,张国庆,吕建伟,等. 316不锈钢在海洋平台上的应用探讨[J]. 涂层与防护, 2023, 44(2): 1 − 3,7. Li Yan, Zhang Guoqing, Lyu Jianwei, et al. Discussion on the application of 316 stainless steel on offshore platform[J]. Coatings and Protection, 2023, 44(2): 1 − 3,7.
[2] 戴红霞, 冯晓丽. 厚度对车用304不锈钢表面激光熔覆钛涂层组织性能的影响[J]. 应用激光, 2020, 40(4): 626 − 630. Dai Hongxia, Feng Xiaoli. The effect of thickness on the microstructure and properties of laser clad titanium coating on 304 stainless steel for vehicles[J]. Applied Laser, 2020, 40(4): 626 − 630.
[3] 卜哲涵. 车用301L不锈钢腐蚀和力学性能研究[D]. 兰州: 兰州理工大学, 2021. Bu Zhehan. Research on corrosion and mechanical properties of 301L stainless steel for vehicles [D]. Lanzhou: Lanzhou University of Technology, 2021.
[4] Zhang Z, Yu T, Kovacevic R. Erosion and corrosion resistance of laser cladded AISI 420 stainless steel reinforced with VC[J]. Applied Surface Science, 2017, 410: 225 − 240. doi: 10.1016/j.apsusc.2017.03.137
[5] 张东玖,程从前,杨华,等. 钝化膜完整性对不锈钢海洋大气腐蚀的影响及其质检方法[J]. 腐蚀与防护, 2023, 44(5): 46 − 50,56. Zhang Dongjiu, Cheng Qianqian, Yang Hua, et al. Effect of passivated film integrity on Marine atmospheric corrosion of stainless steel and its quality inspection methods[J]. Corrosion and Protection, 2023, 44(5): 46 − 50,56.
[6] 尹程辉, 潘吉林, 陈俊航, 等. 热带海洋大气环境下不锈钢的腐蚀寿命评估[J]. 表面技术, 2022, 44(5): 183 − 193, 246. Yin Chenghui, Pan Jilin, Chen Junhang, et al. Corrosion life assessment of stainless steel in tropical marine atmospheric environment[J]. Surface Technology, 2022, 44(5): 183 − 193, 246.
[7] 杨青瑞. 固溶处理对304不锈钢腐蚀性能的影响及腐蚀演化模拟[D]. 银川: 宁夏大学, 2021. Yang Qingrui. Effect of solution treatment on corrosion properties of 304 stainless steel and simulation of corrosion evolution [D]. Yinchuan: Ningxia University, 2021.
[8] 李琳. 316L不锈钢在高温环境的氧化行为及氧化膜的冲刷腐蚀研究[D]. 北京: 中国石油大学(北京), 2020. Li Lin. Research on the oxidation behavior of 316L stainless steel in high temperature environment and the erosion corrosion of oxide film [D]. Beijing: China University of Petroleum (Beijing), 2020.
[9] 胡玉婷, 董鹏飞, 蒋立, 等. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167 − 174. Hu Yuting, Dong Pengfei, Jiang Li, et al. Research on corrosion behavior of TC4 titanium alloy and 316L stainless steel riveted parts in marine atmospheric environment[J]. Chinese Journal of Corrosion and Protection, 2020, 40(2): 167 − 174.
[10] Francis R. Galvanic corrosion of high alloy stainless steels in sea water[J]. British Corrosion Journal, 1994, 29(1): 53 − 57. doi: 10.1179/000705994798268033
[11] 孙荣禄, 杨文杰, 张九海, 等. 钛合金与不锈钢真空扩散焊接的研究[J]. 佳木斯工学院学报, 1997(1): 46 − 50,79. Sun Ronglu, Yang Wenjie, Zhang Jiuhai, et al. Study on vacuum diffusion welding of titanium alloy and stainless steel[J]. Journal of Jiamusi Institute of Technology, 1997(1): 46 − 50,79.
[12] 肖旋, 李海东, 刘海涛, 等. 钛合金真空与不锈钢管件真空扩散焊工艺研究[J]. 热加工工艺, 2022, 52(1): 21 − 24. Xiao Xuan, Li Haidong, Liu Haitao, et al. Research on vacuum diffusion welding process of titanium alloy and stainless steel pipe fittings[J]. Hot Working Process, 2022, 52(1): 21 − 24.
[13] Kahraman N, Gülenç B, Findik F. Joining of titanium/stainless steel by explosive welding and effect on interface[J]. Journal of Materials Processing Technology, 2005, 169(2): 127 − 133. doi: 10.1016/j.jmatprotec.2005.06.045
[14] 张志强, 杨凡, 张天刚, 等. 激光熔覆碳化钛增强钛基复合涂层研究进展[J]. 表面技术, 2020, 49(10): 138 − 151,168. Zhang Zhiqiang, Yang Fan, Zhang Tiangang, et al. Research progress of laser cladding titanium carbide reinforced titanium-based composite coatings[J]. Surface Technology, 2020, 49(10): 138 − 151,168.
[15] Zhang Y, Chen Y K, Zhou J P, et al. Forming mechanism and mechanical property of pulsed laser welded Ti alloy and stainless steel joint using copper as interlayer[J]. Journal of Materials Research and Technology, 2020, 9(2): 1425 − 1433. doi: 10.1016/j.jmrt.2019.11.068
[16] Tanprayoon D, Srisawadi S, Sato Y, et al. Microstructure and hardness response of novel 316L stainless steel composite with TiN addition fabricated by SLM[J]. Optics & Laser Technology, 2020, 129: 106238.
[17] Gao Fuyang, Mu Zhuangzhuang, Ma Zhaowei, et al. Fine microstructure characterization of titanium alloy laser narrow gap welded joint[J]. China Welding, 2021, 30(3): 31 − 38.
[18] 田志刚, 李新梅, 秦忠, 等. 激光熔覆CoCrFeNiSix高熵合金涂层的组织与性能[J]. 焊接学报, 2022, 43(12): 53 − 63. Tian Zhigang, Li Xinmei, Qin Zhong, et al. Microstructure and properties of laser cladding CoCrFeNiSix high entropy alloy coating[J]. Transactions of the China Welding Institution, 2022, 43(12): 53 − 63.
[19] Sun Z, Ji X, Zhang W, et al. Microstructure evolution and high temperature resistance of Ti6Al4V/Inconel625 gradient coating fabricated by laser melting deposition[J]. Materials & Design, 2020, 191: 108644.
[20] 张亚运, 魏金山, 齐彦昌, 等. TA2/Q235复合板用Ni基过渡层熔焊接头组织和性能[J]. 焊接学报, 2019, 40(1): 75 − 79. Zhang Yayun, Wei Jinshan, Qi Yanchang, et al. Microstructure and properties of welded joints with Ni base transition layer for TA2/Q235 composite plates[J]. Transactions of the China Welding Institution, 2019, 40(1): 75 − 79.
[21] Wu W, Zhang M, Ding X, et al. Microstructure and mechanical property of fusion weld butt joints of TA1/X80 composite plate with TiNi and NiCrMo double-transition layers[J]. Chinese Journal of Materials Research, 2016, 30(5): 372 − 378.
-
期刊类型引用(2)
1. 赵衍华，张粟泓，王非凡，郝云飞，宋建岭，孙世烜，王国庆. 搅拌摩擦焊接与加工技术进展. 航天制造技术. 2025(01): 1-25 . 
百度学术
2. 刘柏韬，顾彬，余海东. 关于铝合金薄板高速搅拌摩擦焊接搅拌头的新型设计. 机械设计与研究. 2023(05): 152-157 . 百度学术
其他类型引用(3)
计量
- 文章访问数: 309
- HTML全文浏览量: 39
- PDF下载量: 84
- 被引次数: 5