TA2/Q235复合板用Ni基过渡层熔焊接头组织和性能
Microstructure and property of fusion welding butt joints of TA2/Q235 composite plate with Ni alloy transition layers
-
摘要: 采用Ni基过渡填充材料，进行TA2/Q235复合板对接熔化焊试验，研究了接头组织形貌、成分分布、相组成及力学性能. 结果表明，近焊缝区，TA2覆层组织主要是板条α相，Q235基层组织为块状珠光体和铁素体；焊缝中Ti层组织主要为呈树枝晶生长的β相，并含有NiTi2，Ni3Ti，TiFe，TiFe2和TiCr2相，Ni基层中主要是γ-Ni，并含有少量Fe3Ni2，CrNi2和(CrNiMo)化合物，Ti层与Ni基层之间存在宽约50 μm过渡层，过渡层中存在大量针叶状NiTi2，NiTi金属间化合物，被CrNi2相包覆，从Ti层到Ni基层，Ti元素缓慢下降，Ni元素先升高后降低，Cr，Mo元素波动升高；Ti层及与Ni基焊缝的过渡层中的金属间化合物和脆性相，提高了硬度，降低了塑韧性.Abstract: Fusion welding of TA2/Q235 composite plate was carried out by taking Ni alloy as filled material. The microstructure, chemical, phase composition and mechanical properties of the weld metal were investigated. Results showed that the microstructure of TA2 coating was mainly lath α-phase and microstructure of Q235 matrix was massive pearlite and ferrite near the weld zone. In the weld, microstructure of Ti layer was mainly a dendritic growth of β-phase, containing NiTi2, Ni3Ti, TiFe, TiFe2 and TiCr2. Microstructure of Ni alloy layer was mainly γ-Ni, and contained a small amount of Fe3Ni2, CrNi2 and (CrNiMo) compounds. Between Ti layer and Ni layer, there was a transition layer width of 50 μm , and a lot of needle were in the transition layer such as NiTi2 and NiTi intermetallic compound coated by CrNi2 phase. From the Ti layer to the Ni alloy layer, element Ti decreased slowly, Ni increased first and then decreased and Cr, Mo element increased slowly. The intermetallic and brittle phases in the Ti layer and the transition layer increased the hardness and reduced the ductility.
-
-
[1] 汪 汀. 钛/钢复合板反应釜筒体的焊接工艺[J]. 材料开发与应用, 2003, 18(2): 15 ? 18
Wang Ting. Welding process of reaction tube body of titanium steel composite plate[J]. Development and Application of Materials, 2003, 18(2): 15 ? 18[2] 陈满乾, 刘亚芬. TA2/Q235B钛钢复合板的焊接[J]. 焊接, 2007(8): 53 ? 55
Chen Manqian, Liu Yafen. Welding of TA2/Q235B titanium steel composite plate[J]. Welding & Joining, 2007(8): 53 ? 55[3] Kundu S, Ghosh M, Laik A, et al. Diffusion bonding of commercially pure titanium to 304 stainless steel by using copper interlayer[J]. Materials Science and Engineering A, 2005, 407(1-2): 154 ? 160. [4] 孙荣禄, 杨文杰, 于 斌, 等. 钛合金与不锈钢扩散焊中间金属的选择[J]. 宇航材料工艺, 1997(5): 15 ? 18
Sun Ronglu, Yang Wenjie, Yu Bin, et al. Selection of intermediate metals for diffusion welding of titanium alloy and stainless steel[J]. Aerospace Materials & Technology, 1997(5): 15 ? 18[5] Kundu S, Sam S, Mishra B, et al. Diffusion bonding of microduplex stainless steel and Ti alloy with and without interlayer: interface microstructure and strength properties[J]. Metallurgical and Materials Transactions A, 2014, 45(1): 371 ? 383. [6] 孙荣禄, 李慕勤, 张九海, 等. 中间过渡金属对钛合金与不锈钢扩散焊接头强度的影响[J]. 焊接学报, 1996, 27(4): 212 ? 218
Sun Ronglu, Li Muqin, Zhang Jiuhai, et al. Effect of intermediate transition metal on the strength of titanium alloy and stainless steel diffusion welded joints[J]. Transactions of the China Welding Institution, 1996, 27(4): 212 ? 218[7] 孙 玮. 氩弧焊接TA2及Ti62421s合金组织、性能的研究[D]. 长沙: 中南大学, 2012. [8] 王敬忠, 颜学柏, 阎静亚, 等. 钛-钢复合板生产中的过渡层材料[J]. 有色金属工程, 2009, 61(4): 39 ? 42
Wang Jingzhong, Yan Xuebai, Yan Jingya, et al. Transition layer materials in the production of titanium-steel composite sheets[J]. Nonferrous Metals Engineering, 2009, 61(4): 39 ? 42[9] 吴伟刚, 张 敏, 丁 旭, 等. TA1/X80复合板用TiNi/NiCrMo双过渡层熔焊对接接头组织及性能[J]. 材料研究学报, 2016(5): 372 ? 378
Wu Weigang, Zhang Min, Ding Xu, et al. Microstructure and properties of butt joints of TiNi/NiCrMo double transition layer welded joints for TA1/X80 composite sheets[J]. Chinese Journal of Materials Research, 2016(5): 372 ? 378[10] Qin B, Sheng G M, Huang J W, et al. Phase transformation diffusion bonding of titanium alloy with stainless steel[J]. Materials Characterization, 2006, 56(1): 32 ? 38. [11] Okamoto H. Cr-Ti (chromium-titanium)[J]. Journal of Phase Equilibria, 2002, 23(4): 382. [12] 葛 鹏, 吴 欢, 赵永庆. Mo、V、Cr对钛合金β相的合金化效应[J]. 中国材料进展, 2016, 35(10): 795 ? 798
Ge Peng, Wu Huan, Zhao Yongqing. Alloying effect of Mo, V and Cr on β phase of titanium alloy[J]. Materials China, 2016, 35(10): 795 ? 798 -
期刊类型引用(9)
1. 程磊，张旭航，韩盈，程志诚，余伟. 中间层材料Fe和Nb对高强钛-钢复合管界面及剪切强度的影响. 金属学报. 2024(01): 117-128 . 
百度学术
2. 姚尚君，苗鑫，陈思杰，郝丽丽，李振豪. 焊接温度对钛/钢复合管瞬时液相扩散焊接头组织与性能的影响. 机械工程材料. 2023(02): 33-38 . 百度学术
3. 刘文明，欧阳凯，张新明，张朝明，程新路，陈成. 焊后热处理对S30408/Q345R复合板焊接接头残余应力的影响. 材料热处理学报. 2023(03): 217-226 . 百度学术
4. 张敏，王新宝，王浩军，马克，朱子越，张志强. 激光熔覆TC4/Inconel 625/316L不锈钢梯度材料组织与性能. 焊接学报. 2023(07): 16-23+129-130 . 本站查看
5. 闫婉迪，孙新丰，张岩，李福山，徐荣正. 钛/钢层状复合板焊接技术的现状与展望. 有色金属工程. 2021(04): 33-41 . 百度学术
6. 陈立佳，赵力东，王旭，周正，郭星晔，贺定勇. NiCrBSi超音速火焰喷涂层在不同温度下的磨损行为. 焊接学报. 2021(05): 65-70+102 . 本站查看
7. 胡奉雅，许国敬，陈伟，冷雪松，付魁军，闫久春. 钛/钢复合板焊接技术研究现状及发展趋势. 焊接学报. 2021(06): 30-43+98-99 . 本站查看
8. 安同邦，由恒源，李弟，孔海军，赵丹，刘亦洋. TA2/Q235复合板Nb/Cu双过渡层熔焊焊缝组织性能. 热加工工艺. 2019(09): 18-21 . 百度学术
9. 季霄，孙中刚，唱丽丽，常辉，邢飞. 激光熔化沉积Ti6Al4V/Inconel625梯度耐高温涂层组织演变行为研究. 中国激光. 2019(11): 145-153 . 百度学术
其他类型引用(6)
计量
- 文章访问数: 950
- HTML全文浏览量: 22
- PDF下载量: 16
- 被引次数: 15
下载: