齿形对超声波焊接泡沫镍薄板与实体铝薄板的影响
Effect of teeth shape on ultrasonic spot welding joints of nickel foam sheet and aluminum solid sheet
-
摘要: 采用超声波点焊工艺成功焊接了电池电极及催化剂载体所使用的泡沫镍薄板与纯铝实体薄板，在与泡沫镍接触的砧座处采用了粗细两种齿形设计，对比了不同齿形引起的不同塑性形变程度对焊接性能的影响. 分析了齿形及工艺参数对拉伸性能及断口形貌的影响. 结果表明，细齿形砧座30 J试样拉伸性能最优，拉伸载荷与断裂能分别达到泡沫镍母材的58.0%与69.1%. 测试了两种齿形砧座焊接的接头在3.5%NaCl溶液中的阳极极化曲线，对比了其耐腐蚀性能. 能谱分析结果表明，跨过界面扩散的元素含量极少，焊接界面没有明显金属间化合物层产生，焊接过程属于固态过程.
-
关键词:
- 超声波点焊|泡沫金属|薄板|异质接头
Abstract: Nickel foam sheet and pure aluminum solid sheet for electrodes and catalyst carrier were successfully welded via ultrasonic spot welding. Two kinds of sizes of anvil teeth which were in contact with the nickel foam were designed. Effects of anvil teeth shapes on plastic deformation and performances were compared. Influence of teeth shapes and welding parameters on tensile properties and fracture morphologies were analyzed. The results showed that the 30 J specimen welded by small teeth anvil had the optimal tensile strength and fracture energy, which reached 58% and 69.1% of nickel foam base metal, respectively. The anodic polarization curves of two kinds of welded joints in 3.5% NaCl solution were compared. The results of energy-dispersion spectrum analysis showed that the element diffusion across the interface diffusion was insufficient, and no obvious intermetallic compound layer in the welding interface was observed. The welding process was solid state process. -
-
[1] Yuan J, Chen C, Hao Y, et al. Three-dimensionally porous CoMn2O4, thin films grown on Ni foams for high-performance lithium-ion battery anodes[J]. Journal of Materials Science, 2017, 52(10): 1 ? 8. [2] Jiang T, Zhang S, Qiu X, et al. Preparation and characterization of silicon-based three-dimensional cellular anode for lithium ion battery[J]. Electrochemistry Communications, 2007, 9(5): 930 ? 934. [3] Longerich S, Piontek D, Ohse P, et al. Joining strategies for open porous metallic foams on Iron and nickel base materials[J]. Advanced Engineering Materials, 2007, 9(8): 670 ? 678. [4] Nowacki J, Moraniec K. Welding of metallic AlSi foams and AlSi–SiC composite foams[J]. Archives of Civil & Mechanical Engineering, 2015, 15(4): 940 ? 950. [5] Born C, Kuckert H, Wagner G, et al. Ultrasonic torsion welding of sheet metals to cellular metallic materials[J]. Advanced Engineering Materials, 2003, 5(11): 779 ? 786. [6] Born C, Wagner G, Eifler D. Ultrasonically welded aluminium foams/sheet metal–joints[J]. Advanced Engineering Materials, 2006, 8(9): 816 ? 820. [7] Ren D, Zhao K, Pan M, et al. Ultrasonic spot welding of magnesium alloy to titanium alloy[J]. Scripta Materialia, 2017, 126: 58 ? 62. [8] Mirza F A, Macwan A, Bhole S D, et al. Effect of welding energy on microstructure and strength of ultrasonic spot welded dissimilar joints of aluminum to steel sheets[J]. Materials Science & Engineering A, 2016, 668: 73 ? 85. [9] Kumar S, Wu C S, Padhy G K, et al. Application of ultrasonic vibrations in welding and metal processing: A status review[J]. Journal of Manufacturing Processes, 2017, 26: 295 ? 322. -
期刊类型引用(7)
1. 唐天祥，史清宇，周军，张春波，梁武，周梦然，张弓，陈高强. GH4169惯性摩擦焊界面摩擦及瞬态热过程数值模拟研究. 航空制造技术. 2024(10): 36-44+52 . 
百度学术
2. 梁武，周军，张春波，张露，乌彦全，李运雷. FGH96/IN718惯性摩擦焊接头高温拉伸断裂特征. 焊接学报. 2023(09): 44-52+131-132 . 本站查看
3. 许乔郅，张国栋，袁鸿，王金雪. FGH101高温合金惯性摩擦焊接头的显微组织与力学性能. 热加工工艺. 2023(23): 63-66+71 . 百度学术
4. 张露，张春波，廖仲祥，乌彦全，张国栋，周军. IN718/FGH96惯性摩擦焊接头焊缝区微观组织状态与织构分布特征. 电焊机. 2022(04): 8-13 . 百度学术
5. 张广刚，赵强，刘佳涛，白瑞祥，董红刚. 基于三维双塑性体摩擦副模型的FGH96高温合金管惯性摩擦焊数值模拟. 焊接. 2022(07): 14-20 . 百度学术
6. 郑守峰，赵强，黄文彬，王树锋，刘佳涛，祝文卉. FGH98合金惯性摩擦焊接头显微组织与力学性能. 焊接. 2022(10): 21-26 . 百度学术
7. 刘莹莹，李洁洁，田万涛，吴方林，谭千辉. 异种合金惯性摩擦焊的研究现状. 焊接. 2021(01): 35-41+63 . 百度学术
其他类型引用(4)
计量
- 文章访问数: 429
- HTML全文浏览量: 4
- PDF下载量: 13
- 被引次数: 11
下载: