工艺参数对可伐合金/DM308钼组玻璃激光焊接接头结合性能的影响
Effect of process parameters on laser welded joint bonding properties between Kovar alloy and DM308 glass
-
摘要: 采用YLS-6000型光纤激光器对可伐合金4J29与钼组玻璃DM308进行激光焊接，研究了工艺参数对接头强度和界面结构的影响，分析了界面元素扩散行为. 结果表明,激光功率为700～800 W，焊接速度为4.5 mm/s，离焦量为0时，接头抗剪强度达到最大值，为10.97 MPa；4J29/DM308激光焊接头界面结合良好，存在反应层，分界线清晰可见. 玻璃侧有大量气孔产生，界面某些部位存在少量气孔，导致产生微裂纹；在高温条件下，元素扩散越均匀，界面反应生成Fe2SiO4越多，接头强度越高.Abstract: Laser welding between Kovar alloy and DM308 Mo glass using YLS-6000 fiber laser was performed. The effects of process parameters on joint strength and interface microstructure were studied as well as diffusion behavior of interface elements. The result shows that: (1) When the laser power is 700-800 W, the welding speed is 4.5 mm/s and the focal distance is 0 mm, the joint shear strength reaches the maximum value of 10.97 MPa; (2) The bonding quality of Kovar alloy/DM308 glass is generally good. A thin reaction layer was observed at the interface. The boundary between the welded seam and the substrates is clear. Microcracks exist in some positions of interface due to the presence of a lot of pores in the glass side; (3) Under high temperature conditions, the element diffusion is more uniform, the more Fe2SiO4is generated at the interface reaction, and the joint strength is the higher.
-
Keywords:
- process parameters /
- Kovar alloy /
- DM308 glass /
- diffusion /
- laser welding
-
-
[1] Dongqiang L, Zhifeng W, Jian L,et al. Experimental study of glass to metal seals for parabolic trough receivers[J]. Renewable Energy, 2012, 48: 85-91.[2] 李卓然, 徐晓龙. 玻璃与金属连接技术研究进展[J]. 失效分析与预防, 2013(2): 123-130.Li Zhuoran, Xu Xiaolong. Review of bonding technology of glass to metal[J]. Failure Analysis and Prevention, 2013(2): 123-130.[3] Yan L, Yunzhou Z, Yong Y,et al. Microstructure of reaction layer and its effect on the joining strength of SiC/SiC joints brazed using Ag-Cu-In-Ti alloy[J]. Journal of Advanced Ceramics, 2014, 3(1): 71-75.[4] 涂 冶, 季凌飞, 鲍 勇, 等. 高硼硅3.3玻璃和可伐合金的激光封接界面研究[J]. 应用激光, 2011(1): 12-14.Tu Ye, Ji Lingfei, Bao Yong,et al. Joining behavior and interface analysis of pyrex glass-to-Kovar alloy with fiber laser[J]. Applied Laser, 2011(1): 12-14.[5] 栗卓新, 铁 敏, 李 红, 等. 异种材料连接中表面预处理及对接头强度影响的研究进展[J]. 北京工业大学学报, 2015(1): 153-160.Li Zhuoxin, Tie Min, Li Hong,et al. Progress on surface pretreatment and its effect on the joint strength in dissimilar materials joining[J]. Journal of Beijing University of Technology, 2015(1): 153-160.[6] Iwamoto C. Microstructure of aluminum/glass joint bonded by ultrasonic wire welding[J]. Metallurgical and Materials Transactions A, 2014, 45(3): 1371-1375.[7] Guodong Z, Guanghua C. Direct welding of glass and metal by 1 kHz femtosecond laser pulses.[J].Journal of Applied Mechanics, 2015, 82(10): 8957-8961.[8] Sizhu W, Dong W, Jian X,et al. Characterization and mechanism of glass microwelding by double-pulse ultrafast laser irradiation[J]. Optics Express, 2012, 20(27): 28893-28905.[9] 铁 敏, 李 红, 栗卓新, 等. 硼硅玻璃与可伐合金的激光熔接工艺[J]. 焊接学报. 2016, 37(6): 55-58.Tie Min, Li Hong, Li Zhuoxin,et al. Laser welding process of borosilicate glass and FV alloy[J]. Transactions of the China Welding Institution, 2016, 37(6): 55-58.[10] 刘翠荣. 玻璃(陶瓷)与金属阳极键合界面结构及力学性能[D]. 太原: 太原理工大学, 2008.[11] Bruce D. Field-assisted bonding of beta-alumina to metals[J]. Journal of the Ameican Ceramic Society, 1979, 62(11-12): 545-547. -
期刊类型引用(7)
1. 唐天祥，史清宇，周军，张春波，梁武，周梦然，张弓，陈高强. GH4169惯性摩擦焊界面摩擦及瞬态热过程数值模拟研究. 航空制造技术. 2024(10): 36-44+52 . 
百度学术
2. 梁武，周军，张春波，张露，乌彦全，李运雷. FGH96/IN718惯性摩擦焊接头高温拉伸断裂特征. 焊接学报. 2023(09): 44-52+131-132 . 本站查看
3. 许乔郅，张国栋，袁鸿，王金雪. FGH101高温合金惯性摩擦焊接头的显微组织与力学性能. 热加工工艺. 2023(23): 63-66+71 . 百度学术
4. 张露，张春波，廖仲祥，乌彦全，张国栋，周军. IN718/FGH96惯性摩擦焊接头焊缝区微观组织状态与织构分布特征. 电焊机. 2022(04): 8-13 . 百度学术
5. 张广刚，赵强，刘佳涛，白瑞祥，董红刚. 基于三维双塑性体摩擦副模型的FGH96高温合金管惯性摩擦焊数值模拟. 焊接. 2022(07): 14-20 . 百度学术
6. 郑守峰，赵强，黄文彬，王树锋，刘佳涛，祝文卉. FGH98合金惯性摩擦焊接头显微组织与力学性能. 焊接. 2022(10): 21-26 . 百度学术
7. 刘莹莹，李洁洁，田万涛，吴方林，谭千辉. 异种合金惯性摩擦焊的研究现状. 焊接. 2021(01): 35-41+63 . 百度学术
其他类型引用(4)
计量
- 文章访问数: 746
- HTML全文浏览量: 9
- PDF下载量: 0
- 被引次数: 11
下载: