基于光纤激光的LY12铝合金焊接试验分析
Welding of LY12 aluminum alloy based on fibre laser
-
摘要: 在飞机制造领域，铝合金主要用于制造飞机蒙皮、梁、桁条和框架等结构.采用多模光纤激光器进行了1.4 mm厚LY12铝合金的激光焊接试验，研究了焊接工艺参数对铝合金焊缝形貌的影响规律，并对焊接接头的显微硬度及断口形貌进行了分析.结果表明，大功率高速度连续激光焊缝的成形具有不稳定性，当功率为2 200 W，焊接速度为55 mm/s，保护气体流量为10 L/min时，可以获得成形良好且无宏观缺陷的焊接接头.接头的平均抗拉强度约为388 MPa，达到母材抗拉强度的63.98%，断裂类型为韧脆混合型断裂.Abstract: In aircraft manufacturing industry, the aluminum alloy is mainly used in the skin, beam, purlin and frame structures. Laser welding of 1.2 mm thick LY12 aluminum alloy sheets was conducted with multimode fibre laser. The influence of laser welding parameters on aluminum alloy weld shape was studied, and the fracture appearance and microhardness of welded joint were analyzed. The results show that the weld appearance with large power and high speed continuous laser was instable. The welded joint with good shape and free defects can be obtained with laser power of 2 200 W, welding speed of 55 mm/s and shielding gas flow rate of 10 L/min. The average tensile strength of joint was 388 MPa, reaching 63.98% of that of the base metal. The fracture of the joint was a mixed ductilebrittle mode.
-
-
[1] 孙乎浩,薛松柏,冯晓梅,等.舰船用6082铝合金TIG焊组织与力学性能分析[J].焊接学报,2014,35(2): 91-94.Sun Huhao,Xue Songbai,Feng Xiaomei,etal.Microstructure and mechanical properties of weld joint of marine 6082 aluminum alloy by TIG welding[J].Transactions of the China Welding Institution,2014,35(2): 91-94.[2] 张 健,雷 振,王旭友.高速列车6005A铝合金型材焊接热裂纹分析[J].焊接学报,2012,33(8): 60-64.Zhang Jian,Lei Zhen,Wang Xuyou.Weld hot crack analysis of6005A aluminum profile for high-speed train[J].Transactions of China Welding Institution,2012,33(8): 60-64.[3] 李 显,宋永伦,卢振洋,等.2219铝合金高频耦合脉冲TIG焊接工艺[J].焊机学报,2015,36(5): 17-20.Li Xian,Song Yonglun,Lu Zhenyang,etal.High frequency energy coupling pulsed TIG welding process on 2219 aluminum alloy[J].Transactions of the China Welding Institution,2015,36(5): 17-20.[4] 胡芳友,回 丽,易德先,等.飞机损伤的激光抢修技术[J].中国激光,2009,36(9): 2245-2250.Hu Fangyou,Hui Li,Yi Dexian,etal.Laser repair of aircraft battle damage[J].Chinese Journal of Lasers,2009,36(9):2245-2250.[5] 胡芳友,胡宝良.适应现代海战需要,加快我海军飞机战伤抢修建设[J].国防科技,2008,29(3): 61-66.Hu Fangyou,Hu Baoliang.Meeting the needs of modern naval warfare,quickening the construction of our naval aircraft war-wound rush repairing[J].National Defense Science & Technology,2008,29(3): 61-66.[6] 李成功,傅恒志,于 翘.航空航天材料[M].北京: 国防工业出版社,2002.[7] 刘 兵,彭超群,王日初,等.大飞机用铝合金的研究现状及展望[J].中国有色金属学报,2010,20(9): 1705-1715.Liu Bin,Peng Chaoqun,Wang Richu,etal.Recent development and prospects for giant plane aluminum alloys[J].The Chinese Journal of Nonferrous Metals,2010,20(9): 1705-1715.[8] Filatov Y A,Yelagin V I,Zakharov V V.New Al-Mg-Sc alloys[J].Materials Science and Engineering A,2000,280: 97-101.[9] 卢长亮,胡芳友,黄旭仁,等.激光熔铸修理航空铝合金LY12CZ组织与疲劳性能[J].兵器材料科学与工程,2011,34(6): 58-61.Lu Changliang,Hu Fangyou,Huang Xuren,etal.Microstructure and fatigue properties of aviation aluminum alloy LY12CZ repaired by laser melt casting[J].Ordnance Material Science and Engineering,2011,34(6): 58-61.[10] 任旭东,皇甫喁卓,阮 亮,等.激光冲击对中高温服役条件下镍基合金K417显微硬度的影响[J].中国激光,2012,39(7): 0703005.Ren Xudong,Huangfu Yongzhuo,Ruan Liang,etal.Effects of laser shock processing on micro-hardness of Ni-Based superalloy K417 at elevated temperature[J].Chinese Journal Lasers,2012,39(7): 0703005. -
期刊类型引用(9)
1. 高博轩，赵弘，苗兴园. 基于改进GWO-GRNN的管道焊缝三维重构测量. 机床与液压. 2024(01): 1-10 . 
百度学术
2. 陈晓明，王丽，马良，周峰，袁山山. 钢筋工程焊缝质量检测技术研究进展. 北京理工大学学报. 2024(12): 1215-1224 . 百度学术
3. 唐昌华，吴琼，时兵，陈坚，李洪亮. 基于压缩感知的激光复合成像超分辨三维重构方法. 激光杂志. 2023(09): 109-113 . 百度学术
4. 李诺薇，邹维科，种法力. 基于3D激光扫描传感器的焊缝区域跟踪方法设计. 激光与红外. 2023(11): 1650-1656 . 百度学术
5. 余志，白小亮. 一种石油管内焊缝余高及刮槽深度的测量方法. 石油工业技术监督. 2022(05): 17-19 . 百度学术
6. 杨国威，张金丽. 基于光栅投影的焊后焊缝表面三维测量. 焊接学报. 2022(04): 100-105+112+119-120 . 本站查看
7. 马涛，丁克勤，舒安庆，刘亚男. 基于布里渊分布式光纤的储液罐变形场重构方法研究. 压力容器. 2021(04): 11-19 . 百度学术
8. 胡曦，余震，刘海生. 管道全位置焊缝三维测量研究. 石油机械. 2021(09): 129-136 . 百度学术
9. 李亮亮，郑世伟，单清群，左玉达. 转向架焊接结构件深度缺陷超声相控阵检测及三维可视化. 焊接. 2021(09): 44-50+64 . 百度学术
其他类型引用(12)
计量
- 文章访问数: 438
- HTML全文浏览量: 26
- PDF下载量: 117
- 被引次数: 21
下载: